Clinical Oral Investigations

, Volume 23, Issue 3, pp 1295–1308 | Cite as

Physical property investigation of contemporary glass ionomer and resin-modified glass ionomer restorative materials

  • Matthew Moberg
  • John Brewster
  • John Nicholson
  • Howard RobertsEmail author
Original Article
  • 265 Downloads

Abstract

Objectives

The objective of this study was to investigate selected physical properties of nine contemporary and recently marketed glass ionomer cement (GIC) and four resin-modified glass ionomer cement (RMGI) dental restorative materials.

Materials and methods

Specimens (n = 12) were fabricated for fracture toughness and flexure strength using standardized, stainless steel molds. Testing was completed on a universal testing machine until failure. Knoop hardness was obtained using failed fracture toughness specimens on a microhardness tester, while both flexural modulus and flexural toughness was obtained by analysis of the flexure strength results data. Testing was completed at 1 h, 24 h, 1 week, and then at 1, 3, 6, and 12 months. Mean data was analyzed with Kruskal-Wallis and Mann-Whitney (p = 0.05).

Results

Physical properties results were material dependent. Physical properties of the GIC and RMGI products were inferior at 1 h compared to that at 24 h. Some improvement in selected physical properties were noted over time, but development processes were basically concluded by 24 h. A few materials demonstrated improved physical properties over the course of the evaluation.

Conclusions

Under the conditions of this study:
  1. 1.

    GIC and RMGI physical property performance over time was material dependent;

     
  2. 2.

    Polyalkenoate maturation processes are essentially complete by 24 h;

     
  3. 3.

    Although differences in GIC physical properties were noted, the small magnitude of the divergences may render such to be unlikely of clinical significance;

     
  4. 4.

    Modest increases in some GIC physical properties were noted especially flexural modulus and hardness, which lends support to reports of a maturing hydrogel matrix;

     
  5. 5.

    Overall, GIC product physical properties were more stable than RMGI;

     
  6. 6.

    A similar modulus reduction at 6 months for both RMGI and GIC produced may suggest a polyalkenoate matrix change; and

     
  7. 7.

    Globally, RMGI products demonstrated higher values of flexure strength, flexural toughness, and fracture toughness than GIC materials.

     

Clinical relevance

As compared to RMGI materials, conventional glass ionomer restorative materials demonstrate more stability in physical properties.

Keywords

Polyalkenoate Glass ionomer Resin modified glass ionomer Hydrogel matrix Physical property testing 

Notes

Acknowledgments

The opinions offered in the work are those of the authors only and do not reflect the official opinion of the United States Air Force, Department of Defense, or the United States Government.

Funding

This work was supported by 81 Medical Group Protocol FKE20150010N.FI.

Compliance with ethical standards

Conflict of interest

The authors declare that they have no conflict of interest.

Ethical approval

This article does not contain any studies with human participants or animals performed by any of the authors.

Informed consent

For this type of study, formal consent is not required.

Supplementary material

784_2018_2554_Fig6_ESM.png (78 kb)
Supplemental Figure 1

Header: GIC Mean Flexure Strength 12 Month Results (MPa). Footer: n = 12 (PNG 78 kb)

784_2018_2554_MOESM1_ESM.tif (4 mb)
High resolution image (TIF 4067 kb)
784_2018_2554_Fig7_ESM.png (170 kb)
Supplemental Figure 2

Header: RMGI Mean Flexure Strength (MPa). Footer: n = 12 (PNG 169 kb)

784_2018_2554_MOESM2_ESM.tif (36.8 mb)
High resolution image (TIF 37707 kb)
784_2018_2554_Fig8_ESM.png (219 kb)
Supplemental Figure 3

Header: GIC Mean Flexural Modulus (GPa). Footer: n = 12 (PNG 218 kb)

784_2018_2554_MOESM3_ESM.tif (26.2 mb)
High resolution image (TIF 26838 kb)
784_2018_2554_Fig9_ESM.png (180 kb)
Supplemental Figure 4

