Fabrication of Geopolymers from Untreated Kaolin Clay for Construction Purposes
- 82 Downloads
A new geopolymeric material has been fabricated from local Saudi Arabian resources using inorganic mineral polymerization technique. In this technique, the mineral polymer is synthesized from the following components: naturally occurring kaolin clay mineral, silica sand, sodium hydroxide, and water. Homogeneous samples of known amounts of clay minerals and silica sand were mixed with different ratios of clay and sand and sodium hydroxide solutions ranging from 13 to 19.7 mol/l. To accelerate the chemical polymerization reaction, the molded reactants were cured at 80 °C in an oven for 24 h to form stable and hard geopolymeric material. The synthesis parameters of mass of clay mineral, sand, NaOH and water were varied according to a statistical analysis design of experiment. The optimum amount of water is limited by the plastic limit of the clay, which is determined to be around 25%. Based on the results of the experimental design a geoploymer with a compressive strength of 27.1 MPa was achieved by sand to kaolin ratio of 1.5, water to kaolin ratio of 0.25 and NaOH to kaolin ratio of 0.17 under dry conditions and 18.1 MPa under wet conditions.
KeywordsKaolin Geopolymers TGA XRD Construction Minerals
The authors would like to acknowledge the support provided by King Abdulaziz City for Science and Technology (KACST) through the Science and Technology Unit at King Fahd University of Petroleum and Minerals (KFUPM) for funding this work through Project No. 11-ADV2131-04 as part of the National Science, Technology and Innovation Plan”.
- Alshaaer M, Cuypers H, Wastiels J (2002) Stabilization of kaolinitic soil for construction purposes by using mineral polymerisation technique. Paper presented at the 6th international conference on concrete technology for developing countries, Amman-Jordan, October, 2002Google Scholar
- Davidovits J (2011) Geopolymer chemistry and applications, 3rd edn. Institut Géopolymère, FranceGoogle Scholar
- El-Maghraby A, Khaled KF, Elsabawy KM (2013) Formation of leucite crystals from metakaolin-based geopolymer using kaolin and bentonite. Int J Chem Sci 11:740–750Google Scholar
- Gogo JO (1990) Geological and geotechnical evaluation of latosols from Ghana, and their improvement for construction. Vrije University of BrusselsGoogle Scholar
- Kim HK, Lee HK (2013) Effects of high volumes of fly ash, blast furnace slag, and bottom ash on flow characteristics, density, and compressive strength of high-strength mortar. J Mater Civ Eng 25:662–665. https://doi.org/10.1061/(asce)mt.1943-5533.0000624 CrossRefGoogle Scholar
- Mohsen Q, Mostafa NY (2010) Investigating the possibility of utilizing low kaolinitic clays in production of geopolymer bricks. J Ceramics-Silikaty 54:160–168Google Scholar
- Mustafa Al Bakri AM, Kamarudin H, Bnhussain M, Khairul Nizar I, Rafiza AR, Izzat AM (2011) Chemical reactions in the geopolymerisation process using fly ash-based geopolymer: a review. Aust J Basic Appl Sci 5:1199–1203Google Scholar
- Nayak B, Mishra BK, Behera S, Kumar V (2012) Composition for building material and a process for the preparation thereof. Google PatentsGoogle Scholar
- Vickers L, van Riessen A, Rickard WA (2015) Chemistry of geopolymers. In: Fire-resistant geopolymers. SpringerBriefs in Materials. Springer, Singapore, pp 39–52. https://doi.org/10.1007/978-981-287-311-8_3