Kinetic color analysis for assessing the effects of borate and glycerol on thermal modification of wood

  • Li YanEmail author
  • Jeffrey J. Morrell
Original
  • 47 Downloads

Abstract

The effects of borate and glycerol impregnation of Douglas-fir heartwood prior to open-air oven thermal modification at 160–200 °C for 2–4 h on wood color were measured. These materials were used to analyze the effects of modifying agents on thermal decomposition of wood by color nondestructive assessments. Kinetic analysis using time–temperature superposition and the horizontal shift factor were employed to quantify color changes. Lightness values were significantly affected by heating time and temperature, while red/green and yellow/blue values were significantly affected by pretreatments and thermal modification temperatures. Total color differences tended to increase with heating temperature and time. The calculated values of the apparent activation energy on non-impregnated, borate-impregnated and glycerol-impregnated wood ranged from 94.9 to 126.4 kJ/mol, 46.5 to 74.3 kJ/mol and 54.3 to 79.7 kJ/mol, respectively. The results suggest that borate and glycerol decreased the apparent activation energy of thermal degradation reactions and could function as a catalyst to accelerate thermal modification. Time–temperature superposition color kinetic analysis could be used to assess the effects of modifying agents on thermal decomposition.

Notes

Acknowledgements

The senior author is grateful for the support of National Natural Science Foundation of China (NSFC) No. 31400500.