Header: RMGI Mean Flexural Modulus (GPa). Footer: n = 12 (PNG 180 kb)

784_2018_2554_MOESM4_ESM.tif (52.7 mb)
High resolution image (TIF 53928 kb)
784_2018_2554_MOESM5_ESM.jpg (566 kb)
Supplemental Figure 5 Header: GIC Mean Flexural Toughness (mJ/mm3). Footer: n = 12 (JPG 566 kb)
784_2018_2554_MOESM6_ESM.jpg (490 kb)
Supplemental Figure 6 Header: RMGI Mean Flexural Toughness (mJ/mm3). Footer: n = 12 (JPG 489 kb)
784_2018_2554_Fig10_ESM.png (72 kb)
Supplemental Figure 7

Header: GIC Mean Hardness Results (KHN). Footer: n = 12 (PNG 72 kb)

784_2018_2554_MOESM7_ESM.tif (4 mb)
High resolution image (TIF 4093 kb)
784_2018_2554_Fig11_ESM.png (148 kb)
Supplemental Figure 8

Header: RMGI Mean Hardness Results (KHN). Footer: n = 12 (PNG 148 kb)

784_2018_2554_MOESM8_ESM.tif (254 kb)
High resolution image (TIF 254 kb)
784_2018_2554_MOESM9_ESM.jpg (490 kb)
Supplemental Figure 9 Header: GIC Mean Fracture Toughness (MPa √m). Footer: n = 12 (JPG 490 kb)
784_2018_2554_MOESM10_ESM.jpg (452 kb)
Supplemental Figure 10 Header: RMGI Mean Fracture Toughness (MPa √m). Footer: n = 12 (JPG 451 kb)
784_2018_2554_MOESM11_ESM.docx (22 kb)
Supplemental Table 1 (DOCX 22 kb)
784_2018_2554_MOESM12_ESM.docx (22 kb)
Supplemental Table 2 (DOCX 22 kb)

