Texture and microstructural development in gelcast barium hexaferrite

  • D. B. Hovis
  • K. T. FaberEmail author
  • E. A. Kenik
Article

Abstract

The development of texture in barium hexaferrite by templated grain growth was studied as a function of the Fe2O3/BaCO3 ratio, B2O3 additions in the starting materials, and sintering temperature. A magnetic field was used to orient the template particles during the gelcasting process. Excess BaCO3 resulted in abnormal grain growth and maximized texture, while B2O3 additions promoted coarsening, but no abnormal grain growth.

Keywords

B2O3 BaCO3 Orientation Image Microscopy Barium Hexaferrite Texture Direction 

Notes

Acknowledgements

This work was supported by the National Science Foundation under Grant Nos. DMR-9800257 and DMR-0520513. A portion of the electron microscopy was conducted in the SHaRE User Facility at the Oak Ridge National Laboratory, which is sponsored by the Division of Scientific User Facilities, Office of Science, U.S. Department of Energy.

References

  1. 1.
    Seabaugh MM, Kerscht IH, Messing GL (1997) J Am Ceram Soc 80:1181CrossRefGoogle Scholar
  2. 2.
    Suvaci E, Seabaugh MM, Messing GL (1999) J Eur Ceram Soc 19:2465CrossRefGoogle Scholar
  3. 3.
    Duran C, Trolier-McKinstry S, Messing GL (2000) J Am Ceram Soc 83:2203CrossRefGoogle Scholar
  4. 4.
    Gonenli IE, Messing GL (2001) J Eur Ceram Soc 21:2495CrossRefGoogle Scholar
  5. 5.
    Hovis DB, Faber KT (2001) Scripta Mater 44:2525CrossRefGoogle Scholar
  6. 6.
    Messing GL, Sabolsky EM, Kwon S, Trolier-McKinstry S (2002) Key Eng Mater 206–2:1293Google Scholar
  7. 7.
    Paulik SW, Faber KT, Fuller ER Jr (1994) J Am Ceram Soc 77:454CrossRefGoogle Scholar
  8. 8.
    Zimmerman MH, Faber KT, Fuller ER Jr (1997) J Am Ceram Soc 80:2725CrossRefGoogle Scholar
  9. 9.
    Zimmerman MH, Baskin DM, Faber KT, Fuller ER Jr, Allen AJ, Keane DT (2001) Acta Mater 49:3231CrossRefGoogle Scholar
  10. 10.
    Lacour C, Paulus M (1975) Physica Status Solidi A Appl Res 27:441CrossRefGoogle Scholar
  11. 11.
    Lacour C, Paulus M (1975) Physica Status Solidi A Appl Res 28:71CrossRefGoogle Scholar
  12. 12.
    Steier HP, Requena J, Moya JS (1999) J Mater Res 14:3647CrossRefGoogle Scholar
  13. 13.
    Ozkan OT, Erkalfa H, Yildirim A (1994) J Eur Ceram Soc 14:351CrossRefGoogle Scholar
  14. 14.
    Fang TT, Hwang B, Shiau FS (1989) J Mater Sci Lett 8:1386CrossRefGoogle Scholar
  15. 15.
    Ha JS (2000) Ceram Int 26:251CrossRefGoogle Scholar
  16. 16.
    ASTM C373–88 (1999) Standard test method for water absorption, bulk density, apparent porosity and apparent specific gravity of fired whiteware products, ASTM International, West Conshohocken, PAGoogle Scholar
  17. 17.
    Field DP (1997) Ultramicroscopy 67:1CrossRefGoogle Scholar
  18. 18.
    Schwarzer RA (1997) Micron 28:249CrossRefGoogle Scholar
  19. 19.
    Seabaughs MM, Vaudin MD, Cline JP, Messing GL (2000) J Am Ceram Soc 83:2049CrossRefGoogle Scholar
  20. 20.
    Suvaci E, Messing GL (2000) J Am Ceram Soc 83:2041CrossRefGoogle Scholar
  21. 21.
    Hillert M (1965) Acta metall 13:227CrossRefGoogle Scholar
  22. 22.
    Batti P (1969) Annali Di Chimica 50:1461Google Scholar
  23. 23.
    Goto Y, Takada T (1960) J Am Ceram Soc 43:150CrossRefGoogle Scholar
  24. 24.
    Van Hook H (1964) J Am Ceram Soc 47:579CrossRefGoogle Scholar
  25. 25.
    Cho SH, Nam HD (1982) Mater Res Bull 17:1265CrossRefGoogle Scholar
  26. 26.
    Levin EM (1959) In: Reser MK (ed) Phase diagrams for ceramists. The American Ceramic Society, Columbus, OHGoogle Scholar
  27. 27.
    Wittenauer MA, Nyenhuis JA, Schlindler AI, Sato H, Friedlaender FJ, Truedson J, Karim R, Patton CE (1993) J Cryst Growth 130:533CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC 2008

Authors and Affiliations

  1. 1.Department of Materials Science and EngineeringRobert R. McCormick School of Engineering and Applied Science, Northwestern UniversityEvanstonUSA
  2. 2.Materials Science and Technology DivisionOak Ridge National LaboratoryOak RidgeUSA
  3. 3.Department of Materials Science and EngineeringCase Western Reserve UniversityClevelandUSA

Personalised recommendations