Bio-based furan coatings: adhesion, mechanical and thermal properties

Abstract

In this study, preparation of polyfurfuryl alcohol (PFA) as a renewable binder resin with an origin in biomass conversion is reported for developing a heat-resistant coating. PFA resin was synthesized in the presence of maleic anhydride as a catalyst. Various techniques were used to characterize the synthesized PFA resin. In the second step, different coating samples were prepared using PFA resin. Flexibility, adhesion strength and thermal/curing behavior of the coating samples were investigated as a function of their compositions such as the resin, plasticizers and titanium dioxide (TiO2) contents. The coatings were cured optimally at 150 °C according to isothermal and non-isothermal DSC measurements. Leveling property of the coatings was significantly improved in the presence of TiO2 due to a corresponding increased viscosity of the compound. The adhesion strength of the coating was low due to the aromaticity of PFA chains, high cross-linking degree of the binder resin and the difference existing between thermal expansion coefficient of the coating and steel substrate. In the presence of dioctyl phthalate and long-oil alkyd resin as plasticizers, flexibility and adhesion strength of the coatings were significantly improved up to 15 mm and 2.7 MPa, respectively. High thermal stability of the coatings was supported by TGA findings but it was deteriorated in the presence of alkyd resin. Alkyd resin, a plasticizer, increased the extent of cross-linking due to the chain flexibility enhancement according to DSC and DMTA findings. Finally, a heat-resistant coating formulation containing 9.3 wt% long-oil alkyd resin and 9.3 wt% TiO2 was selected as a good candidate for heat-resistant coating development due to the highest thermal and mechanical properties shown.

This is a preview of subscription content, log in to check access.

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9

References

  1. 1.

    Zhao T, Zhang D, Ding C, Zhou J, Zhu J, Jiang L (2014) A multi-functional polymer coating that is heat-resistant, hydrophobic and transparent. Particuology 17:4–7. https://doi.org/10.1016/j.partic.2014.04.006

  2. 2.

    Radhakrishna LMS (2013) Heat-resistant anti-corrosive paint from epoxy-silicone vehicles. Anti-Corros Methods Mater 44:400–406

  3. 3.

    Youssef EA (1996) Heat-resistant anticorrosive paints based on Egyptian manganese ore. Anti-Corros Methods Mater 43:17–21

  4. 4.

    Wu Q, Ma X, Zheng F, Lu X, Lu Q (2019) Synthesis of highly transparent and heat-resistant polyimides containing bulky pendant moieties. Polym Int 68:1186–1193

  5. 5.

    Liu Y, Imae I, Kawakami Y (2004) Novel thermally resistant polysilphenylenesiloxanes with a high content of vinyl substituents. Polym Int 53:1259–1265

  6. 6.

    Mikhailova AM, Tamboura M (2012) Heat-resistant and anti-corrosion urethane-silicone-based coatings. Silicon 4:197–208. https://doi.org/10.1007/s12633-012-9123-1

  7. 7.

    Chen M, Xiong P, Zhou Q, Ni L, Wang G (2014) Synthesis, curing behavior and thermal properties of silicon-containing hybrid polymers with Si–C=C units. Polym Int 63:1531–1536

  8. 8.

    Schmitt CR (1974) Polyfurfuryl alcohol resin. Polym Plast Technol Eng 3:121–158

  9. 9.

    Guigo N, Mija A, Vincent L, Sbirrazzuoli N (2010) Eco-friendly composite resins based on renewable biomass resources: polyfurfuryl alcohol/lignin thermosets. Eur Polym J 46:1016–1023

  10. 10.

    Assary RS, Kim T, Low JJ, Greeley J, Curtiss LA (2012) Glucose and fructose to platform chemicals: understanding the thermodynamic landscapes of acid-catalysed reactions using high-level ab initio methods. Phys Chem Chem Phys 14:16603–16611

  11. 11.