References

  1. 1.
    Wilson AD, Kent BE (1971) The glass-ionomer cement, a new translucent dental filling material. J Appl Chem 21:313CrossRefGoogle Scholar
  2. 2.
    Wilson AD, Batchelor RF (1967) Dental silicate cements I. The chemistry of erosion. J Dent Res 46:1078–1085Google Scholar
  3. 3.
    Wilson AD (1989) Developments in glass-ionomer cements. Int J Prosthodont 2:438–446Google Scholar
  4. 4.
    Nicholson JW (1998) Chemistry of glass-ionomer cements: a review. Biomaterials 19:485–494CrossRefGoogle Scholar
  5. 5.
    Hatton PV, Brook IM (1992) Characterization of the ultrastructure of glass-ionomer (poly-alkenoate) cement. Br Dent J 173:275–277CrossRefGoogle Scholar
  6. 6.
    Cattani-Lovente MA, Godin C, Meyer JM (1994) Mechanical behavior of glass ionomer cements affected by the long-term storage in water. Dent Mater 10:37–44CrossRefGoogle Scholar
  7. 7.
    Matsuya S, Maeda T, Ohta M (1996) IR and NMR analyses of hardening and maturation of glass-ionomer cement. J Dent Res 75:1920–1927CrossRefGoogle Scholar
  8. 8.
    Crisp S, Lewis BG, Wilson AD (1976) Characterization of glass-ionomer cements. 1. Long term hardness and compressive strength. J Dent 4:162–166CrossRefGoogle Scholar
  9. 9.
    Sidhu SK, Nicholson JW (2016) A review of glass ionomer cements for clinical dentistry. J Funct Biomater 28.  https://doi.org/10.3390/jfb7030016
  10. 10.
    Mitra SB (1991) Adhesion to dentin and physical properties of a light-cured glass-ionomer liner/base. J Dent Res 70:72–74CrossRefGoogle Scholar
  11. 11.
    Baig MS, Fleming GJP (2015) Conventional glass-ionomer materials: a review of the developments in glass powder, polyacid liquid and the strategies of reinforcement. J Dent 42:897–912.  https://doi.org/10.1016/j.jdent.2015.04.004 CrossRefGoogle Scholar
  12. 12.
    Khoroushi M, Keshani F (2013) A review of glass-ionomers: from conventional glass-ionomer to bioactive glass-ionomer. Dent Res J (Isfahan) 10:411–420Google Scholar
  13. 13.
    Baig MS, Dowling AH, Fleming GJ (2013) Hertzian indentation testing of glass-ionomer restoratives: a reliable and clinically relevant testing approach. J Dent 41:968–973.  https://doi.org/10.1016/j.jdent.2013.04.004 CrossRefGoogle Scholar
  14. 14.
    Moshaverinia A, Roohpour N, Cheea WWL, Schricker SR (2012) A review of polyelectrolyte modifications in conventional glass-ionomer dental cements. J Mater Chem.  https://doi.org/10.1039/c2jm14880c, www.rsc.org/materials
  15. 15.
    Prosser HJ, Powis DR, Brant PJ, Wilson AD (1984) Characterization of glass-ionomer cements. The physical properties of current materials. J Dent 12:231–240CrossRefGoogle Scholar
  16. 16.
    McLean JW, Gasser O (1985) Glass cermet cements. Quintessence Int 16:333–343Google Scholar
  17. 17.
    Simmons JJ (1983) The miracle mixture: glass-ionomer and alloy powder. Tex Dent J 100:6–12Google Scholar
  18. 18.
    Williams JA, Billington RW, Pearson GJ (1992) The comparative strengths of commercial glass-ionomer cements with and without metal additions. Br Dent J 172:279–282CrossRefGoogle Scholar
  19. 19.
    Wren AW, Kidari A, Cummins NM, Towler MR (2010) A spectroscopic investigation into the setting and mechanical properties of titanium containing glass polyalkenoate cements. J Mater Sci Mater Med 21:2355–2364.  https://doi.org/10.1007/s10856-010-4089-2 CrossRefGoogle Scholar
  20. 20.
    Guggenberger R, May R, Stefan KP (1998) New trends in glass-ionomer chemistry. Biomaterials 19:479–483CrossRefGoogle Scholar
