Repair of directionally solidified superalloy GTD-111 by laser-engineered net shaping

  • Leijun Li
Article

Abstract

GTD-111 directionally solidified superalloy was repaired by the Nd:YAG laser based laser-engineered net shaping (LENS) process. Selection of process parameters are discussed against the formation of deposits and occurrence of defects. Formation of microfissures, porosity, lack of fusion, and stray crystals in the deposit zone was studied. It was identified that formation of stray crystals in the directionally solidified alloy could be due to two types of sources: the shape of the melt pool, and the existence of second-phase particles at the melt pool fusion boundary.

Keywords

Weld Pool Post Weld Heat Treatment Molten Pool Post Weld Heat Treatment Deposit Zone 

Notes

Acknowledgements

The author would like to thank Ms. Anne Koleman of General Electric for providing the GTD-111 bucket test material and research assistants Mr. Michael Harrison and Mr. Tian Tang for helping with the experiments.

References

  1. 1.
    Daleo JA, Wilson JR (1998) J Eng Gas Turbine Power 120:375CrossRefGoogle Scholar
  2. 2.
    Sims CT, Stoloff NS, Hagel WC (1987) Superalloy II. John Wiley & Sons, New York, p 98Google Scholar
  3. 3.
    Liu W, DuPont JN (2003) Scripta Mat 48:1337CrossRefGoogle Scholar
  4. 4.
    Liu W, DuPont JN (2003) Met Trans A 34A:1337Google Scholar
  5. 5.
    Messler RW Jr (1999) Principles of welding. John Wiley & Sons, p 428Google Scholar
  6. 6.
    Kurz W, Fisher DJ (1989) Fundamentals of solidification, 3rd edn. Trans Tech PublicationsGoogle Scholar
  7. 7.
    David SA,Vitek JM, Babu SS, Boatner LA, Reed RW (1997) Sci Technol Welding Joining 2(2):79–88CrossRefGoogle Scholar
  8. 8.
    Liu W, DuPont JN (2004) Acta Mater 52:4833Google Scholar
  9. 9.
    Li L, Messler RW Jr (2002) Mat Met Trans A 33A(7):2031CrossRefGoogle Scholar
  10. 10.
    Park JW et al (2003) J Appl PhysGoogle Scholar
  11. 11.
    Sajjadi SA et al (2002) Mater Sci Eng A325, p 484Google Scholar
  12. 12.
    Gaumann M, Bezencon C, Canalis P, Kurz W (2001). Acta Mater 49:1051CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC 2006

Authors and Affiliations

  1. 1.Department of Mechanical & Aerospace EngineeringUtah State UniversityLoganUSA

Personalised recommendations