Water intrusion-extrusion in silicalite-1 with tunable mesoporosity prepared in fluoride medium
- 115 Downloads
Experimental water intrusion–extrusion isotherms were performed at room temperature on mesoporous silicalite-1 samples, prepared in fluoride medium and using carbon black or surfactant, [3-(trimethoxysilyl)propyl]hexadecyldimethylammonium chloride, as porogen and templating agents, respectively. The increase of the porous volume observed for the silicalite-1 sample prepared in the presence of carbon black leads to an increase of the water intruded volume at high pressure (100 MPa). Therefore, the amount of stored energy in this water–zeolite system is greater than for a conventional “water–silicalite-1” system. However, the fluoride route appears to be a less effective method than the alkaline route.
KeywordsZeolite Carbon Black Microporous Volume Water Intrusion Trimethoxysilyl
This work was supported by the Agence Nationale de la Recherche under contract # BLANC06-3_144027 and the ACI program “Nanothermomécanique”.
- 5.Madsen C, Jacobsen CJH (1999) Chem Commun 673Google Scholar
- 8.Soulard M, Patarin J, Eroshenko V, Regis RC (2004) In: Van Steen E et al (eds) Proceedings of the 14th international zeolite conference, p 1830Google Scholar
- 10.Guth JL, Kessler H, Wey R (1986) In: Murakami Y et al (eds) Proceedings of the 10th international zeolite conference, p 121Google Scholar
- 13.Shaojie L, Xiaohua S, Yuan L, Huafei L, Li J, Ling H (2006) Brevet CN1792158Google Scholar