  21. 21.
    Tüzüner T, Kuşgӧz A, Er K, Taşdemіr T, Buruk K, Kemer B (2011) Antibacterial activity and physical properties of conventional glass-ionomer cements containing chlorhexidine diacetate/cetrimide mixtures. J Esthet Restor Dent 23:46–56.  https://doi.org/10.1111/j.1708-8240.2010.00385.x CrossRefGoogle Scholar
  22. 22.
    Xie D, Weng Y, Guo X, Zhao J, Gregory RL, Zheng C (2011) Preparation and evaluation of a novel glass-ionomer cement with antibacterial functions. Dent Mater 27:487–496.  https://doi.org/10.1016/j.dental.2011.02.006 CrossRefGoogle Scholar
  23. 23.
    Boyd D, Towler MR, Watts S, Hill RG, Wren AW, Clarkin OM (2008) The role of Sr2+ on the structure and reactivity of SrO-CaO-ZnO-SiO2 ionomer glasses. J Mater Sci Mater Med 19:953–957CrossRefGoogle Scholar
  24. 24.
    Kiri L, Boyd D (2015) Predicting composition-property relationships for glass ionomer cements: a multifactor central composite approach to material optimization. J Mech Behav Biomed Mater 46:285–291.  https://doi.org/10.1016/j.jmbbm.2015.02.007 CrossRefGoogle Scholar
  25. 25.
    Sidhu SK, Watson TF (1995) Resin-modified glass ionomer materials. A status report for the American Journal of Dentistry. Am J Dent 8:59–67Google Scholar
  26. 26.
    Friedl KH, Powers JM, Hiller KA (1995) Influence of different factors on bond strength of hybrid ionomers. Oper Dent 20:74–80Google Scholar
  27. 27.
    Kakaboura A, Eliades G, Palaghias G (1996) An FTIR study on the setting mechanism of resin-modified glass ionomer restoratives. Dent Mater 12:173–178CrossRefGoogle Scholar
  28. 28.
    Tay FR, Pashley EL, Huang C, Hashimoto M, Sano H, Smales RJ, Pashley DH (2001) The glass-ionomer phase in resin-based restorative materials. J Dent Res 80:1808–1812CrossRefGoogle Scholar
  29. 29.
    Mitra SB, Lee CY, Bui HT, Tantbirojn D, Rusin RP (2009) Long-term adhesion and mechanism of bonding of a paste-liquid resin-modified glass-ionomer. Dent Mater 25:459–466.  https://doi.org/10.1016/j.dental.2008.09.008 CrossRefGoogle Scholar
  30. 30.
    Fukuda R, Yoshida Y, Nakayama Y, Okazaki M, Inoue S, Sano H, Suzuki K, Shintani H, Meerbeek BV (2003) Bonding efficacy of polyalkenoic acids to hydroxyapatite, enamel, and dentin. Biomaterials 24:1861–1867CrossRefGoogle Scholar
  31. 31.
    Yiu CK, Tay FR, King NM, Pashley DH, Sidhu SK, Neo JC et al (2004) Interaction of glass ionomer cements with moist dentin. J Dent Res 83:283–289CrossRefGoogle Scholar
  32. 32.
    Yip HK, Tay FR, Ngo HC, Smales RJ, Pashley DH (2001) Bonding of contemporary glass ionomer cements to dentin. Dent Mater 17:456–470CrossRefGoogle Scholar
  33. 33.
    Tay FR, Smales RJ, Ngo H, Wei SH, Pashley DH (2000) Effect of different conditioning protocols on adhesion of a GIC to dentin. J Adhes Dent 3:153–167Google Scholar
  34. 34.
    Hammesfahr PD Developments in resionomer systems. In: Hunt P (ed) Glass ionomers: The next generation. Proceedings of the 2nd International Symposium on Glass Ionomers, June 1994, Philadelphia, PA. International Symposia in Dentistry, PC, Philadelphia, pp 47–55Google Scholar
  35. 35.
    Berzins DW, Abey S, Costache MC, Wilkie CA, Roberts HW (2010) Resin-modified glass-ionomer setting reaction competition. J Dent Res 89:82–86.  https://doi.org/10.1177/0022034509355919 CrossRefGoogle Scholar
  36. 36.
    Roberts HW, Berzins DC (2015) Early reaction kinetics of contemporary glass-ionomer restorative materials. J Adhes Dent 17:67–75.  https://doi.org/10.3290/j.jad.a33526. Google Scholar
