Stoichiometry of Silicon Dioxide Films Obtained by Ion-Beam Sputtering
- 8 Downloads
The composition of SiOx films produced by ion-beam sputtering (IBS) of silicon and quartz targets were studied by infrared spectrometry. Films with thicknesses of 150–390 nm were formed on silicon substrates. It was found that increase in the partial pressure of oxygen in the working gas, increase in the temperature of the substrate, and the presence of a positive potential on the target during reactive IBS of silicon shifted the main absorption band νas into the high-frequency region and increased the composition index from 1.41 to 1.85. During IBS of a quartz target the stoichiometry of the films deteriorates with increase of the energy of the sputtering argon ions. This may be due to increase of the deposition rate. Increase in the current of the thermionic compensator, increase of the substrate temperature, and addition of oxygen led to the formation of SiOx films with improved stoichiometry.
Keywordsion-beam sputtering silicon dioxide films IR spectroscopy composition stoichiometry
Unable to display preview. Download preview PDF.
- 1.N. A. Valisheva, A. A. Guzev, A. P. Kovchavtsev, G. L. Kuryshev, T. A. Levtsova, and Z. V. Panova, Mikroélektronika, 38, No. 2, 99–106 (2009).Google Scholar
- 10.H.-D. Kurland, J. Grabow, C. Stötzel, and F. A. Müller, J. Ceram. Sci. Tech., 5, No. 4, 275–280 (2014).Google Scholar
- 11.V. Bhatt, S. Chandra, S. Kumar, C. M. S. Reuthan, and P. N. Dixit, Indian J. Pure Appl. Phys., 45, 377–381 (2007).Google Scholar
- 13.I. Radovič, Y. Serruys, Y. Limoge, M. Milosavlevič, N. Romčevič, and N. Bibič, Optoelectron. Adv. Mater., Rapid Commun., 1, No. 5, 247–251 (2007).Google Scholar
- 14.E. V. Telesh, N. K. Kasinskii, and V. S. Tomal’, Vestn. PGU, No. 4, 121–127 (2012).Google Scholar
- 17.Yu. A. Pentin and L. V. Vilkov, Physical Methods of Investigation in Chemistry, Mir, Moscow [Russian translation] (2006), pp. 199–214.Google Scholar
- 19.M. Misawa, Y. Kobayashi, and K. Suzuki, Proc. Int. Ion Engineering Congress, ISIAT′83 & IPAT′83, Kyoto (1983), pp. 957–962.Google Scholar
- 20.D. S. Veselov and Yu. A. Voronov, J. Phys.: Conf. Ser., 747, 012022 (2016).Google Scholar
- 22.A. P. Dostanko, E. S. Akulich, and V. Ya. Shiripov, Zh. Prikl. Spektrosk., 50, No. 3, 436–439 (1989) [A. P. Dostanko, E. S. Akulich, V. Ya. Shiripov, and S. A. Sobolev, J. Appl. Spectrosc., 50, No. 3, 303–306 (1989)].Google Scholar
- 25.A. P. Dostanko, S. M. Avakov, L. P. Anufriev, S. V. Bordusov, D. A. Golosov, S. M. Zavadskii, N. S. Koval’chuk, A. O. Korobko, V. L. Lanin, S. I. Mafveiko, V. A. Rusetskii, E. V. Telesh, E. A. Titko, and G. A. Trapashko, Integrated Technologies of Micro- and Nanostructured Layers: Monograph [in Russian], Bestprint, Minsk (2013), pp. 157–161.Google Scholar