Crack growth in structural adhesive joints in aqueous environments

  • A. J. Kinloch
  • C. F. Korenberg
  • K. T. Tan
  • J. F. Watts
Article

Abstract

The adhesive fracture energy, Gc, of metallic joints, bonded with a rubber-toughened epoxy adhesive, has been measured using monotonically-loaded tests. Such tests have been conducted in various relative humidities and in water, at 21 °C. Two surface pretreatments have been employed for the substrates prior to bonding: a simple grit-blast and degrease (‘GBD’) pretreatment or a grit-blast, degrease and silane primer (‘GBS’) pretreatment. The joints were formed using metallic substrates which were either (a) aluminium-alloy substrates, (b) steel substrates, or (c) ‘dissimilar’ substrates (i.e. one substrate being aluminium-alloy with the other one being steel). For both test environments, when Gc was plotted against the crack velocity, three regions of fracture behaviour could be distinguished. At low rates of displacement the crack grew in a stable manner, visually along the interface, and relatively low crack velocities could be readily measured. This was termed ‘Region I’ and here the value of Gc measured in the aqueous environment was relatively low compared to that measured in a relatively dry environment of 55% relative humidity. On the other hand, at relatively high rates of displacement the crack always grew in a stick-slip manner mainly cohesively in the adhesive layer at approximately 20 km/min. This was termed ‘Region III’, and here the value of Gc was relatively high and independent of the environmental test conditions employed. In this region the crack was considered to grow faster than the water molecules were able to reach the crack tip, which explains the independence of Gc upon the test environment. In between ‘Region I’ and ‘Region III’, a transition region was observed which was designated as ‘Region II’. The major effect of the ‘GBS’ pretreatment, compared to the ‘GBD’ pretreatment, was to increase the value of Gc both in ‘Regions I and III’, although the presence of the silane primer had the far greater effect in ‘Region I’.

Keywords

Adhesive Layer Crack Velocity Dissimilar Joint Surface Pretreatment Unstable Crack Growth 

Notes

Acknowledgements

The authors would like to thank Dr. D. Tod (QinetiQ) for financial support. They also wish to thank Mr. Steve Greaves of the University of Surrey for conducting the XPS studies and Professor Jim Castle for invaluable discussions regarding corrosion phenomena.

References

  1. 1.
    Kinloch AJ (ed) (1983) Durability of structural adhesives. Applied Science Publishers, LondonGoogle Scholar
  2. 2.
    Kinloch AJ (1987) Adhesion and adhesives: science and technology. Chapman and Hall, LondonCrossRefGoogle Scholar
  3. 3.
    Kinloch AJ (1997) Proc Inst Mech Eng 211(Part G):307Google Scholar
  4. 4.
    Digby RP, Shaw SJ (1998) Int J Adhes Adhes 18:261CrossRefGoogle Scholar
  5. 5.
    Blackman BRK, Hadavinia H, Kinloch AJ, Paraschi M, Williams JG (2003) Eng Fract Mech 70:233CrossRefGoogle Scholar
  6. 6.
    O’Brien FEM (1948) J Sci Instrum 25:73CrossRefGoogle Scholar
  7. 7.
    Wiederhorn SM (1967) J Am Ceram Soc 50:407CrossRefGoogle Scholar
  8. 8.
    Arnott DR, Kindermann MR (1995) J Adhesion 48:101CrossRefGoogle Scholar
  9. 9.
    Gurumurthy CK, Kramer EJ, Hui CY (2001) Int J Fract 109:1CrossRefGoogle Scholar
  10. 10.
    Lane MW, Snodgrass JM, Dauskardt RH (2001) Microelect Reliab 41:1615CrossRefGoogle Scholar
  11. 11.
    Snodgrass JM, Pantelidis D, Jenkins ML, Bravman JC, Dauskardt RH (2002) Acta Mater 50:2395CrossRefGoogle Scholar
  12. 12.
    Kook SY, Dauskardt RH (2002) J Appl Phys 91:1293CrossRefGoogle Scholar
  13. 13.
    Strohband S, Dauskardt RH (2003) Interface Sci 11:11CrossRefGoogle Scholar
  14. 14.
    Gurumurthy CK, Kramer EJ, Hui CY (2006) J Adhesion 82:239CrossRefGoogle Scholar
  15. 15.
    Curley AJ, Hadavinia H, Kinloch AJ, Taylor AC (2000) Int J Fract 103:41CrossRefGoogle Scholar
  16. 16.
    Gledhill RA, Kinloch AJ (1975) J Mater Sci Lett 10:1261CrossRefGoogle Scholar
  17. 17.
    Arnott DR, Kindermann MR (1995) J Adhesion 48:85CrossRefGoogle Scholar
  18. 18.
    Korenberg CF, Kinloch AJ, Watts JF (2005) J Adhesion 80:169CrossRefGoogle Scholar
  19. 19.
    Maugis D (1980) J Mater Sci 20:3041CrossRefGoogle Scholar
  20. 20.
    Gledhill RA, Kinloch AJ (1974) J Adhesion 6:315CrossRefGoogle Scholar
  21. 21.
    Kinloch AJ, Dukes WA, Gledhill RA (1975) Adhesion science and technology, 9B. Plenum Press, New York, p 597CrossRefGoogle Scholar
  22. 22.
    Yahalom J, Aladjem A (eds) (1980) Stress corrosion cracking. Freund, Tel AvivGoogle Scholar
  23. 23.
    Gettings M, Kinloch AJ (1977) J Mater Sci 12:2511CrossRefGoogle Scholar
  24. 24.
    Plueddeman EP (ed) (1982) Silane coupling agents. Plenum Press, New YorkGoogle Scholar
  25. 25.
    Davis SJ, Watts JF (1996) Int J Adhes Adhes 16:5CrossRefGoogle Scholar
  26. 26.
    Abel M-L, Digby RP, Fletcher IW, Watts JF (2000) Surf Interface Anal 29:115CrossRefGoogle Scholar
  27. 27.
    Davis SJ, Watts JF (1996) J Mater Chem 6:479CrossRefGoogle Scholar
  28. 28.
    Watts JF, Castle JE (1983) J Mater Sci 18:2987CrossRefGoogle Scholar
  29. 29.
    Lediheiser H (1987) J Adhes Sci Technol 1:79CrossRefGoogle Scholar
  30. 30.
    Castle JE, Epler DC (1975) Surf Sci 53:286CrossRefGoogle Scholar
  31. 31.
    Rattana A, Hermes JD, Abel M-L, Watts JF (2002) Int J Adhes Adhes 22:205CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC 2007

Authors and Affiliations

  • A. J. Kinloch
    • 1
  • C. F. Korenberg
    • 1
    • 3
  • K. T. Tan
    • 1
    • 4
  • J. F. Watts
    • 2
  1. 1.Department of Mechanical EngineeringImperial College LondonLondonUK
  2. 2.The Surface Analysis Laboratory, School of EngineeringUniversity of SurreyGuildfordUK
  3. 3.British MuseumLondonUK
  4. 4.NISTGaithersburgUSA

Personalised recommendations