The effect of skin characteristics on the environmental behavior of die cast AZ91 magnesium alloy

  • E. AghionEmail author
  • N. Lulu
Article

Abstract

The skin characteristics of die cast AZ91 magnesium alloys and their consequent environmental behavior were evaluated in correlation with die cast wall thickness. The metallurgical examination of the skins was carried out using scanning electron microscopy (SEM), SPX-surface analyses with ESCALAB 250 apparatus, and X-ray diffraction analysis. The corrosion behavior of the skins was evaluated by immersion tests and by potentiodynamic polarization measurements in 3.5% NaCl solution saturated with Mg (OH)2 at room temperature. The results show that the corrosion resistance of die cast specimens with relatively greater thickness was improved compared to the corrosion resistance of thin wall specimens. This was explained in light of the obtained skin characteristics, mainly in terms of aluminum content, β phase (Mg17Al12) quantity and morphology, and level of porosity.

Keywords

Corrosion Resistance Magnesium Alloy Corrosion Performance Thick Specimen Improve Corrosion Resistance 

Notes

Acknowledgements

The authors would like to thank the Magnesium Research Institute of Dead Sea Magnesium for the preparation of the die casting specimens, and N. Frumin and D. Mogilyanski from Ben-Gurion University for their kind assistance in the XPS and XRD analyses, respectively.

References

  1. 1.
    Shan S, Gokhale AM (2003) Mater Sci Eng A Struct Mater 361:267CrossRefGoogle Scholar
  2. 2.
    Song G, Atrens A, Dargusch M (1998) Corros Sci 41:249CrossRefGoogle Scholar
  3. 3.
    Yu B-L, Uan J-Y (2005) Metall Mater Trans A 36A:2245CrossRefGoogle Scholar
  4. 4.
    Lafront A-M, Dub D, Tremblay R, Ghali E, Blawert C, Dietzel W (2008) Can Metall Q 47(4):459CrossRefGoogle Scholar
  5. 5.
    Ghali E, Dietzel W, Kainer KU (2004) J Mater Eng Perform 13(1):7CrossRefGoogle Scholar
  6. 6.
    Song G, Atrens A, Wu X, Zhang B (1998) Corros Sci 40(10):1769CrossRefGoogle Scholar
  7. 7.
    Zhao MC, Liu M, Song G, Atrens A (2008) Corros Sci 50:1939CrossRefGoogle Scholar
  8. 8.
    Uan J-Y, Li CF, Yu BL (2008) Metall Mater Trans A 39a:703CrossRefGoogle Scholar
  9. 9.
    Weiler JP, Wood JT (2006) Mater Sci Eng A 419:297CrossRefGoogle Scholar
  10. 10.
    Cho CY, Uan J-Y, Lin HJ (2005) Mater Sci Eng A 402:193CrossRefGoogle Scholar
  11. 11.
    Song G, Atrens A (1998) In: Mordike B, Kainer K (eds) Magnesium alloys and their applications. Wolfsburg, Germany, p 28 (April: 415–419)Google Scholar
  12. 12.
    Aghion E, Moscovitch N, Arnon A (2007) Mater Sci Eng A 447:341CrossRefGoogle Scholar
  13. 13.
    Aghion E, Moscovitch N, Arnon A (2007) Mater Sci Technol 23:270CrossRefGoogle Scholar
  14. 14.
    Song G, Atrens A (2003) Adv Eng Mater 5(12):837CrossRefGoogle Scholar
  15. 15.
    Lunder O, Nisancioglu K, Hanses RS (1993) SAE Technical paper No. 930755Google Scholar
  16. 16.
    Kuhlein M, Galovsky U (2004) Mater Corros 55(6):444CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC 2009

Authors and Affiliations

  1. 1.Department of Materials EngineeringBen-Gurion University of the NegevBeer-ShevaIsrael

Personalised recommendations