    Marefat Seyedlar R, Imani M, Mirabedini SM (2016) Curing of poly(furfuryl alcohol) resin catalyzed by a homologous series of dicarboxylic acid catalysts: kinetics and pot life. J Appl Polym Sci 133:43–53. https://doi.org/10.1002/app.44009

  12. 12.

    Marefat Seyedlar R, Imani M, Mirabedini SM (2017) Rheokinetics in curing process of polyfurfuryl alcohol: effect of homologous acid catalysts. Iran Polym J 26:281–293

  13. 13.

    Guigo N, Mija A, Zavaglia R, Vincent L, Sbirrazzuoli N (2009) New insights on the thermal degradation pathways of neat poly(furfuryl alcohol) and poly(furfuryl alcohol)/SiO2 hybrid materials. Polym Degrad Stab 94:908–913. https://doi.org/10.1016/j.polymdegradstab.2009.03.008

  14. 14.

    Marefat Seyedlar R, Imani M, Mirabedini SM (2018) Curing of polyfurfuryl alcohol resin catalyzed by a homologous series of dicarboxylic acid catalysts : 2. Swelling behavior and thermal properties. J Appl Polym Sci 135:45770

  15. 15.

    Wewerka EM, Loughran ED, Walters KL (1971) A study of the low molecular weight components of furfuryl alcohol polymers. J Appl Polym Sci 15:1437–1451. https://doi.org/10.1002/app.1971.070150612

  16. 16.

    Renhe H, Hongmei G, Yaoji LQT (2011) Curing mechanism of furan resin modified with different agents and their thermal strength. Res Dev 5:161–165

  17. 17.

    Dunlop AP, Peters F (1953) The Furans. Reinhold, New York, p 548

  18. 18.

    Barsberg S, Thygesen LG (2009) Poly(furfuryl alcohol) formation in neat furfuryl alcohol and in cymene studied by ATR-IR spectroscopy and density functional theory (B3LYP) prediction of vibrational bands. Vib Spectrosc 49:52–63. https://doi.org/10.1016/j.vibspec.2008.04.013

  19. 19.

    Choura M, Belgacem NM, Gandini A (1996) Acid-catalyzed polycondensation of furfuryl alcohol: mechanisms of chromophore formation and cross-linking. Macromolecules 29:3839–3850. https://doi.org/10.1021/ma951522f

  20. 20.

    Fawcett AH, Dadamba W (1982) Characterization of furfuryl alcohol oligomers by 1H and 13C NMR spectroscopy. Macromol Chem Phys 183:2799–2809

  21. 21.

    Mittal KL (1983) Adhesion aspects of polymeric coatings. Plenum Press, New York

  22. 22.

    Zhang Y (1995) Adhesion of epoxy coatings to an alloy-coated steel sheet, Doctor of Philosophy thesis. Department of Materials Engineering, University of Wollongong. http://ro.uow.edu.au/theses/1481

  23. 23.

    Mittal KL (1995) Adhesion measurement of films and coatings, vol 640. VSP, Utrecht

  24. 24.

    Fitzer E, Schäfer W (1970) The effect of crosslinking on the formation of glasslike carbons from thermosetting resins. Carbon N Y 8:353–364. https://doi.org/10.1016/0008-6223(70)90075-8

  25. 25.

    Zhang H (2004) Fire-safe polymers and polymer composites. Office of Aviation Research, Federal Aviation Administration

  26. 26.

    Burket CL, Rajagopalan R, Marencic AP, Dronvajjala K, Foley HC (2006) Genesis of porosity in polyfurfuryl alcohol derived nanoporous carbon. Carbon N Y 44:2957–2963. https://doi.org/10.1016/j.carbon.2006.05.029

  27. 27.

    Jacobs PM, Jones FR (1992) The influence of heterogeneous crosslink density on the thermomechanical and hygrothermal properties of an unsaturated polyester resin: 1. Thermomechanical response. Polymer (Guildf) 33:1418–1422

  28. 28.

