, Volume 42, Issue 8, pp 2598–2602 | Cite as

On the origin of blue-green luminescence in spray pyrolysed ZnO thin films

  • P. M. Ratheesh KumarEmail author
  • K. P. Vijayakumar
  • C. Sudha Kartha
Article

Abstract

Origin of the well-known blue-green emission of spray pyrolysed ZnO thin films has been discussed on the basis of variation of the properties due to different treatment of the samples such as ion beam irradiation and doping. 120 MeV Au ions and 80 MeV Ni ions were used for ion beam irradiation while indium was used for doping studies. It was assumed that, Au ions might have produced huge amount of defects while the defects might be less in Ni irradiated films due to the difference in energy and mass number. Photoluminescence studies of pristine sample showed only one emission at 517 nm at room temperature while the irradiated films showed a decrease in intensity of this emission. Indium doping also reduced the intensity of this emission. But additional emissions were also observed in these films. Based on the observations, we proposed that the blue-green emission was due to the transition from conduction band to the level due to oxygen antisite (OZn).

Keywords

Oxygen Vacancy Zinc Vacancy Irradiate Film Chemical Spray Pyrolysed Indium Doping 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Notes

Acknowledgement

One of the authors (PMR) is grateful to Ministry of Non-Conventional Energy (MNES), India for the financial assistance through National Renewable Energy (NRE) Fellowship. Another author (KPV) is grateful to the Cochin University of Science and Technology for granting him sabbatical leave to do this work. Authors acknowledge Dr. Fouran Singh, Nuclear Science Center, New Delhi for PL measurements. Assistance from UGC, India through DSA II scheme is also gratefully acknowledged.

References

  1. 1.
    Sano M, Miyamoto K, Kato H, Yao T (2004) J Appl Phys 95:5527CrossRefGoogle Scholar
  2. 2.
    Norton DP, Heo YM, Ivill MP, Ip K, Pearton SJ, Chisholm MF, Steiner T (2004) Mater Today 7(6):34CrossRefGoogle Scholar
  3. 3.
    Heo YW, Norton DP, Pearton SJ (2005) J Appl Phys 98:73502CrossRefGoogle Scholar
  4. 4.
    Ratheesh Kumar PM, Sudha Kartha C, Vijayakumar KP, Singh F, Avasthi DK, Abe T, Kashiwaba Y, Okram GS, Kumar M, Sarvesh Kumar M (2005) J Appl Phys 97:13509CrossRefGoogle Scholar
  5. 5.
    Garces NY, Wang L, Bai L, Giles NC, Halliburton LE, Cantwell G (2001) Appl Phys Lett 81:2285Google Scholar
  6. 6.
    Studenikin SA, Golego N, Cocivera M (1998) J Appl Phys 84:2287CrossRefGoogle Scholar
  7. 7.
    Minami T, Nanto H, Takata S (1981) J Lumin 24/25:63CrossRefGoogle Scholar
  8. 8.
    Kang HS, Kang JS, Kim JW, Lee SY (2004) J Appl Phys 95:1246CrossRefGoogle Scholar
  9. 9.
    Vanheusden K, Seager CH, Warren WL, Tallant DR, Voigt JA (1996) Appl Phys Lett 68:403CrossRefGoogle Scholar
  10. 10.
    Egelhaaf H.-J., Oelkrug D (1996) J Cryst Growth 161:190CrossRefGoogle Scholar
  11. 11.
    Xu PS, Sun YM, Shi CS, Xu GFQ, Pan HB (2003) Nucl Instrum Meth Phys Res B 199:286CrossRefGoogle Scholar
  12. 12.
    Lin B, Fu Z, Jia Y (2001) Appl Phys Lett 79:943CrossRefGoogle Scholar
  13. 13.
    Hur T-B, Jeen GS, Hwang Y-H, Kim H-K (2003) J Appl Phys 94:5787CrossRefGoogle Scholar
  14. 14.
    Kityk IV, Ebothe J, Hichou AE, Addou M, Bougrine A, Sahraouni B (2002) J Phys Condens Matter 14:5407CrossRefGoogle Scholar
  15. 15.
    Van Vechten JA (1975) J Electrochem Soc 122:419CrossRefGoogle Scholar
  16. 16.
    Sun YM (2000) Ph.D. Thesis, University of Science and Technology of China, July 2000Google Scholar
  17. 17.
    Ortiz A, Falcony C, Hernandez AJ, Garcia M, Alonso JC (1997) Thin Solid Films 293:103CrossRefGoogle Scholar
  18. 18.
    Jin BJ, Im S, Lee SY (2000) Thin Solid Films 366:107CrossRefGoogle Scholar
  19. 19.
    Wang YG, Lau SP, Zhang XH, Lee HW, Hng HH, Tay BK (2003) J Crystal Growth 252:265CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC 2006

Authors and Affiliations

  • P. M. Ratheesh Kumar
    • 1
    Email author
  • K. P. Vijayakumar
    • 1
  • C. Sudha Kartha
    • 1
  1. 1.Department of PhysicsCochin University of Science and TechnologyCochinIndia

Personalised recommendations