  37. 37.
    Yelamanchili Y, Darvell BW (2008) Network competition in a resin-modified glass-ionomer cement. Dent Mater 24:1065–1069.  https://doi.org/10.1016/j.dental.2007.12.005 CrossRefGoogle Scholar
  38. 38.
    Young AM (2002) FTIR investigation of polymerization [sic] and polyacid neutralization kinetics in resin-modified glass-ionomer dental cements. Biomaterials 23:3289–3295CrossRefGoogle Scholar
  39. 39.
    Young A, Sherpa G, Pearson B, Schottlander, Waters DN (2000) Use of Raman spectroscopy in the characterisation of the acid–base reaction in glass-ionomer cements. Biomaterials 21:1971–1979CrossRefGoogle Scholar
  40. 40.
    Stamboulis A, Matsuya S, Hill RG, Law RV, Udoh K, Nakagawa M, Matsuya Y (2006) MAS-NMR spectroscopy studies in the setting reaction of glass ionomer cements. J Dent 34:574–581CrossRefGoogle Scholar
  41. 41.
    Wasson EA, Nicholson JW (1993) Change in pH during setting of polyelectrolyte dental cements. J Dent 21:122–126CrossRefGoogle Scholar
  42. 42.
    Griffin SG, Hill RG (1999) Influence of glass composition on the properties of glass polyalkenoate cements. Part I: influence of aluminium to silicon ratio. Biomaterials 20:1579–1586CrossRefGoogle Scholar
  43. 43.
    Algera TJ, Kleverlaan CJ, Prahl-Andersen B, Feilzer AJ (2006) The influence of environmental conditions on the material properties of setting glass-ionomer cements. Dent Mater 22:852–856CrossRefGoogle Scholar
  44. 44.
    Tay M, Braden M (1981) Dielectric properties of glass ionomer cements. J Dent Res 60:1311–1314CrossRefGoogle Scholar
  45. 45.
    Watts C (1998) Analysis of reactions in glass-polyalkenoate/resin systems by dielectric impedance spectroscopy. Biomaterials 19:551–577CrossRefGoogle Scholar
  46. 46.
    Babu TA, Ramesh KV, Sastry DL (2012) Studies on electrical and thermal properties of dental glass ionomer cement. J Biomed Sci Eng 5:638–638.  https://doi.org/10.4236/jbise.2012.511078 CrossRefGoogle Scholar
  47. 47.
    ŠSantić A, Čalogović AM, Pavić L, Gladić J, Vučić Z, Lovrić D, Prskalo K, Janković B, Tarle Z, Moguš-Milanković A (2015) New insights into the setting processes of glass ionomer cements from analysis of dielectric properties. J Am Ceram Soc 98:3869–3876.  https://doi.org/10.1111/jace.13830 CrossRefGoogle Scholar
  48. 48.
    Watts DC (1986) The development of surface hardness in visible light cured posterior composites. J Dent 14:169–174CrossRefGoogle Scholar
  49. 49.
    Roberts HW, Berzins D (2014) Thermal analysis of contemporary glass-ionomer restorative materials. J Therm Anal Calorim 115:2099–2106.  https://doi.org/10.1007/s10973-013-3428-1 CrossRefGoogle Scholar
  50. 50.
    Wan ACA, Yap AUJ, Hastings GW (1999) Acid-base complex reactions in resin-modified and conventional glass ionomer cements. J Biomed Mater Res 48:700–704.  https://doi.org/10.1007/s00784-013-1074-4 CrossRefGoogle Scholar
  51. 51.
    Shiozawa M, Takahashi H, Iwasaki N (2014) Fluoride release and mechanical properties after 1-year water storage of recent restorative glass ionomer cements. Clin Oral Invest 18:1053–1060.  https://doi.org/10.1007/s00784-013-1074-4
  52. 52.
    Wren AW, Coughlan A, Laffir FR, Towler MR (2013) Comparison of a SiO2-CaO-ZnO-SrO glass polyalkenoate cement to commercial dental materials: glass structure and physical properties. J Mater Sci Mater Med 24:271–280.  https://doi.org/10.1007/s10856-012-4813-1 CrossRefGoogle Scholar
  53. 53.