References

  1. Badini C, Saracco G, Russo N, Specchia V (2000) A screening study on the activation energy of vanadate-based catalysts for diesel soot combustion. Catal Lett 69:207–215CrossRefGoogle Scholar
  2. Bekhta P, Niemz P (2003) Effect of high temperature on the changes in color, dimensional stability and mechanical properties of spruce wood. Holzforschung 57:539–546CrossRefGoogle Scholar
  3. Brischke C, Welzbacher CR, Brandt K, Rapp AO (2007) Quality control of thermally modified timber: interrelationship between heat treatment intensities and CIE Lab* color data on homogenized wood samples. Holzforschung 61:19–22CrossRefGoogle Scholar
  4. Calonego FW, Severo ETD, Furtado EL (2010) Decay resistance of thermally-modified Eucalyptus grandis wood at 140 °C, 160 °C, 180 °C, 200 °C and 220 °C. Bioresour Technol 101(23):9391–9394CrossRefGoogle Scholar
  5. Chen Y, Tshabalala MA, Gao J, Stark NM, Fan Y (2014) Color and surface chemistry changes of extracted wood flour after heating at 120 °C. Wood Sci Technol 48:137–150CrossRefGoogle Scholar
  6. Ding HZ, Wang ZD (2007) Time–temperature superposition method for predicting the permanence of paper by extrapolating accelerated ageing data to ambient conditions. Cellulose 14:171–181CrossRefGoogle Scholar
  7. Esteves BM, Pereira HM (2009) Wood modification by heat treatment: a review. BioResources 4(1):370–404Google Scholar
  8. Esteves BM, Doningos IJ, Pereira HM (2008a) Pine wood modification by heat treatment in air. BioResources 3(1):142–154Google Scholar
  9. Esteves B, Velez MA, Domingos I, Pereira H (2008b) Heat-induced colour changes of pine (Pinus pinaster) and eucalypt (Eucalyptus globulus) wood. Wood Sci Technol 42(5):369–384CrossRefGoogle Scholar
  10. Fengel D, Wegener G (1989) Wood: chemistry, ultrastructure, reactions. Walter de Gruyter, Berlin, p 26Google Scholar
  11. Goli G, Marcon B, Fioravanti M (2014) Poplar wood heat treatment: effect of air ventilation rate and initial moisture content on reaction kinetics, physical and mechanical properties. Wood Sci Technol 48(6):1303–1316CrossRefGoogle Scholar
  12. Johansson D, Morén T (2006) The potential of colour measurement for strength prediction of thermally treated wood. Holz Roh Werkst 64:104–110CrossRefGoogle Scholar
  13. Lekounougou S, Kocaefe D (2014) Effect of thermal modification temperature on the mechanical properties, dimensional stability, and biological durability of black spruce (Picea mariana). Wood Mat Sci Eng 9(2):59–66CrossRefGoogle Scholar
  14. Luo S, Cao J, Wang X (2013) Investigation of the interfacial compatibility of PEG and thermally modified wood flour/polypropylene composites using the stress relaxation approach. BioResources 8(2):2064–2073Google Scholar
  15. Marcon B, Goli G, Matsuo M, Gril J, Kawai S (2018) Kinetic analysis of poplar wood properties by thermal modification in conventional oven. iForest 11:131–139CrossRefGoogle Scholar
  16. Matsumura Y, Okumura M, Usami Y, Kagawa K, Yamashita H, Anpo M, Haruta M (1997) Low-temperature decomposition of methanol to carbon monoxide and hydrogen with low activation energy over Pd/ZrO2 catalyst. Catal Lett 44:189–191CrossRefGoogle Scholar
  17. Matsunaga M, Obataya E, Minato K, Nakatsubo F (2000) Working mechanism of adsorbed water on the vibrational properties of wood impregnated with extractives of pernambuco (Guilandina echinata Spreng.). J Wood Sci 46:122–129CrossRefGoogle Scholar
  18. Matsuo M, Yokoyama M, Umemura K, Gril J, Yano K, Kawai S (2010) Color changes in wood during heating: kinetic analysis by applying a time–temperature superposition method. Appl Phys A 99:47–52CrossRefGoogle Scholar
  19. Matsuo M, Yokoyama M, Umemura K, Sugiyama J, Kawai S, Gril J, Kubodera S, Mitsutani T, Ozali H, Sakamoto M, Imamura M (2011) Aging of wood: analysis of color changes in cellulose during heat treatment. J Wood Sci 58:113–119CrossRefGoogle Scholar
  20. Matsuo M, Umemura K, Kawai S (2012) Kinetic analysis of color changes in cellulose during heat treatment. J Wood Sci 58:113–119CrossRefGoogle Scholar
  21. Matsuo M, Umemura K, Kawai S (2014) Kinetic analysis of color changes in keyaki (zelkova serrata) and sugi (Cryptomeria japonica) wood during heat treatment. J Wood Sci 60:12–20CrossRefGoogle Scholar
  22. Matsuo MU, Mitsui K, Kobayshi I, Kohara M, Yoshida M, Yamamoto H (2016) Effect of hygrothermal treatment on wood properties: color changes and kinetic analysis using four softwood and seven hardwood species. Wood Sci Technol 50:1145–1160CrossRefGoogle Scholar
  23. Mitsui K, Takada H, Sugiyama M, Hasegawa R (2001) Changes in the properties of light-irradiated wood with heat treatment. Part 1. Effect of treatment conditions on the change in color. Holzforschung 55:601–605CrossRefGoogle Scholar
  24. Obataya E, Minato K (2009) Potassium acetate-catalyzed acetylation of wood at low temperatures II: vapor phase acetylation at room temperature. J Wood Sci 55:23–26CrossRefGoogle Scholar
  25. Olarescu MC, Ispas CM, Cosereanu C (2014) Effect of thermal treatment on some properties of lime wood. Eur J Wood Prod 72:559–562CrossRefGoogle Scholar
  26. Poncsάk S, Kocaefe D, Bouazara M, Pichette A (2006) Effect of high temperature on the mechanical properties of birch (Betula papyrifera). Wood Sci Technol 40:647–663CrossRefGoogle Scholar
  27. Sandberg D, Kutnar A, Mantanis G (2018) Wood modification technologies—a review. Forest 10:895–908Google Scholar
  28. Tjeerdsma B, Boonstra M, Pizzi A, Tekely P, Militz H (1998) Characterisation of thermally modified wood: molecular reasons for wood performance improvement. Holz Roh Werkst 56:149–153CrossRefGoogle Scholar
  29. Toshimi H (1995) Kinetics of pyrolysis of wood and cellulose. Mokuzai Gakkaishi 41(10):879–886Google Scholar
  30. Tuong VM, Li J (2010) Effect of heat treatment on the change in color and dimensional stability of acacia hybrid wood. BioResources 5(2):1257–1267Google Scholar
  31. Yan L, Chen Z (2016) Dynamic mechanical analysis of viscoelastic properties of heat treated glycerol-impregnation poplar wood. International research group on wood protection document no. IRG/WP/16-40732Google Scholar
  32. Yan L, Morrell JJ (2014) Effect of thermal modification on physical and mechanical properties of Douglas-fir heartwood. BioResources 9(4):7152–7161CrossRefGoogle Scholar
  33. Yan L, Morrell JJ (2015) Mold and decay resistance of thermally modified Douglas-fir heartwood. For Prod J 65(5/6):272–277Google Scholar
  34. Yan L, Cao J, Jin X (2010) Deformation fixation, mechanical properties and chemical analysis of compressed Populus cathayana wood pretreated by glycerin. For Stud China 12(4):213–217CrossRefGoogle Scholar
  35. Yan L, Cao J, Gao W, Zhou X, Zhao G (2011) Interaction between glycerin and wood at various temperatures from stress relaxation approach. Wood Sci Technol 45(6):215–222CrossRefGoogle Scholar

Copyright information

© Springer-Verlag GmbH Germany, part of Springer Nature 2018

Authors and Affiliations

  1. 1.College of ForestryNorthwest A&F UniversityYanglingChina
  2. 2.Department of Wood Science and EngineeringOregon State UniversityCorvallisUSA

Personalised recommendations