Stuctural, optical and radiation shielding properties of zinc boro-tellurite alumina glasses
- 134 Downloads
In this work, boro-telluride glasses with additional zinc, aluminum, and alkali–alkaline modifiers have been synthesized using the melt-quenching–annealing method. Six glasses were fabricated with composition of [(60 − x)B2O3–(10 + x)TeO2–10ZnO–10Al2O3–5Li2O–5MgO] all in mol% and x varied from 0, 10, 20, 30, 40 and 50. The aim of this work is to understand the effect of changing the main glass former from B2O3 → TeO2, to obtain new optical materials. To confirm the amorphous nature of these six glasses, X-ray diffraction was characterized for all six glasses from 10° to 80°. Optical absorption with wavelength range 200–800 nm in room temperature was measured, and the optical absorption coefficient α(λ) calculated to obtain the cutoff wavelength. In addition, gamma photons shielding features of the prepared K1–K6 glasses were evaluated by means of some essential parameters such as mass attenuation coefficients (µ/ρ) and effective atomic number (Zeff) at five energies between 0.356 and 1.33 MeV. No significant difference between the theoretical and simulation µ/ρ values was found. The effective atomic number results indiacte that as the TeO2 content increases, the photons’ attenuation increases. The number of interactions of gamma photons with K6 sample (which contains the maximum amount of TeO2) is relatively high (in comparison to the rest of the samples), which results in more attenuation and thus better shielding features for K6.
The authors would like to gratefully acknowledge the use of the services and facilities of Universiti Putra Malaysia (UPM), Malaysia, where this work was supported by UPM under GP-IPM/2016/9484400 Grant. Also, the authors would like to thank Prof. Mohamed Bourham, North Carolina State University, Department of Nuclear Engineering, Raleigh, USA, for his useful discussion.
- 8.H.O. Tekin, T.T. Erguze, M.I. Sayyed, V.P. Singh, T. Manici, E.E. Altunsoy, O. Agar, An investigation on shielding properties of different granite samples using mcnpx code, Digest Journal of Nanomaterials and Biostructures, 13, 381–389 (2018)Google Scholar
- 15.K. Siva Rama, K. Reddy, K. Swapna, S. Mahamuda, M. Venkateswarlu, M.V.V.K. Srinivas Prasad, A.S. Rao, G.V. Prakash, Structural, optical absorption and photoluminescence spectral studies of Sm3+ ions in Alkaline-Earth Boro Tellurite glasses, Opt. Mater. (Amst). 79, 21–32 (2018). https://doi.org/10.1016/j.optmat.2018.03.005 CrossRefADSGoogle Scholar
- 28.G. Lakshminarayana, K.M. Kaky, S.O. Baki, S. Ye, A. Lira, I.V. Kityk, M.A. Mahdi, Concentration dependent structural, thermal, and optical features of Pr3+-doped multicomponent tellurite glasses. J. Alloys Compd. 686, 769–784 (2016). https://doi.org/10.1016/j.jallcom.2016.06.069 CrossRefGoogle Scholar
- 36.K.M. Kaky, G. Lakshminarayana, S.O. Baki, Y.H. Taufiq-Yap, I.V. Kityk, M.A. Mahdi, Structural, thermal, and optical analysis of zinc boro-aluminosilicate glasses containing different alkali and alkaline modifier ions. J. Non. Cryst. Solids. 456, 55–63 (2017). https://doi.org/10.1016/j.jnoncrysol.2016.10.044 CrossRefADSGoogle Scholar
- 37.J.N. Ayuni, M.K. Halimah, Z.A. Talib, H.A.A. Sidek, W.M. Daud, A.W. Zaidan, A.M. Khamirul, Optical properties of ternary TeO2–B2O3–ZnO glass system, IOP Conf. Ser. Mater. Sci. Eng. 17 (2011). https://doi.org/10.1088/1757-899X/17/1/012027
- 42.D. Souri, K. Shomalian, Band gap determination by absorption spectrum fitting method (ASF) and structural properties of different compositions of (60-x) V2O5-40TeO2-xSb2O3 glasses. J. Non. Cryst. Solids. 355, 1597–1601 (2009). https://doi.org/10.1016/j.jnoncrysol.2009.06.003 CrossRefADSGoogle Scholar
- 44.M.J. Berger, J.H. Hubbell, S.M. Seltzer, J. Chang, J.S. Coursey, R. Sukumar, K. Zucker, D.S. Olsen, http://www.nist.gov/pml/data/xcom/index.cfm (2010)
- 49.M.I. Sayyed, G. Lakshminarayana, M.A. Mahdi, Evaluation of radiation shielding parameters for optical materials. Chalcogenide Lett. 14, 43–47 (2017)Google Scholar