, Volume 42, Issue 12, pp 4170–4176 | Cite as

X-ray irradiation induced optical absorptions in silver and manganese doped soda-lime silicate glass

  • Jiawei Sheng
  • Liqiang JiangEmail author
Article
  • 84 Downloads

Abstract

Silver nanoclusters formation was observed in Ag-doped or Ag–Mn-doped soda-lime silicate glasses after X-ray irradiation followed by thermal annealing. Silver nanoclusters were formed with mean-size of about 3 nm after heating at 420 °C for 1 h in Ag-doped glass, and were disappeared after heating at 600 °C for 1 h. Mn3+ was formed in Mn-doped glass after X-ray irradiation followed by heating at 400 °C for 1 h, and was reduced to Mn2+ upon subsequently heating at 600 °C for 1 h. The presence of Mn3+ led to a purple color, while the silver nanoclusters provided a yellow color in the glass. The Ag-doped or Mn-doped glass may be viable as recyclable coloration glasses. In Ag–Mn-doped glass silver nanoclusters were formed only after heating at a high temperature of 600 °C following the irradiation. In addition, manganese showed a similar X-ray-induced behavior in the Mn-doped glass and the Ag–Mn-doped glass. In contrast, silver behaved differently in the Ag-doped glass and the Ag–Mn-doped glass. Unlike those in Ag-doped glass, the silver nanoclusters would not be dissolved in Ag–Mn-doped once they were formed.

Keywords

Electron Spin Resonance Electron Spin Resonance Spectrum Thermal Annealing Electron Spin Resonance Signal Ag2O 

Notes

Acknowledgements

The author gratefully acknowledges the financial support for this work from Zhejiang Provincial Natural Science Foundation of China (R404108), Zhejiang Provincial Special Hired Professor Foundation, and Scientific Research Foundation of Zhejiang Provincial Education Department (20040556). Dr Bill X. Huang of NIH/NIAAA were acknowledged for the English improvement.

References

  1. 1.
    Weyl WR (1959) Coloured glasses. Dawson’s of Pall Mall, London, p 89Google Scholar
  2. 2.
    Wong J, Angell CA (1976) Glass: structure by spectroscopy. Marcel Dekker, New York, p 191Google Scholar
  3. 3.
    Yamashita M, Yao Z, Matsumoto Y, Utagawa Y, Kadono K, Yazawa T (2004) J Non-Cryst Solids 333:37CrossRefGoogle Scholar
  4. 4.
    Sheng J, Kadono K, Yazawa T (2002) Glass Tech 43:238Google Scholar
  5. 5.
    Sheng J, Kadono K, Yazawa T (2004) Phys Chem Glass 45:27Google Scholar
  6. 6.
    Sheng J, Kadono K, Utagawa Y, Yazawa T (2002) Appl Radiat Isot 56:621CrossRefGoogle Scholar
  7. 7.
    Jiang L (2004) Phys Chem Glass 45:291Google Scholar
  8. 8.
    Jiang L, Sheng J (2005) J Mater Sci 39:5177CrossRefGoogle Scholar
  9. 9.
    Borsella E, Gonella F, Mazzoldi P, Quaranta A, Battaglin G, Polloni R (1998) Chem Phys Lett 284:429CrossRefGoogle Scholar
  10. 10.
    Friebele EJ (1991) In: Uhlmann DR, Kreidl NJ (eds) Optical and properties of glass. American Ceramic Society, Westerville, OH, p 205Google Scholar
  11. 11.
    Marshall CD, Speth JA, Payne SA (1997) J Non-Cryst Solids 212:59CrossRefGoogle Scholar
  12. 12.
    Griscom DL (1984) J Non-Cryst Solids 64:229CrossRefGoogle Scholar
  13. 13.
    Rajaram M, Friebele EJ (1989) J Non-Cryst Solids 108:1CrossRefGoogle Scholar
  14. 14.
    Johnson PB, Christy RW (1972) Phys Rev B 6:4370CrossRefGoogle Scholar
  15. 15.
    Arnold GW, Borders JA (1977) J Appl Phys 48:1488CrossRefGoogle Scholar
  16. 16.
    Peters DP, Strohhofer C, Brongersma ML, van der Elsken J, Polman A (2000) Nucl Instr Meth B 168:237CrossRefGoogle Scholar
  17. 17.
    Takeda S, Yamamoto K, Matsumoto K (2000) J Non-Cryst Solids 265:133CrossRefGoogle Scholar
  18. 18.
    Gangopadhyay P, Magudapathy P, Kesavamoorthy R, Panigrahi BK, Nair KGM, Satyam PV (2004) Chem Phys Lett 388:416CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC 2007

Authors and Affiliations

  1. 1.College of Chemical Engineering and Materials ScienceZhejiang University of TechnologyHangzhouChina

Personalised recommendations