Effect of microstructure on the modulus of PAN-based carbon fibers during high temperature treatment and hot stretching graphitization

  • Dongfeng LiEmail author
  • Haojing Wang
  • Xinkui Wang
Article

Abstract

The changes of microstructure and Young’s modulus of PAN-based carbon fibers during the high temperature treatment (2400–3000 °C, stretching 0%) and hot stretching graphitization (0–5%, 2400 °C) were compared. It was observed that although the Young’s modulus of the fibers could be increased by the two graphitization techniques, the microstructure parameters determined by X-ray diffraction were different for the same value of modulus. The relationship between microstructure and modulus showed that Young’s modulus not only depended on the preferred orientation, but also related to the crystallite size (Lc and La) and shape (La/Lc). On the other hand, it was found that crystallite size of the fibers was mainly affected by heat treatment temperature and the crystallite shape could be altered by hot stretching graphitization. Further investigation indicated that the fibers were composed of turbostratic carbon structure even after heat treated to 3000 °C, which could be detected from the absence of 101 and 112 peaks in X-ray diffraction pattern, and the interlayer spacing (d002) and preferred orientation (Z) were only 0.3430 nm and 14.71°, respectively.

Keywords

Crystallite Size Carbon Fiber Prefer Orientation Heat Treatment Temperature High Temperature Treatment 

Notes

Acknowledgements

This research has been supported by funds from Chinese Academy of Science. The authors wish to thank Professor He Fu of the Key Laboratory of Carbon Materials, Institute of Coal Chemistry, Chinese Academy of Sciences, for useful advice, remarks and suggestions.

References

  1. 1.
    Chand S (2000) J Mater Sci 35:1303CrossRefGoogle Scholar
  2. 2.
    Rubin L (1993) In: Buckley JD, Edie DD (eds) Carbon–carbon materials and composites. Noyes publications, New Jersey, p 267Google Scholar
  3. 3.
    Chung DDL (1994) In: Carbon fiber composites. Butterworth-Heinemann, Newton, p 81CrossRefGoogle Scholar
  4. 4.
    Dorey G (1987) J Phys D: Appl Phys 20:245CrossRefGoogle Scholar
  5. 5.
    Ozbek S, Isaac DH (1994) Mater Manuf Process 9:199CrossRefGoogle Scholar
  6. 6.
    Ozbek S, Isaac DH (2000) Carbon 38:2007CrossRefGoogle Scholar
  7. 7.
    Bacon R (1973) In: Walker PL Jr, Thrower PA (eds) Chemistry and physics of carbon, vol 9. Marcel Dekker, New York, p 1Google Scholar
  8. 8.
    Huang Y, Young RJ (1995) Carbon 33:97CrossRefGoogle Scholar
  9. 9.
    Edie DD (1998) Carbon 36:345CrossRefGoogle Scholar
  10. 10.
    Fitzer E (1989) Carbon 27:621CrossRefGoogle Scholar
  11. 11.
    Endo M (1988) J Mater Sci 23:598CrossRefGoogle Scholar
  12. 12.
    Johnson DJ, Tyson CN (1969) J Appl Phys 2:787Google Scholar
  13. 13.
    Kogure K, Sines G, Gerard LJ (1994) Carbon 32:715CrossRefGoogle Scholar
  14. 14.
    Johnson DJ (1987) J Phys D: Appl Phys 20:286CrossRefGoogle Scholar
  15. 15.
    Ogale AA, Lin C, Anderson DP, Kearns KM (2002) Carbon 40:1309CrossRefGoogle Scholar
  16. 16.
    Johnson DJ (1980) Phil Trans R Soc Lond A 294:443CrossRefGoogle Scholar
  17. 17.
    Johnson DJ (1987) In: Walker PL Jr, Thrower PA (eds) Chemistry and physics of carbon, vol 20. Marcel Dekker, New York, p 1Google Scholar
  18. 18.
    Ruland W (1968) In: Walker PL Jr (ed) Chemistry and physics of carbon, vol 4. Marcel Dekker, New York, p 1Google Scholar
  19. 19.
    Cuesta A, Dhamelincout P, Laureyns A, Martinez-Alonso, Tascon JMD (1998) J Mater Chem 8:2875Google Scholar
  20. 20.
    Jones SP, Fain CC, Fdid DD (1997) Carbon 35:1533CrossRefGoogle Scholar
  21. 21.
    Tuinstra F, Koenig JL (1970) J Chem Phys 53:1126CrossRefGoogle Scholar
  22. 22.
    Melanitis N, Tetlow PL, Galiotis C (1996) J Mater Sci 31:851CrossRefGoogle Scholar
  23. 23.
    Murakami M, Nishiki N, Nakamura K, Ehara J, Okada H, Kouzaki T, Watanabe K, Hoshi T, Yoshimura S (1992) Carbon 30:255CrossRefGoogle Scholar
  24. 24.
    Richards BP (1968) J Appl Crystallogr 1:35CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC 2007

Authors and Affiliations

  1. 1.Key Laboratory of Carbon Materials, Institute of Coal ChemistryChinese Academy of ScienceTaiyuanChina
  2. 2.Graduate University of the Chinese Academy of SciencesBeijingChina
  3. 3.Department of ChemistryXingtai CollegeXingtaiChina

Personalised recommendations