Modifying the surface energy and hydrophobicity of the low-density silica aerogels through the use of combinations of surface-modification agents
- 612 Downloads
Aerogels are lightweight, highly transparent, thermally insulating materials comprising interconnected nanostructured pores. Low surface energy aerogels were prepared from ambient pressure drying of sodium silicate-based gels by modifying the pore surfaces with silylating agents including trimethylchlorosilane (TMCS), hexamethyldisiloxane (HMDSO), and hexamethyldisilazane (HMDZ), in combination with each other. Hydrophobic properties of the resulted aerogels were studied by contact angle measurements. Fourier-transform infrared spectroscopy (FTIR) was used to monitor the changes in chemical bonds within the aerogels due to surface modification. The microstructure was studied by transmission electron microscopy (TEM). Effect of temperature on the hydrophobicity of the aerogels was studied by thermogravimetric analysis/differential thermal analysis (TGA-DTA). Surface modification of silica gels with various mixtures of surface-modification agents showed different behaviors. Aerogels made by HMDZ and HMDSO combination comprised 5 nm pores and particles and showed a high surface energy, whereas aerogels prepared by HMDSO and TMCS combination had lower surface energy with relatively larger particle and pore sizes with a more uniform distribution of both. The properties of the latter sample were attributed to a greater degree of surface modification and negligible condensation of OH groups. This preparation produced silica aerogels with a low density (0.042 g/cc), low surface energy (3.39 N cm−1), low thermal conductivity (0.050 W K−1 m−1), high optical transmission (85% at 700 nm) and hydrophobic (154° contact angle) with high hydrophobic thermal stability (425 °C). Moreover, the contact angle for materials prepared by this method decreased negligibly over 12 months’ storage in ambient conditions.
KeywordsContact Angle Surface Modification Pore Size Distribution Capillary Pressure Water Drop
Authors are grateful to the Condensed Matter Advisory Committee, Department of Science and Technology (DST), New Delhi, Government of India, for the financial support for this work through a major research project on “Aerogels” (No. SR/S2/CMP-67/2006).
- 2.Forest L, Gibiat C, Woignier T (1998) In: Proceedings of the fifth international symposium on aerogels (ISA 5). J Non-Cryst Solids 225:287Google Scholar
- 3.Guise MT, Hosticka B, Earp BC, Norris PM (1995) In: Proceedings of the fourth international symposium on aerogels (ISA 4). J Non-Cryst Solids 186:317Google Scholar
- 7.Jones SM (2007) J Sol-Gel Sci Technol 40(16):351Google Scholar
- 9.Nakajima K et al (1996) Kogyo-zairyo 44:68Google Scholar
- 10.Brinker CJ, Scherer GW (1989) Sol-gel science. Academic, New YorkGoogle Scholar
- 12.Deshpande R, Smith D, Brinker CJ (1996) US Patent 5,565,142Google Scholar
- 20.Uzma K, Bangi H, Venkateswara Rao , A Parvathy Rao (2008) Science and Technology of Advanced Materials 9Google Scholar
- 23.Blake TD (1993) In: Berg JC (ed) Wettabiltiy. Marcel Dekker, New YorkGoogle Scholar
- 33.Shi F, Wang LJ, Liu JX, Li N (2004) Building materials 6:9, in ChineseGoogle Scholar
- 35.Rouquerol F, Rouquerol J, Sing K (1999) Adsorption by powders and porous solids, principles, methodology and applications. Academic PressGoogle Scholar