A study of screen printing of stretchable circuits on polyurethane substrates

  • Z. W. ZhongEmail author
  • R. W. L. Tang
  • S. H. Chen
  • X. C. Shan
Technical Paper
  • 407 Downloads

Abstract

The interest in flexible stretchable printed electronics has increased because of the wide applications, especially for wearables devices. The conventional manufacturing processes were time consuming and expensive, which led to developing of stretchable interconnects using screen printing. In this research, meander patterns of varying meander angles were designed and screen-printed on thermoplastic polyurethane substrates. Silver inks and carbon inks were used to print the circuits, which were subjected to tensile tests while their changes in resistance were measured. The electrical characteristics were utilised to determine the elastic limits of the circuits and the conditions for cyclic tests of up to 10,000 cycles. It was found that the maximum strain at break of the silver ink was 47%. Carbon ink had a higher initial resistance value and the maximum strain at break was 125%. The best stretchability was obtained at the 0° meander angle, a curing time of 30 min and curing temperature of 130 °C with oven cooling.

Notes

References

  1. Arulvanan P, Zhong ZW (2006) Assembly and reliability of PBGA packages on FR-4 PCBs with SnAgCu solder. Microelectron Eng 83(11–12):2462–2468CrossRefGoogle Scholar
  2. Aziz NA (2013) Development of a scale-up version of stretchable sensor for robotic application. Report of Nanyang Technological Univeristy, SingaporeGoogle Scholar
  3. BASF (2011) Thermoplastic polyurethane elastomer (TPU). Lemforde, ElastogranstraßeGoogle Scholar
  4. Bossuyta F, Guentherb J, Löherc T, Seckelc M, Sterkena T, Vriesd JD (2011) Cyclic endurance reliability of stretchable electronic substrates. Microelectron Reliab 51(3):628–635CrossRefGoogle Scholar
  5. Cai L, Zhang S, Zhang Y, Li J, Miao J, Wang Q, Yu Z, Wang C (2018) Direct printing for additive patterning of silver nanowires for stretchable sensor and display applications. Adv Mater Technol 3(2):1700232CrossRefGoogle Scholar
  6. Cui Z, Han Y, Huang Q, Dong J, Zhu Y (2018) Electrohydrodynamic printing of silver nanowires for flexible and stretchable electronics. Nanoscale 10(15):6806–6811CrossRefGoogle Scholar
  7. DuPont (2014) DuPont microcircuit materials introduces stretchable inks for wearable electronics. Retrieved 30 Aug 2016, from http://www.dupont.com/products-and-services/electronic-electrical-materials/media/press-releases/20141204-stretchable-inks-for-wearable-electronics.html
  8. Feng X, Wei L, Yong Z (2011) Controlled 3D buckling of silicon nanowires for stretchable electronics. ACS Nano 5(1):672–678CrossRefGoogle Scholar
  9. Goldberg HD, Brown RB, Liu DP, Meyerhoff ME (1994) Screen Printing a technology for the batch fabrication of integrated chemical-sensor arrays. Sensor Acuators 21(2):171–183CrossRefGoogle Scholar
  10. Gonzalez M, Axisa F, Bulcke MV, Brosteaux D, Vandevelde B, Vanfleteren J (2008) Design of metal interconnects for stretchable electronic circuits. Microelectron Reliab 48(6):825–832CrossRefGoogle Scholar
  11. Hicks EM, Ultee AJ, Drougas J (1965) Spandex elastic fibers. Science 147(3656):373–379CrossRefGoogle Scholar
  12. Ho X, Cheng CK, Tham CL, Lee RST, Lu H, Suriya A, Shan X (2015) Conformable and transparent electronics. Singapore Report of Singapore Institute of Manufacturing TechnologyGoogle Scholar
  13. Hobby A (1997) Screen printing for the industrial user. Gwent Group Retrieved 5 Sep 2016, from http://www.gwent.org/gem_screen_printing.html
  14. Hong H, Chen C-M (2014) Design, fabrication and failure analysis of stretchable electrical routings: review. Sensors 14(7):11855–11877CrossRefGoogle Scholar
  15. Hornyak T (2008) “RFID powder”. Sci Am 298:68–71Google Scholar
  16. Huck WTS, Bowden N, Onck P, Pardoen T, Hutchinson JW, Whitesides GM (2000) Ordering of spontaneously formed buckles on planar surfaces. Langmuir 16(7):3497–3501CrossRefGoogle Scholar
  17. Khang DY, Rogers JA, Lee HH (2008) Mechanical buckling: mechanics, metrology, and stretchable electronics. Adv Funct Mater 19(10):1526–1536CrossRefGoogle Scholar
  18. Kim D-H, Xiao J, Song J, Huang Y, Roger JA (2010) Stretchable, curvilinear electronics based on inorganic materials. Adv Mater 22(19):2108–2124CrossRefGoogle Scholar
  19. Kim D-H, Lu N, Ma R, Kim Y-S, Kim R-H, Wang S, Wu J, Won SM, Tao H, Islam A, Yu KJ, Kim T-I, Chowdhury R, Ying M, Xu L, Li M, Chung H-J, Keum H, McCormick M, Liu P, Zhang Y-W, Omentto FG, Huang Y, Coleman T, Rogers JA (2011) Epidermal Electronics. Science 333(6044):838–843CrossRefGoogle Scholar
