, Volume 42, Issue 12, pp 4418–4427 | Cite as

Co-precipitation synthesis of Nd:YAG nano-powders: the effect of Nd dopant addition with thermal treatment

  • Eugenio Caponetti
  • Maria Luisa Saladino
  • Filomena Serra
  • Stefano EnzoEmail author
Article

Abstract

Nanopowders of Yttrium Aluminium Garnet doped with neodymium ions were obtained by the co-precipitation method from the reaction of aluminium, yttrium and neodymium nitrate with ammonia. The amount of neodymium was selected in order to produce samples of nominal stoichiometry NdXY(3–X)Al5O12 (where X = 0.006, 0.012, 0.024, 0.048, 0.081, 0.096, 0.17, 0.19, 0.38, 0.54, and 0.72, respectively). After washing and drying, the hydroxide precursors were subjected to Thermo-Gravimetry and Differential Thermal Analysis experiments from room temperature up to 1500 °C, which showed the presence of exothermal events accompanying phase transformation phenomena. X-ray diffraction investigations conducted with a high-resolution powder diffractometer on the specimens arrested at selected temperature of the thermograms, evidenced the amorphous-to-crystalline transformation phenomena leading to the garnet phase as the main product. On increasing the concentration of Nd, the presence of the monoclinic Y4Al2O9 phase was also detected together with a variable amount of a metastable hexagonal YAlO3 phase. Precise determination of the cubic garnet lattice parameters as a function of the neodymium content according to the Rietveld method shows a change from the value of 12.016 (±2) Å when X = 0 up to 12.128 (±2) Å for X = 0.720 with two distinctive regimes of increase. The line broadening analysis of X-ray profiles after correction for instrumental factors indicates that the average crystallite size is in the range 50–80 nm. Field-Emission Gun-Scanning Electron Microscopy observations showed the presence of aggregation features in the powders with a rounded morphology and a relatively uniform and narrow particle size distribution, with the average size figures in substantial agreement with the diffraction analyses.

Keywords

Neodymium Yttrium Aluminium Garnet YAlO3 Isothermal Treatment Garnet Phase 

Notes

Acknowledgements

This work is carried out within two collaborative Projects, entitled “Nanostructured Luminescent Oxides”, and “Synthesis of nanopowders assisted by microwaves” respectively, funded by the Italian Ministry for Education, University and Science (PRIN call 2003).

We acknowledge useful discussions with prof. G. Cocco, L. Schiffini (Univ. of Sassari, Italy) and prof. M. Baricco (Univ. of Torino, Italy) on the phase metastability.

We thank Dr. G. M. Ingo and Tilde De Caro (ISMN-CNR Montelibretti, Roma, Italy) for FEG-SEM micrographs, Dr. P. Guerra (Dipartimento di Ingegneria Chimica dei Processi e dei Materiali—Univ. of Palermo, Italy) for EDX analysis and Dr. Luca Lutterotti for making available a copy of the programme MAUD running in a personal computer. (http://www.ing.unitn.it/∼luttero/).

