Effects of nanocrystalline ferrite particles on densification and magnetic properties of the NiCuZn ferrites
- 155 Downloads
Effects of nanocrystalline ferrite particles addition on densification behavior and magnetic properties of the NiCuZn ferrites were investigated. It was confirmed that nanocrystalline ferrite particles enhanced densification of the samples obviously. The reason was attributed to the nanocrystalline particles, which spread around the micron-sized ferrite particles, increased contacting area and inter-diffusion of the particles. When the amount of nanocrystalline particles addition reached to 30 wt%, the samples obtained an approximate densification behavior as the 1.5 wt% Bi2O3 added samples. Due to relatively bigger grain size, higher sintering density and no different chemical composition sintering aids added, the sample with 30wt% nanocrystalline ferrite particles got the highest permeability and relatively high Q-factor when sintered at 900.
KeywordsFerrite Bi2O3 Surface Free Energy Sinter Density Increase Sinter Temperature
This work is supported by the National Fund for Distinguished Young Scholars (No. 60425102) and Youths' Teacher Supporting Project of University of Electronic Science and Technology of China (UESTC).