  20. Lacour SP, Jones J, Wagner S, Li T, Suo Z (2005) Stretchable interconnects for elastic electronic surfaces. Proc IEEE 93(8):1459–1467CrossRefGoogle Scholar
  21. Lee J-W, Mun KK, Yoo YT (2009) A comparative study on roll-to-roll gravure printing on PET and BOPP webs aqueous ink. Progress Org Coat 64:98–108CrossRefGoogle Scholar
  22. Li T, Huang Z, Suo Z, Lacour SP, Sigurd W (2004) Stretchbility of thin metal films on elastomer substrates. Appl Phys Lett 85(16):3435–3437CrossRefGoogle Scholar
  23. Lötters JC, Olthuis W, Veltink PH, Bergveld P (1997) The mechanical properties of the rubber elastic polymer polydimethylsiloxane for sensor applications. J Micromech Microeng 7(3):145–147CrossRefGoogle Scholar
  24. Merilampi S, Björninen T, Haukka V, Ruuskanen P, Ukkonen L, Sydänheimo L (2010) Analysis of electrically conductive silver ink on stretchable substrates under tensile loading. Microelectron Reliab 50(12):2001–2011CrossRefGoogle Scholar
  25. Mohammed Ali M, Maddipatla D, Narakathu BB, Chlaihawi AA, Emamian S, Janabi F, Bazuin BJ, Atashbar MZ (2018) Printed strain sensor based on silver nanowire/silver flake composite on flexible and stretchable TPU substrate. Sens Actuat A Phys 274:109–115CrossRefGoogle Scholar
  26. Nagase America. Electric conductive ink for printed electronics. Electric conductive inks for printed electronics. Retrieved 30 August 2016. http://nagaseamerica.com/product/electric-conductive-ink-printed-electronics/
  27. Owczarek JA, Howland FL (1990) A study of the off-contact screen printing process-Part 1: model of the printing process and some results derived from experiments. IEEE Trans Compon Hybrids Manuf Technol 13(2):358–367CrossRefGoogle Scholar
  28. Pardo DA, Jabbour GE, Peyghambarian N (2000) Application of screen printing in the fabrication of organic light-emitting devices. Adv Mater 12(17):1249–1252CrossRefGoogle Scholar
  29. Romeo A, Liu Q, Suo Z, Lacour SP (2013) Elastomeric substrates with embedded stiff platforms for stretchable electronics. Appl Phys Lett 102(13):Article Number: 131904Google Scholar
  30. Sirringhaus H, Kawase T, Friend RH, Shimoda T, Inbasekaran M, Wu W, Woo EP (2000) High-resolution inkjet printing of all-polymer transistor circuits. Science 290(5499):2123–2126CrossRefGoogle Scholar
  31. Tai Y-L, Yang Z-G (2012) Preparation of stable aqueous conductive ink with silver nanoflakes and its application on paper-based flexible electronics. Surf Interf Anal 44(5):529–534CrossRefGoogle Scholar
  32. Tang RWL (2017) Mechanical and electrical characteristics of screen printed stretchable circuits. Report of Project B190. Nanyang Technological University, SingaporeGoogle Scholar
  33. University of Cambridge (2008) Polymer stress-strain curve. DoITPoMS Retrieved 10 March 2017, from https://www.doitpoms.ac.uk/tlplib/polymers/stress-strain.php
  34. Wu HP, Liu JF, Wu XJ, Ge MY, Wang YW, Zhang GQ, Jiang JZ (2006) High conductivity of isotropic conductive adhesives filled with silver nanowires. Int J Adhes Adhes 26(8):617–621CrossRefGoogle Scholar
  35. Xu F, Zhu Y (2012) Highly conductive and stretchable silver nanowire conductor. Adv Mater 24(37):5117–5122CrossRefGoogle Scholar
  36. Xu L, Gutbrod S, Bonifas AP, Su Y, Sulkin MS, Lu N, Chung H-J, Jang K-I, Liu Z, Ying M, Lu C, Webb RC, Kim J-S, Laughner JI, Cheng H, Liu Y, Ameen A, Jeong J-W, Kim G-T, Huang Y, Efimov IR, Rogers JA (2014) 3D multifunctional integumentary membranes for spatiotemporal cardiac measurements and stimulation across the entire epicaedium. Nat Commun 5:Article Number: 3329Google Scholar
  37. Zhong ZW, Goh KS (2000) Flip chip on Fr-4, ceramics and flex. J Electron Manuf 10(2):89–96CrossRefGoogle Scholar
  38. Zhong ZW, Arulvanan P, Shi XQ (2005) Lead-free PCB assembly and effects of process conditions on the profile and reliability of solder joints. Solder Surf Mount Technol 17(4):33–37CrossRefGoogle Scholar
  39. Zhong ZW, Ng HH, Chen SH, Shan XC (2018) Hot roller embossing of multi-dimensional microstructures using elastomeric molds. Microsyst Technol Micro Nanosyst Inf Storage Process Syst 24(3):1443–1452Google Scholar

Copyright information

© Springer-Verlag GmbH Germany, part of Springer Nature 2018

Authors and Affiliations

  1. 1.School of Mechanical and Aerospace EngineeringNanyang Technological UniversitySingaporeSingapore
  2. 2.Singapore Institute of Manufacturing Technology (SIMTech)SingaporeSingapore

Personalised recommendations