Effect of flexure induced transverse crack and self-healing on chloride diffusivity of reinforced mortar

  • Mustafa ŞahmaranEmail author
Article

Abstract

Cracks in reinforced concrete are unavoidable. Durability is of increasing concern in the concrete industry, and it is significantly affected by the presence of cracks. The corrosion of reinforcing steel due to chloride ions in deicing salts or sea-water is a major cause of premature deterioration of reinforced concrete structures. Although, it is generally recognized that cracks accelerate the ingress of chlorides in concrete, a lack of consensus on this subject does not yet allow reliable quantification of their effects. The present work studies the relationship between crack widths and chloride diffusivity. Flexural load was introduced to generate cracks of width ranging between 29 and 390 μm. As crack width was increased, the effective diffusion coefficient was also increased, thus reducing the initiation period of corrosion process. For cracks with widths less than 135 μm, the effect of crack widths on the effective diffusion coefficient of mortar was found to be marginal, whereas for crack widths higher than 135 μm the effective diffusion coefficient increased rapidly. Therefore, the effect of crack width on chloride penetration was more pronounced when the crack width is higher than 135 μm. Results also indicate that the relation between the effective diffusion coefficient and crack width was found to be power function. In addition, a significant amount of self-healing was observed within the cracks with width below 50 μm subjected to NaCl solution exposure. The present research may provide insight into developing design criteria for a durable concrete and in predicting service life of a concrete structures.

Keywords

Crack Width Effective Diffusion Coefficient Chloride Diffusion Mortar Specimen Chloride Penetration 

References

  1. 1.
    De Schutter G (2000) In: Durability of marine concrete structures damaged by early age thermal cracking. International RILEM Workshop on Life Prediction and Aging Management of Concrete Structures, Cannes, France, Oct. 16–17, 2000Google Scholar
  2. 2.
    Poulsen E (2006) Diffusion of chloride in concrete: theory and application. Taylor & Francis, LondonGoogle Scholar
  3. 3.
    Raharinaivo A, Brevet P, Grimaldi G, Pannier G (1986) In: Relationship between concrete deterioration and reinforcing-steel corrosion. Durability of building materials, vol 4, pp 97–112Google Scholar
  4. 4.
    Gowripalan N, Sirivivatnanon V, Lim CC (2000) J Cement Concrete Res 30(5):725CrossRefGoogle Scholar
  5. 5.
    Mangat PS, Gurusamy K (1987) J Cement Concrete Res 17(3):385CrossRefGoogle Scholar
  6. 6.
    Rodriguez OG, Hooton RD (2003) ACI Mater J 100(2):120Google Scholar
  7. 7.
    Konin A, Francois R, Arliguie G (1998) Mater Struct 31(209):310CrossRefGoogle Scholar
  8. 8.
    Francois R, Arliguie G (1999) Mag Concrete Res 51(2):143CrossRefGoogle Scholar
  9. 9.
    Aldea CM, Shah SP, Karr A (1999) J Mater Civil Eng 11(3):181CrossRefGoogle Scholar
  10. 10.
    ACI Committee 224R (2001) Control of cracking in concrete structures, ACI 224-01. American Concrete Institute, Detroit, MichiganGoogle Scholar
  11. 11.
    ACI Committee 318 (1995) Building code requirements for reinforced concrete, ACI 318-95. American Concrete Institute, Detroit, MichiganGoogle Scholar
  12. 12.
    ACI Committee 350 (1989) Environmental engineering concrete structures, ACI 350R-89. American Concrete Institute, Detroit, MichiganGoogle Scholar
  13. 13.
    AASHTO (1998) LRFD bridge design specifications, 2nd ed. American Association of State Highway and Transportation Officials, Washington, DCGoogle Scholar
  14. 14.
    CAN3-A23.3-M84 (1984) Design of concrete structures for buildings. Canadian Standards Association, OntarioGoogle Scholar
  15. 15.
    CEB-FIB Model Code 1990 (1993) CEB information report no. 213/214. Comite Euro-International DuBeton, LausanneGoogle Scholar
  16. 16.
    Code of practice for the structural use of concrete – part 1. Design, materials and workmanship. British Standards Institution Publication CP 110, London, England, May 1977Google Scholar
  17. 17.
    Standard specification for design and construction of concrete structures – part 1 (Design). Japan Society of Civil Engineers, SP-1, Tokyo, Japan, 1986Google Scholar
  18. 18.
    U.S. Bureau of Public Roads – Bridge Division (1967) Strength and serviceability criteria – reinforced concrete bridge members. U.S. Department of Transportation, Washington, DCGoogle Scholar
  19. 19.
    AASHTO (2001) Standard method of test for resistance of concrete to chloride ion penetration, AASHTO T 259-80. AASHTO, USAGoogle Scholar
  20. 20.
    AASHTO (2001) Standard method of test for sampling and testing for chloride ion in concrete and concrete raw materials, AASHTO T 260-97. AASHTO, USAGoogle Scholar
  21. 21.
    Crank J (1975) The mathematics of diffusion, 2nd edn. Oxford University Press, LondonGoogle Scholar
  22. 22.
    Tognazzi C, Ollivier J-P, Carcasses M, Torrenti J-M (1998) In: Petit Ch, Pijaudier-Cabot G, Reynouard JM (eds) Couplage Fissuration-De´gradation Chimique des Mate´riaux Cimentaires: Premiers Re´sultats sur les Proprie´te´s de Transfert, Ouvrages, ge´omate ´riaux et interactions. Herme’s, Paris, pp 69–84Google Scholar
  23. 23.
    Gerard B, Reinhardt HW, Breysse D (1997) In: Reinhardt HW (ed) Measured transport in cracked concrete, penetration and permeability of concrete. RILEM, France, Report 16, pp 123–153Google Scholar
  24. 24.
    Evardsen C (1999) ACI Mater J 96(4):448Google Scholar
  25. 25.
    Reinhardt HW, Jooss M (2003) J Cement Concrete Res 33(7):981CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC 2007

Authors and Affiliations

  1. 1.Department of Civil EngineeringGaziantep UniversityGaziantepTurkey

Personalised recommendations