Enhancing the adhesion strength of polyurethane coatings by dispersing layered silicates via sonication and high-shear mixing method


Low adhesion strength of polyurethane coating to a steel substrate is often attributed to poor steel preparation. However, the ratio of diisocyanate/polyol and dispersion of fillers within a polyurethane coating matrix influence the adhesion strength, optical and corrosion resistance properties. Poor dispersion of nano-fillers in a polymer coating matrix can lead to low adhesion strength, because close packing of nanoparticles often hides the hydroxyl groups required to form polar–polar bonds with the steel surface. This study combines sonication and high-shear mixing methods with shorter mixing times to prepare polyurethane nanocomposite coatings with various clay concentrations while keeping the ratio of diisocyanate/polyol constant. Fourier-transform infrared spectroscopy (FTIR), transmission electron microscopy (TEM) and X-ray diffraction, thermogravimetric analysis and pull-off are used to characterize polyurethane nanocomposite coatings. FTIR results confirm that sonication and high-shear mixing successfully prepare polyurethane-based coatings. TEM shows uniformly dispersed clay particles in polyurethane matrices. The adhesion strength improved on addition of 1–5 wt% C30B organoclay, with the highest improvement (34.4%) at 3 wt% loading. The corrosion resistance of polyurethane coatings was improved by the incorporation of organoclays into their matrices. Onset degradation temperature is also delayed by 4.1–8.5% as the clay concentration increased from 1 to 5 wt%.

This is a preview of subscription content, log in to check access.

Access options

Buy single article

Instant unlimited access to the full article PDF.

US$ 39.95

Price includes VAT for USA

Subscribe to journal

Immediate online access to all issues from 2019. Subscription will auto renew annually.

US$ 199

This is the net price. Taxes to be calculated in checkout.

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11
Fig. 12
Fig. 13


  1. 1.

    Guan SW (2003) 100% solids polyurethane and polyurea coatings technology coatings. Coat World 49–58

  2. 2.

    Bayer O, Muller E, Petersen S, Piepenbrink HF, Windemuth E (1950) Polyurethanes. VI. New highly elastic synthesis. Vulcollans Angew Chem 62:57

  3. 3.

    Varma AJ, Deshpande MD, Nadkarni VM (1985) Polyurethane/montmorillonite nanocomposites. Angew Makromol Chem 132:2003–2009

  4. 4.

    Kaushik A, Dheeraj A, Vipin S (2011) Synthesis and characterization of organically modified clay/castor oil based chain extended polyurethane nanocomposites. J Compos 42:1534–1541

  5. 5.

    Choudalakis G, Gotsis A (2009) Permeability of polymer/clay nanocomposites: a review. Eur Polym J 45:967–984

  6. 6.

    Ahmed NM, Abdel-Fatah HTM (2012) In recent researches in corrosion evaluation and protection. In: Razavi RS (ed) In Tech, Chap 4, p 67

  7. 7.

    Rehab A, Salahuddin N (2005) Nanocomposite materials based on polyurethane intercalated into montmorillonite clay. Mater Sci Eng A 399:368–376

  8. 8.

    Patel HM, Kachhia PH, Patel KS, Shah MD (2019) Synthesis of diphosphorus-based polyurethane esters and their application in flame-retardant nanoclay coatings. Poylm Bull.

  9. 9.

    Chang JH, An YU (2002) Nanocomposites of polyurethane with various organoclays: Thermomechanical properties, morphology, and gas permeability. J Polym Sci Part B Polym Phys 40:670–677

  10. 10.

    Solarski S, Benali S, Rochery M, Devaux E, Alexandre M, Monteverde F, Dubois P (2005) Synthesis of a polyurethane/clay nanocomposite used as coating: interactions between the counterions of clay and the isocyanate and incidence on the nanocomposite structure. J Appl Polym Sci 95:238–244

  11. 11.

    Nematollahi M, Heidarian M, Peikari M, Kassiriha S, Arianpouya N, Esmaeilpour M (2010) Comparison between the effect of nanoglass flake and montmorillonite organoclay on corrosion performance of epoxy coating. Corros Sci 52:1809–1817

  12. 12.

    Heidarian M, Shishesaz M, Kassiriha S, Nematollahi M (2010) Characterization of structure and corrosion resistivity of polyurethane/organoclay nanocomposite coatings prepared through an ultrasonication assisted process. Prog Org Coat 68:180–188

  13. 13.

    Varughese K, Review. DuPont Coatings. Web 2010 C, Alaa MA, Yusoh K, Hasany SF (2015) Synthesis and characterization of polyurethane–organoclay nanocomposites based on renewable castor oil polyols. Polym Bull 72:1–17

  14. 14.

    Ashhari S, Sarabi AA, Kasiriha SM, Zaarei D (2011) Aliphatic polyurethane–montmorillonite nanocomposite coatings: preparation, characterization, and anticorrosive properties. J Appl Polym Sci 119:523–529

  15. 15.

    Song M, Hourston D, Yao K, Tay J, Ansarifar M (2003) High performance nanocomposites of polyurethane elastomer and organically modified layered silicate. J Appl Polym Sci 90:3239–3243

  16. 16.

    Ahmad MB, Gharayebi Y, Salit MS, Hussein MZ, Shameli K (2011) Comparison of in situ polymerization and solution-dispersion techniques in the preparation of polyimide/montmorillonite (MMT) nanocomposites. Int J Molecul Sci 12:6040–6050

  17. 17.

    Chattopadhyay DK, Webster DC (2009) Thermal stability and flame retardancy of polyurethanes. Prog Polym Sci 34:1068–1133

  18. 18.

    Verma G, Kaushik A, Ghosh AK (2013) Comparative assessment of nano-morphology and properties of spray coated clear polyurethane coatings reinforced with different organoclays. Prog Org Coat 76:1046–1056

  19. 19.

    Joshi M, Banerjee K, Prasanth R, Thakare V (2006) Polymer/clay nanocomposite based coatings for enhanced gas barrier property. Indian J Fibre Text Res 31:202–214

Download references


Thanks to the Tshwane University of Technology for granting this study, Rand Water Company, South Africa, for funding this project and National Centre for Nanostructured Materials (NCNSM) for allowing the use of characterization facilities. Furthermore, I like to acknowledge Dr Vincent Ojijo, Mr Cliff Thompson and Dr Vincent Khumalo for their scientific guidance; Mr Mpho Motloung assisting and Dr Orebotse Botlhoko for assisting with the SAXS and contact angle measurements, respectively.

Author information

Correspondence to Thomas Malwela.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Skosana, S.J., Khoathane, C. & Malwela, T. Enhancing the adhesion strength of polyurethane coatings by dispersing layered silicates via sonication and high-shear mixing method. Polym. Bull. (2020).

Download citation


  • Polyurethane coatings
  • High-shear mixing
  • Nanocomposites
  • Adhesion strength