Accelerated creep testing for aramid fibres using the stepped isothermal method

  • K. G. N. C. Alwis
  • C. J. BurgoyneEmail author
Article

Abstract

The article shows how the stepped isothermal method (SIM), which has hitherto been applied to polyester fibres, can be applied to the creep testing of aramids. The method is an improvement over the time temperature superposition method since a complete creep curve can be obtained from a single fibre. However, adjustments have to be made to account for the temperature changes and the past history of the fibre. Techniques are shown for performing these adjustments and the resulting master curves are compared from several different tests with different temperature sequences. Activation energies are calculated, which show that the same mechanism is acting at all stages, and creep rupture lifetime predictions are made which are longer than those hitherto made by extrapolations from short-term creep tests.

Keywords

Creep Rate Creep Strain Master Curve Temperature Step Aramid Fibre 

References

  1. 1.
    Thornton JS, Allen SR, Thomas RW (1997) Approaches for the prediction of long term viscoelastic properties of geosynthetics from short term tests Geosynthetics. IFAI, vol 1. Long Beach, CA, pp 277–291Google Scholar
  2. 2.
    Thornton JS, Allen SR, Thomas RW, Sandri D (1998) The stepped isothermal method for TTS and its application to creep data on polyester yarn. Sixth International Conference on Geosynthetics, Atlanta, USAGoogle Scholar
  3. 3.
    Thornton JS, Paulson JN, Sandri D (1998a) Conventional and stepped isothermal methods for characterizing long term creep strength of polyester geogrids. Sixth International Conference on Geosynthetics, Atlanta, USAGoogle Scholar
  4. 4.
    ASTM D6992-03. Standard test method for accelerated tensile creep and creep-rupture of geosynthetic materials based on time-temperature superposition using the stepped isothermal methodGoogle Scholar
  5. 5.
    Zornberg JG, Byler BR, Knudsen JW (2004) J Geotech Geoenviron Eng ASCE 130(11):1158CrossRefGoogle Scholar
  6. 6.
    Tamuzs V, Maksimovs R, Modniks J (2001) In: Burgoyne CJ (ed) Fibre reinforced plastics for reinforced concrete structures (FRPRCS-5). Cambridge, UK, p 527Google Scholar
  7. 7.
    Alwis KGNC (2003) Accelerated testing for long-term stress-rupture behaviour of aramid fibres. Thesis submitted to the University of CambridgeGoogle Scholar
  8. 8.
    Alwis KGNC, Burgoyne CJ (2006) J Appl Compos Mater 13(4):249. doi: https://doi.org/10.1007/s10443-006-9017-8 CrossRefGoogle Scholar
  9. 9.
    Ferry JD (1970) Viscoelastic properties of polymers. WileyGoogle Scholar
  10. 10.
    Arridge RGC (1975) Mechanics of polymers. Oxford University Press, LondonGoogle Scholar
  11. 11.
    Guimaraes GB (1988) Parallel-lay aramid ropes for use in structural engineering. PhD thesis submitted to the University of LondonGoogle Scholar
  12. 12.
    Pottick LA, Allen SR, Farris RJ (1984) J Appl Polym Sci 29:3915. doi: https://doi.org/10.1002/app.1984.070291224 CrossRefGoogle Scholar
  13. 13.
    Ii T, Tashiro K, Kobayashi M, Tadakoro H (1987) Macromolecules 20:347. doi: https://doi.org/10.1021/ma00168a020 CrossRefGoogle Scholar
  14. 14.
    Rojstaczer S, Cohn D, Marom G (1985) J Mater Sci Lett 4:1233. doi: https://doi.org/10.1007/BF00723467 CrossRefGoogle Scholar
  15. 15.
    Chambers JJ (1986) Parallel-lay aramid ropes for use as tendons in prestressed concrete. PhD thesis submitted to the University of LondonGoogle Scholar
  16. 16.
    Alwis KGNC, Burgoyne CJ (2005) J Compos Constr 9(2):106. doi: https://doi.org/10.1061/(ASCE)1090-0268(2005)9:2(106) CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC 2008

Authors and Affiliations

  1. 1.WS AtkinsSurreyUK
  2. 2.Department of EngineeringUniversity of CambridgeCambridgeUK

Personalised recommendations