    Milkovic J, George EM, Young RA (1979) Interpretation of curing mechanisms of furfuryl alcohol resins. Cellul Chem Technol 13:651–672

  29. 29.

    Chen XS, Zheng GD, Liu ZH, Xu J-P (1991) Study on the condensation and crosslinking reactions of furfuryl alcohol and tris(2-hydroxyethyl) isocyanurate by thermal methods. Chin J Chem 9:8–13

  30. 30.

    Domínguez JC, Madsen B (2014) Chemorheological study of a polyfurfuryl alcohol resin system—pre-gel curing stage. Ind Crop Prod 52:321–328. https://doi.org/10.1016/j.indcrop.2013.11.006

  31. 31.

    Hill LW (1992) Structure/property relationships of thermoset coatings. J Coat Technol 64:28–42

  32. 32.

    Narayan R, Raju KVSN (2002) Properties of acetoacetylated hydroxylated polyesters based polyurethane coatings. Prog Org Coat 45:59–67. https://doi.org/10.1016/S0300-9440(02)00116-9

  33. 33.

    Mirchandani G, Waghoo G, Parmar R, Haseebuddin S, Ghosh SK, Group FP (2009) Oligomeric silsesquioxane reinforced polyurethane with enhanced coating performance. Prog Org Coat 65:444–449. https://doi.org/10.1016/j.porgcoat.2009.03.009

  34. 34.

    Wang X, Hu Y, Song L, Xing W, Lu H, Lv P et al (2010) Effect of antimony doped tin oxide on behaviors of waterborne polyurethane acrylate nanocomposite coatings. Surf Coat Technol 205:1864–1869. https://doi.org/10.1016/j.surfcoat.2010.08.053

  35. 35.

    Bosq N, Guigo N, Vincent L, Sbirrazzuoli N (2015) Thermomechanical behavior of a novel biobased poly (furfurylalcohol)/silica nanocomposite elaborated by smart functionalization of silica nanoparticles. Polym Degrad Stab 118:137–146

  36. 36.

    Krumova M, Lopez D, Benavente R, Mijangos C, Perena JM (2000) Effect of crosslinking on the mechanical and thermal properties of poly (vinyl alcohol). Polymer (Guildf) 41:9265–9272

  37. 37.

    Rodrıguez MT, Gracenea JJ, Kudama AH, Suay JJ (2004) The influence of pigment volume concentration (PVC) on the properties of an epoxy coating: part I. Thermal and mechanical properties. Prog Org Coat 50:62–67. https://doi.org/10.1016/j.porgcoat.2003.10.013

  38. 38.

    Jacquelot E, Galy J, Roche A, Chevet E, Fouissac E, Verchère D (2009) Morphology and thermo-mechanical properties of new hybrid coatings based on polyester/melamine resin and pyrogenic silica. Prog Org Coat 66:86–92. https://doi.org/10.1016/j.porgcoat.2009.06.005

  39. 39.

    Bertarione S, Bonino F, Cesano F, Damin A, Scarano D, Zecchina A (2008) Furfuryl alcohol polymerization in H–Y confined spaces: reaction mechanism and structure of carbocationic intermediates. J Phys Chem B 112:2580–2589

Download references

Acknowledgements

This research was funded by the Iran Polymer and Petrochemical Institute (contract Grant No. 32751105). The authors are sincerely thankful for this financial support.

Author information

Correspondence to Mohammad Imani.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Marefat Seyedlar, R., Imani, M. & Mirabedini, S.M. Bio-based furan coatings: adhesion, mechanical and thermal properties. Polym. Bull. (2020). https://doi.org/10.1007/s00289-020-03124-4

Download citation

Keywords

  • Polyfurfuryl alcohol
  • Binder resin
  • Heat-resistant coating
  • Thermal properties
  • Mechanical properties