, Volume 44, Issue 1, pp 114–121 | Cite as

Effect of shielding gases on mechanical and metallurgical properties of duplex stainless-steel welds

  • P. SathiyaEmail author
  • S. Aravindan
  • R. Soundararajan
  • A. Noorul Haq
Article

Abstract

Duplex stainless steels (DSS) are well known for their higher mechanical strength and better corrosion resistance. DSS is commonly used in the marine construction, petrochemical, and chemical industries. DSS (2205) has equal amounts of α and γ phases. However, unlike the parent metal, the solidification microstructure of the fusion zone in the weld does not have nearly equal amounts of the α and γ phases. Thus the mechanical properties and corrosion resistance of DSS welds are degraded. The interpass temperature plays a vital role in achieving balanced α and γ phases, which in turn results in improved mechanical and corrosion resistance. Gas tungsten arc welding (GTAW) is employed for welding of thin sheets/plates. The GTAW process ensures small amounts of slag formation during welding, which eliminates slag crevices and sites for corrosion attack. Standard 2205 (UNS S31803) DSS sheets of 5 mm thickness, with 22.37% Cr and 5.74% Ni, were used in this study. Weld beads were produced with Zeron-100 super DSS filler wire with higher alloy content (26% Cr and 8% Ni). Argon (Ar) and helium (He) were employed as shielding gases. Heat input was maintained <1 kJ/mm. Interpass temperatures were maintained at 120°C. The ferrite number of the weld metal for the two different shielding gases was investigated. Mechanical properties of joints such as impact strength and hardness were evaluated. Microstructure evaluation was also carried out.

Keywords

Welding Ferrite Austenite Weld Metal Fusion Zone 

Notes

Acknowledgement

The authors would like to express their heartfelt thanks to Mr. P. Veerappan, Proprietor, Keerthana Engineering Works, Tiruchirappalli-15, Tamil Nadu, India, for conducting the welding trials in his factory.

References

  1. 1.
    Folkhard E (1988) Welding metallurgy of stainless steel. Springer-Verlag, Vienna, p 186Google Scholar
  2. 2.
    Karlsson L, Ryen L, Pak S (1995) Weld J 74(11):28sGoogle Scholar
  3. 3.
    Kotecki DJ (2000) Weld J 79(12):346sGoogle Scholar
  4. 4.
    Hilkes J, Bekkers K (1995) Weld J 74(11):51Google Scholar
  5. 5.
    Badij R, Belkessa B, Maza H, Bouabdallah M, Bacroix B, Kahloun C (2004) Mater Sci Forum 217:467Google Scholar
  6. 6.
    Wang S-H, Chiu P-K, Yang J-R, Fang J (2006) Mater Sci Eng A 420:26CrossRefGoogle Scholar
  7. 7.
    Muthupandi V, Bala Srinivasan P, Seshadri SK, Sundaresan S (2003) Mater Sci Eng A 358:9CrossRefGoogle Scholar
  8. 8.
    Bonnefois B, Charles J, Dupoiron F, Soulignac A (1991) Proceedings of the conference on duplex stainless steels ‘91, vol 1, Beaune, France, p 347Google Scholar
  9. 9.
    Bonollo F, Tiziani A, Zambon A, Penasa M (1994) Proceedings of fourth international conference on duplex stainless steels, paper 108, vol 2, Glasgow, Scotland, p 13Google Scholar
  10. 10.
    Brown EL, Burnett ME, Purtscher PT, Krauss G (1983) Metall Mater Trans A 14:791CrossRefGoogle Scholar
  11. 11.
    Zambon A, Bonollo F (1994) Mater Sci Eng A 178:203CrossRefGoogle Scholar
  12. 12.
    Kou S (2003) Welding metallurgy, 2nd edn. Wiley, Hoboken, NJ, p 225Google Scholar
  13. 13.
    Ramirez AJ, Lippold JC, Brandi SD (2003) Metall Mater Trans A 34:1575CrossRefGoogle Scholar
  14. 14.
    Gooch TG (1982) ASM conference on duplex ferritic-austenitic stainless steels, St. Louis, p 573Google Scholar
  15. 15.
    Ku JS, Ho NJ, Tjong SC (1997) J Mater Process Technol 63:770CrossRefGoogle Scholar
  16. 16.
    Honeycombe J, Gooch TG (1978) Proceedings of trends in steels and consumables, The Welding Institute, London, p 28Google Scholar
  17. 17.
    Wahlberg G, Dunlop GL (1987) Proceedings of the conference on stainless steels, The Institute of Metals, University of New York, p 291Google Scholar
  18. 18.
    Hertzman S, Jargelius Pettersson R, Blom R, Kivineve E, Eriksson J (1996) ISIJ Int 7(36):968CrossRefGoogle Scholar
  19. 19.
    Siegmund T, Werner E, Fisher FD (1993) Comput Mater Sci 1:234CrossRefGoogle Scholar
  20. 20.
    Kokawa H, Tomita M, Kuwana T (1995) Weld Int 9(3):8CrossRefGoogle Scholar
  21. 21.
    Ogawa T, Koseki T (1989) Weld J 68:181sGoogle Scholar
  22. 22.
    Charles J (1991) Proceedings of the conference on duplex stainless steels ‘91, Les editions de physique, Beaune, p 3Google Scholar
  23. 23.
    Ogawa K, Komizo Y, Azuma S, Kudo T (1992) Trans Jpn Weld Soc 23(1):40Google Scholar

Copyright information

© Springer Science+Business Media, LLC 2008

Authors and Affiliations

  • P. Sathiya
    • 1
    Email author
  • S. Aravindan
    • 2
  • R. Soundararajan
    • 1
  • A. Noorul Haq
    • 1
  1. 1.Department of Production EngineeringNational Institute of TechnologyTiruchirappalliIndia
  2. 2.Department of Mechanical EngineeringIndian Institute of Technology DelhiNew DelhiIndia

Personalised recommendations