    Azillah MA, Anstice HM, Pearson GJ (1998) Long-term flexural strength of three direct aesthetic restorative materials. J Dent 26:177–182CrossRefGoogle Scholar
  54. 54.
    Wasson EA, Nicholson JW (1993) New aspects of the setting chemistry of glass-ionomer cements. J Dent Res 72:481–483CrossRefGoogle Scholar
  55. 55.
    Dickey B, Price R, Boyd D (2016) Evidence of a complex species controlling the setting reaction of glass ionomer cements. Dent Mater 32:596–605.  https://doi.org/10.1016/j.dental.2016.01.012 CrossRefGoogle Scholar
  56. 56.
    Zainuddin N, Karpukhina N, Hill RG, Law RV (2009) A long-term study on the setting reaction of glass ionomer cements by (27) Al MAS-NMR spectroscopy. Dent Mater 25:290–295.  https://doi.org/10.1016/j.dental.2008.07.008 CrossRefGoogle Scholar
  57. 57.
    de Amorim RG, Leal SC, Mulder J, Creugers NHJ, Frencken JE (2014) Amalgam and ART restorations in children: a controlled clinical trial. Clin Oral Investig 18:117–124.  https://doi.org/10.1007/s00784-013-0955-x CrossRefGoogle Scholar
  58. 58.
    Cefaly DFG, Tapety CMC, Mondelli RFL, Lauris JRP, Phantumvanit P, Navarro MFL (2006) Three-year evaluation of the ART approach in class III and V restorations in permanent anterior teeth. Caries Res 40:389–392CrossRefGoogle Scholar
  59. 59.
    da Mata C, Allen PF, McKenna G, Cronin C, O’Mahony D, Woods N (2015) Two-year survival of ART restorations placed in elderly patients: a randomized controlled clinical trial. J Dent 43:405–411.  https://doi.org/10.1016/j.jdent.2015.01.003 CrossRefGoogle Scholar
  60. 60.
    Faccin ES, Ferreira SH, Kramer PF, Ardenghi TM, Feldens CA (2009) Clinical performance of ART restorations in primary teeth: a survival analysis. J Clin Pediatr Dent 33:295–298CrossRefGoogle Scholar
  61. 61.
    Frencken JE (2010) The ART approach using glass-ionomers in relation to global oral health care. Dent Mater 26:1–6.  https://doi.org/10.1016/j.dental.2009.08.013. CrossRefGoogle Scholar
  62. 62.
    Frencken JE, van 't Hof MA, van Amerongen WE, Holmgren CJ (2004) Effectiveness of single-surface ART restorations in the permanent dentition: a meta-analysis. J Dent Res 83:120–123CrossRefGoogle Scholar
  63. 63.
    Rutar J, Mcallan L, Tyas MJ (2002) Three-year clinical performance of glass ionomer cement in primary molars. Int J Paediatr Dent 12:146–147CrossRefGoogle Scholar
  64. 64.
    Burrow MF, Tyas MJ (2007) Clinical evaluation of three adhesive systems for the restoration of non-carious cervical lesions. Oper Dent 32:11–15CrossRefGoogle Scholar
  65. 65.
    Fagundes TC, Barata THE, Bresciani E, Santiago SL, Franco EB, Lauris JRP, Navarro MF (2014) Seven-year clinical performance of resin composite versus resin-modified glass ionomer restorations in noncarious cervical lesions. Oper Dent 39:578–587.  https://doi.org/10.2341/13-054-C CrossRefGoogle Scholar
  66. 66.
    McComb D, Erickson RL, Maxymiw WG, Wood RE (2002) A clinical comparison of glass ionomer, resin-modified glass ionomer and resin composite restorations in the treatment of cervical caries in xerostomic head and neck radiation patients. Oper Dent 27:430–437Google Scholar
  67. 67.
    Qvist V, Manscherb E, Teglers PT (2004) Resin-modified and conventional glass ionomer restorations in primary teeth: 8-year results. J Dent 32:285–294CrossRefGoogle Scholar
  68. 68.
    van Dijken JWV, Pallesen U (2008) Long-term dentin retention of etch-and-rinse and self-etch adhesives and a resin-modified glass ionomer cement in non-carious cervical lesions. Dent Mater 24:915–922CrossRefGoogle Scholar
