Mechanical properties of green canola meal composites and reinforcement with cellulose fibers
- 24 Downloads
Samples of canola meal (CM), a by-product of canola oil extraction, with different particle sizes and canola protein (CP) content were obtained by ball milling followed by air classification. In an effort to produce highly deformable “green” biodegradable materials, these CM samples were used to prepare CM bioplastics and their mechanical properties were characterized and compared. It was found that greater CP content led to an increase in elongation at break and a decrease in tensile strength; however, particle size of CM had no apparent impact on the tensile properties. Considering its high mechanical properties and miscibility with the CM matrix, cellulose fiber (CF) was added to the composite formulation to fabricate samples with enhanced tensile strength. The effects of fiber loading on mechanical and thermal properties were characterized using tensile testing and dynamic mechanical analysis. Marked improvements in tensile strength and modulus were found with increasing fiber content above 5 wt%, while mechanical properties were constant between fiber contents of 1–5 wt% because of the inefficient packing of the CF, indicating that the fiber content of 5 wt% is a percolation threshold to increase the mechanical property of the CM composite. The DMA results illustrate that the addition of fiber produced an increase in storage modulus and decreased damping factors for the composites with > 5 wt% CF, reflecting strong interfacial adhesion between CM and CF which resulted in a decrease in chain mobility.
KeywordsCanola meal Biodegradable composite Mechanical property Thermal property Extrusion processing
We thank the Canola Council of Canada and Agriculture and Agri-Food Canada through Growing Forward 2 Canola/Flax Science Cluster Programs for financial funding.
- 11.Reddy MM, Misra M, Mohanty AK (2014) Biodegradable blends from corn gluten meal and poly (butylene adipate-co-terephthalate) (PBAT): studies on the influence of plasticization and destructurization on rheology, tensile properties and interfacial interactions. J Polym Environ 22:167–175CrossRefGoogle Scholar
- 15.Manamperi WAR, Pryor SW, Chang SK (2006) Separation and evaluation of canola meal and protein for industrial bioproducts. In: ASABE/CSBE north central intersectional meeting. American Society of Agricultural and Biological Engineers, p 1Google Scholar
- 21.Manamperi WA, Sehrawat J, Fuqua MA, Ulven CA, Pryor SW (2009) Influence of plasticizers on properties of polymers made from canola protein polyester blends. American Society of Agricultural and Biological Engineers, Reno, p 1Google Scholar
- 37.King R, Dietz H (1987) Air classification of rapeseed meal. Cereal Chem 64:411–413Google Scholar
- 44.Ornaghi HL, Bolner AS, Fiorio R, Zattera AJ, Amico SC (2010) Mechanical and dynamic mechanical analysis of hybrid composites molded by resin transfer molding. J Appl Polym Sci 118:887–896Google Scholar
- 53.Chan RT-P (2012) A study on the extrusion of soy protein film incorporated with soy-derived cellulose fibers. Dissertation, University of GuelphGoogle Scholar