References

  1. 1.
    Katsurayama M, Anzai Y, Sugiyama A, Koike M, Kato Y (2001) J Cryst Growth 229:193CrossRefGoogle Scholar
  2. 2.
    Ikesue A (2002) Opt Mater 19:183CrossRefGoogle Scholar
  3. 3.
    Ravichandran D, Roy R, Chakhovskhoi AG, Hunt CE, White WB, Erdei S (1997) J. Lumin 71:291CrossRefGoogle Scholar
  4. 4.
    Leleckaite A, Kareiva A (2004) Opt Mater 26:123CrossRefGoogle Scholar
  5. 5.
    Sim S-M, Keller KA, Mah T-I (2000) J Mater Sci 35:713CrossRefGoogle Scholar
  6. 6.
    Guang Li J, Ikegami T, Lee J-H, Mori T. Yajima Y (2000) J Eur Ceram Soc 20:2395CrossRefGoogle Scholar
  7. 7.
    Chen T-M, Chen SC, Yu C-J (1999) J Sol State Chem 144:437CrossRefGoogle Scholar
  8. 8.
    Marchal J, Hinklin T, Baranwal R, Johns T, Laine RM (2004) Chem Mater 16:822CrossRefGoogle Scholar
  9. 9.
    Johnson BR, Kriven WM (2001) J Mater Res 16:1796CrossRefGoogle Scholar
  10. 10.
    Ghandi AS, Levi CG (2005) J Mater Res 20:1017CrossRefGoogle Scholar
  11. 11.
    Caponetti E, Saladino ML, Chillura Martino D, Pedone L, Enzo S, Russu S, Bettinelli M, Speghini A (2005) Solid St Phenom 106:7CrossRefGoogle Scholar
  12. 12.
    Wang H, Gao L, Niihara K (2000) Mat Sci Eng A288:1Google Scholar
  13. 13.
    Hsu WT, Hu W, Lu C (2003) Mat Sci Eng B104:40CrossRefGoogle Scholar
  14. 14.
    Young RA (ed) (1993) The Rietveld Method, University Press, OxfordGoogle Scholar
  15. 15.
    Lutterotti L, Gialanella S (1998) Acta Mater 46:101CrossRefGoogle Scholar
  16. 16.
    Wagner CNJ (1966) In: Cohen JB, Hilliard JE (ed) Local Atomic Arrangements studied by X-ray Diffraction, Met Soc Conf, vol 36. Gordon & Breach, New York, p 219Google Scholar
  17. 17.
    Palmero P, Esnouf C, Montanaro L, Fantozzi G (2005) J Eur Ceram Soc 25:1565CrossRefGoogle Scholar
  18. 18.
    Chung B-J et al (2003) J Ceram Process. 4:145–150Google Scholar
  19. 19.
    Li J-G, Ikegami T, Lee J-H, Mori T (2003) J Am Ceram Soc 83:961CrossRefGoogle Scholar
  20. 20.
    Li J-G, Ikegami T, Lee J-H, Mori T, Yajima Y. (2000) J Eur Ceram Soc 20:2395CrossRefGoogle Scholar
  21. 21.
    Hess NJ, Maupin GD, Chick LA, Sunberg DS, McCreedy DE, Armstrong TR (1994) J Mater Sci 29:1873CrossRefGoogle Scholar
  22. 22.
    Cannas C, Musinu A, Piccaluga G, Deidda C, Serra F, Bazzoni M, Enzo S (2005) J Sol State Chem 178:1526CrossRefGoogle Scholar
  23. 23.
    Popa NC (1998) J Appl Crystallogr 31:176CrossRefGoogle Scholar
  24. 24.
    Laine RM, Marchal J, Sun H, Pan XQ (2005) Adv Mater 17:830CrossRefGoogle Scholar
  25. 25.
    Inorganic Crystal Structure Database http://icsdweb.FIZ-Karlsruhe.deGoogle Scholar
  26. 26.
    Carda J, Monros G, Escribano P, Alarcon J (1989) J Am Ceram Soc 72:160CrossRefGoogle Scholar
  27. 27.
    Bertaut EF (1950) Acta Cryst 3:14CrossRefGoogle Scholar
  28. 28.
    Shannon RD, Prewitt CT (1969) Acta Cryst B25:925CrossRefGoogle Scholar
  29. 29.
    Lupei A, Stoicescu C, Lupei V (1977) J Cryst Growth 177:207CrossRefGoogle Scholar
  30. 30.
    Bazzoni M, Bettinelli M, Daldosso M, Enzo S, Serra F, Speghini A (2005) J Sol State Chem 178:2301CrossRefGoogle Scholar
  31. 31.
    Carda J, Monros G, Esteve V, Amigo JM (1994) J Sol State Chem 108:24CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC 2007

Authors and Affiliations

  • Eugenio Caponetti
    • 1
  • Maria Luisa Saladino
    • 1
  • Filomena Serra
    • 2
  • Stefano Enzo
    • 2
    Email author
  1. 1.Dipartimento di Chimica Fisica and INSTM-Udr PalermoPalermoItaly
  2. 2.Dipartimento di Chimica and INSTM-Udr SassariUniversity of SassariSassariItaly

Personalised recommendations