  69. 69.
    Friedl K, Hiller KA, Friedl KH (2011) Clinical performance of a new glass ionomer based restoration system: a retrospective cohort study. Dent Mater 27:1031–1037.  https://doi.org/10.1016/j.dental.2011.07.004 CrossRefGoogle Scholar
  70. 70.
    Mickenautsch S, Yengopal V, Leal SC, Oliveria LB, Bezerra AC, Bonecker M (2009) Absence of carious lesions of glass-ionomer and amalgam restorations: a meta-analysis. Eur J Paediatr Dent 10:41–46Google Scholar
  71. 71.
    Türkün LS, Kanik Ö (2016) A prospective six-year clinical study evaluating reinforced glass ionomer cements with resin coating on posterior teeth: Quo Vadis? Oper Dent 41:587–598.  https://doi.org/10.2341/15-331-C CrossRefGoogle Scholar
  72. 72.
    Billington R, Williams J, Pearson GJ (1990) Variation in powder/liquid ratio of a restorative glass-ionomer cement used in general dental practice. Br Dent J 168:164–167CrossRefGoogle Scholar
  73. 73.
    Dowling AH, Fleming GJP (2009) Are encapsulated anterior glass-ionomer restoratives better than their hand-mixed equivalents? J Dent 37:133–140.  https://doi.org/10.1016/j.jdent.2008.10.006 CrossRefGoogle Scholar
  74. 74.
    Gonzalez-Bonet A, Kaufman G, Yang Y, Wong C, Jackson A, Huyang G, Bowen R, Sun J (2015) Preparation of dental resins resistant to enzymatic and hydrolytic degradation in oral environments. Biomacromolecules 16:3381–3388.  https://doi.org/10.1021/acs.biomac.5b01069 CrossRefGoogle Scholar
  75. 75.
    ISO 9917-2:2010. Water based cements–Part 2: resin-modified cements. International Organization for Standardization, GeneveGoogle Scholar
  76. 76.
    Prosser HJ, Powis DR, Brant P, Wilson AD (1984) Characterization of glass-ionomer cements. 7. The physical properties of current materials. J Dent 12:231–240CrossRefGoogle Scholar
  77. 77.
    Ferracane JW (2013) Resin-based composite performance: are there some things we can’t predict? Dent Mater 29:51–58.  https://doi.org/10.1016/j.dental.2012.06.013 CrossRefGoogle Scholar
  78. 78.
    Hu J, Du X, Huang C, Fu D, Ouyang X, Wang Y (2013) Antibacterial and physical properties of EGCG-containing glass ionomer cements. J Dent 41:927–934.  https://doi.org/10.1016/j.jdent.2013.07.014 CrossRefGoogle Scholar
  79. 79.
    Zoergiebel J, Ilie N (2013) Evaluation of a conventional ionomer cement with new zinc formulation: effect of coating, aging and storage agents. Clin Oral Investig 17:619–626.  https://doi.org/10.1007/s00784-012-0733-1 CrossRefGoogle Scholar
  80. 80.
    Bonifácio CC, Kleverlaan CJ, Raggio DP, Werner A, de Carvalho RCR, van Amerongen (2009) Physical-mechanical properties of glass ionomer cements indicated for atraumatic restorative treatment. Aust Dent J 54:233–237CrossRefGoogle Scholar
  81. 81.
    Yamazaki T, Schricker SR, Brantley WA, Culbertson BM, Johnston WJ (2005) Viscoelastic behavior and fracture toughness of six glass-ionomer cements. J Dent Res 96:266–272Google Scholar
  82. 82.
    Xie D, Brantley WA, Culbertson BM, Wang G (2000) Mechanical properties and microstructures of glass-ionomer cements. Dent Mater 16:129–138CrossRefGoogle Scholar
  83. 83.
    Lucksanasombool P, Higgs WAJ, Higgs RJED, Swain MV (2002) Time dependence of the mechanical properties of GICs in simulated physiologic conditions. J Mater Sci Mater Med 13:745–750CrossRefGoogle Scholar
  84. 84.
