, Volume 41, Issue 18, pp 5900–5906 | Cite as

The development of the microstructural and electrical characteristics of NTC thick-film thermistors during firing

  • Marko Hrovat
  • Darko Belavič
  • Janez Holc
  • Jena Cilenšek
Article

Abstract

One kohm/sq. thick-film NTC thermistors (4993, EMCA Remex) with high, non-linear and negative temperature coefficients of resistivity were fired at different temperatures. The development of the resistors’ conductive phase and microstructure was investigated by X-ray diffraction analysis and by scanning electron microscopy. Sheet resistivities, beta factors and noise indices were measured as a function of the firing temperature. In the fired layers of the thermistors the X-ray analyses showed mainly spinel phase and RuO2, which is added to the thick-film NTC materials to decrease the specific resistance and to improve the stability and the current noise. Higher firing temperatures led to more densely sintered microstructures, to increased resistivities and to higher beta factors. The higher resistivities were attributed to the partial exchange of ions on the “B” sites of the spinel structure with aluminium ions.

Keywords

RuO2 Firing Temperature Spinel Phase Alumina Substrate Glass Phase 

Notes

Acknowledgements

The authors wish to thank Mr. Mitja Jerlah (HIPOT-HYB) for printing and firing the samples as well as for measuring the electrical characteristics. The financial support of the Slovenian Research Agency is gratefully acknowledged.

References

  1. 1.
    Martin de Vidales JL, Garcia-Chain P, Rojas RM, Vila E, Garcia Martinez O (1998) J Mater Sci 33(6):1491CrossRefGoogle Scholar
  2. 2.
    Huang J, Hao Y, Lin H, Zhang D, Song J, Zhou D (2003) Mater Sci Eng B99(1–3):523CrossRefGoogle Scholar
  3. 3.
    M-Prudenziati (ed) (1994) Thick film sensors. Elsevier, Amsterdam, pp 127–150Google Scholar
  4. 4.
    Martinez Sarrion ML, Morales M (1995) J Mater Sci 30(10):2610CrossRefGoogle Scholar
  5. 5.
    Park K, Bang DJ (2003) J Mater Sci: Materials in Electronics 14:81Google Scholar
  6. 6.
    Metz D, Caffin P, Legros R, Rousset A (1989) J Mater Sci 24(1): 83CrossRefGoogle Scholar
  7. 7.
    Metz R (2000) J Mater Sci 35(18):4705CrossRefGoogle Scholar
  8. 8.
    van Loan PR (1972) Ceram Bull 51(3):231, 242Google Scholar
  9. 9.
    Pierce JW, Kuty DW, Larry JR (1982) Solid State Technol 25(10):85Google Scholar
  10. 10.
    Hao YD, Chen LJ, Lin H, Zhou DX, Gong SP (1993) Sensors Actuators A35(3):269Google Scholar
  11. 11.
    Macklen ED (ed) (1979) Thermistors, Electrochemical Publications Ltd., Ayr, pp 16–28Google Scholar
  12. 12.
    Park K (2004) Scripta Materialia 50:551CrossRefGoogle Scholar
  13. 13.
    Hrovat M, Jan F (1987) Hybrid Circuits 14:25Google Scholar
  14. 14.
    Hrovat M, Samardžija Z, Holc J, Belavič D (2002) J Mater Sci 37:2331CrossRefGoogle Scholar
  15. 15.
    Shannon RD (1976) Acta Cryst A32:751CrossRefGoogle Scholar
  16. 16.
    Hrovat M, Benčan A, Belavič D, Holc J, Dražič G (2003) Sensors and Actuators A103:341CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC 2006

Authors and Affiliations

  • Marko Hrovat
    • 1
  • Darko Belavič
    • 2
  • Janez Holc
    • 1
  • Jena Cilenšek
    • 1
  1. 1.Jožef Stefan InstituteLjubljanaSlovenia
  2. 2.HIPOT-R&D, d.o.o.SentjernejSlovenia

Personalised recommendations