Abstract
The pitting behavior was investigated on super 13Cr stainless steels in 3.5% NaCl solution in the presence of HAc. The electrochemical measurements including potentiodynamic polarization, electrochemical impedance spectroscopy (EIS), and chronoamperometric experiments were carried out, as well as the SEM surface analysis. The parameters such as E corr and I corr were obtained by fitting technique. Moreover, the equivalent circuit model was applied in the analysis of Nyquist plots, and ZsimWin software was used to analyze the EIS data. The results indicate that the pitting corrosion is accelerated with increasing the amounts of HAc. In addition, pitting nucleation and growth mechanisms were described in this work.
Similar content being viewed by others
References
Burstein T, Liu C, Souto RM, Vines SP (2004) Corros. Eng Sci Tech 39:25. doi:10.1179/147842204225016859
Frankel GS (1998) J Electrochem Soc 145:2186. doi:10.1149/1.1838615
Shibata T, Takeyama T (1976) Nature 260:315. doi:10.1038/260315a0
Gunaltun YM, Larrey D (2000) NACE paper no. 71. NACE, Houston
Crolet JL, Bonis MR (1983) NACE paper no.160. NACE, Houston
Sun Y, George K, Nesic S (2003) NACE paper no. 327. NACE, Houston
George K, Nesic S, de Waard C (2004) NACE paper no. 379. NACE, Houston
Guo XP, Chen ZY, Liu D, Bando K, Tomoe Y (2005) NACE paper no. 306. NACE, Houston
Hedges B, McVeigh L (1999) NACE paper no. 21. NACE, Houston
Gunaltun YM, Belghazi A (2001) NACE paper no. 33. NACE, Houston
Long G, Grandjean F (1996) Mössbauer spectroscopy applied to magnetism and materials science. Plenum, New York
Touzet M et al (1993) Corros Sci 34:1134. doi:10.1016/0010-938X(93)90297-T
Chen Y, Jepson WP (1999) Electrochim Acta 44:4453. doi:10.1016/S0013-4686(99)00160-7
Cao CN, Zhang JQ (2002) An introduction to electrochemical impedance spectroscopy. Science, Beijing
Baek JS, Kim JG, Hur DH, Kim JS (2003) Corros Sci 45:983–994. doi:10.1016/S0010-938X(02)00183-X
Wranglen G (1974) Corros Sci 14:331. doi:10.1016/S0010-938X(74)80047-8
Lott SE, Alkire RC (1989) J Electrochem Soc 136:973. doi:10.1149/1.2096896
Rosenfeld IL, Marshakov IK (1964) Corrosion 20:115
Palmer DA, van Eldik R (1983) Chem Rev 83:651. doi:10.1021/cr00058a004
Acknowledgements
The authors want to thank the Key Laboratory Opening Fund (No. 06A40302) of Corrosion and Protection of Tabular Goods Research Center of China National Petroleum Corporation for supports to this work.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Yin, Z.F., Zhao, W.Z., Tian, W. et al. Pitting behavior on super 13Cr stainless steel in 3.5% NaCl solution in the presence of acetic acid. J Solid State Electrochem 13, 1291–1296 (2009). https://doi.org/10.1007/s10008-008-0675-3
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10008-008-0675-3