    Xie D, Yang Y, Zhao J, Park JG, Zhang JT (2007) A novel comonomer-free light-cured glass-ionomer cement for reduced cytotoxicity and enhanced mechanical strength. Dent Mater 23:994–1003CrossRefGoogle Scholar
  85. 85.
    Weng Y, Howard L, Xie D (2014) A novel star-shaped poly (carboxylic acid) for resin-modified glass-ionomer restoratives. J Biomater Sci Polym Ed 25:1076–1090.  https://doi.org/10.1080/09205063.2014.920169 CrossRefGoogle Scholar
  86. 86.
    Culbertson BM (2006) New polymeric materials for use in glass-ionomer cements. J Dent 34:556–565CrossRefGoogle Scholar
  87. 87.
    Price RBT, Labrie D, Rueggeberg FA, Sullivan B, Kostylev I, Fahey J (2014) Correlation between the beam profile from a curing light and the microhardness of four resins. Dent Mater 30:1345–1357.  https://doi.org/10.1016/j.dental.2014.10.001 CrossRefGoogle Scholar
  88. 88.
    Al-Angari SS, Hara AT, Chu T, Platt J, Eckert G, Cook NB (2014) Physicomechanical properties of a zinc-reinforced glass ionomer restorative material. J Oral Sci 56:11–16.  https://doi.org/10.2334/josnusd.56.11 CrossRefGoogle Scholar
  89. 89.
    De Moor RJG, Verbeeck RMH (1998) Changes in surface hardness of conventional restorative glass ionomer cements. Biomaterials 19:2269–2275CrossRefGoogle Scholar
  90. 90.
    Tyas MJ (1990) Correlation between fracture properties and clinical performance of composite resins in class IV cavities. Aust Dent J 35:46–49CrossRefGoogle Scholar
  91. 91.
    Ferracane JL, Condon JR (1999) In vitro evaluation of the marginal degradation of dental composites under simulated occlusal loading. Dent Mater 15:262–267CrossRefGoogle Scholar
  92. 92.
    Baig MS, Lloyd CH, Fleming GJP (2015) Fracture toughness testing: a discriminatory mechanical testing performance indicator for glass-ionomer restoratives? Dent Mater 31:877–886.  https://doi.org/10.1016/j.dental.2015.04.014 CrossRefGoogle Scholar
  93. 93.
    Ilie N, Hickel R, Valceanu AS, Huth KC (2012) Fracture toughness of dental restorative materials. Clin Oral Investig 16:489–498.  https://doi.org/10.1007/s00784-011-0525-z CrossRefGoogle Scholar
  94. 94.
    Kanchanavasita W, Anstice HM, Pearson GJ (1997) Water sorption characteristics of resin-modified glass-ionomer cements. Biomaterials 18:343–349CrossRefGoogle Scholar
  95. 95.
    Small ICB, Watson TF, Chadwick AV, Sidhu SK (1998) Water sorption in resin-modified glass-ionomer cements: an in vitro comparison with other materials. Biomaterials 19:545–550CrossRefGoogle Scholar
  96. 96.
    Versluis A, Tantbirojn D, Lee MS, Tu LS, DeLong R (2011) Can hygroscopic expansion compensate polymerization shrinkage? Part I. Deformation of restored teeth. Dent Mater 27:126–133.  https://doi.org/10.1016/j.dental.2010.09.007 CrossRefGoogle Scholar
  97. 97.
    Gurgan S, Kutuk ZB, Ergin E, Oztas SS, Cakir FY (2015) Four-year randomized clinical trial to evaluate the clinical performance of a glass ionomer restorative system. Oper Dent 40:134–143.  https://doi.org/10.2341/13-239-C CrossRefGoogle Scholar

Copyright information

© Springer-Verlag GmbH Germany, part of Springer Nature 2018

Authors and Affiliations

  1. 1.42 Medical GroupMaxwell Air Force BaseMontgomeryUSA
  2. 2.Air Force Postgraduate Dental School Keesler AFB MSKeesler AFBBiloxiUSA
  3. 3.Bluefield Centre for BiomaterialsLondonUK
  4. 4.Dental Physical Sciences, Barts & The London School of Medicine and DentistryQueen Mary University of LondonLondonUK
  5. 5.University of KentuckyCollege of DentistryLexingtonUSA

Personalised recommendations