An experimental assessment of the effectiveness of recovery annealing of VVER-1000 vessels on the basis of mechanical tests and structural studies of control samples of the main metal and the weld-seam metal with high nickel content (>1.65%) in the No. 1 unit of the Balakovo nuclear power plant in states after primary irradiation in the control sample channels, annealing in a chosen regime, and repeat accelerated irradiation in the IR-8 research reactor to fluence corresponding to extended service to 60 yr and longer is presented. The mechanical tests and structural studies showed a high degree of recovery of the structure and properties for the chosen temperature–time regime of annealing as well as a lower rate of repeated after the recovery annealing embrittlement as compared with the rate of embrittlement with primary irradiation.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
L. M. Utevskii, E. E. Glikman, and G. S. Kark, Reversible Temper Brittleness of Steel and Iron Alloys, Metallurgiya, Moscow (1985).
Yu. A. Nikolaev, “Radiation embrittlement of Cr–Ni–Mo and Cr–Mo RPV steels,” J. ASTM Intern., 4, No. 8, 1–17 (2007).
S. A. Saltykov, Stoichiometric Metallography, Metallurgiya, Moscow (1976).
P. Kelly, A. Jostsons, R. Blake, and J. Napier, “The determination of foil thickness by scanning transmission electron microscopy,” Phys. Status Solidi (A), 31, 771 (1975).
B. Z. Margolin, A. A. Nikolaev, E. V. Yurchenko, et al., “Analysis of embrittlement of VVER-1000 vessel materials during operation,” Vopr. Materialoved., No. 4(60), 108–123 (2009).
M. K. Miller, A. A. Chernobaeva, Y. I. Shtrombakh, et al., “Evolution of the nanostructure of VVER-1000 RPV materials under neutron irradiation annealing,” J. Nucl. Mater., 385, 615–622 (2009).
E. A. Kuleshova, B. A. Gurovich, Ya. I. Shtrombakh, et al., “Microstructural behavior of VVER-440 reactor pressure vessel steels under irradiation to neutron fluences beyond the design operation period,” J. Nucl. Mater., 342, No. 1–3, 77–89 (2005).
V. A. Gurovich, E. A. Kuleshov, Ya. I. Shtrombakh, et al., “Fine structure behavior of VVER-1000 RPV materials under irradiation,” J. Nucl. Mater., 389, 490–496 (2009).
Author information
Authors and Affiliations
Additional information
Translated from Atomnaya Énergiya, Vol. 109, No. 4, pp. 205–213, October, 2010.
Rights and permissions
About this article
Cite this article
Shtrombakh, Y.I., Gurovich, B.A., Kuleshova, E.A. et al. Experimental assessment of the effectiveness of recovery annealing of VVER-1000 vessels. At Energy 109, 257–265 (2011). https://doi.org/10.1007/s10512-011-9354-z
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10512-011-9354-z