Production of seamless tube from aluminum machining chips via double-step friction stir consolidation

  • Reza Abdi Behnagh
  • Fardin Fathi
  • Mohammad Yeganeh
  • Maryam Paydar
  • Mohsen Agha Mohammad
  • Yiliang LiaoEmail author
ORIGINAL ARTICLE
  • 63 Downloads

Abstract

At this present work, the feasibility of producing seamless tubes through recycling of aluminum machining chips via the double-step friction stir consolidation (FSC) process was investigated. This process was done in two distinct steps. At the first step, the chips are loaded into the container and slightly compacted, and then a rotating tool with a designated diameter is plunged into the chips at a chosen rotational speed and feed rate. Due to the frictional heating, the softened materials are compressed and merged to form a consolidated cylindrical bulk material eventually. In the second step, a rotating tool that is smaller in diameter than the first tool is again plunged into the recycled round bars at a selected rotational speed and feed rate, forcing the material radially outwards and afterwards forming tubes. The results show that the process is a feasible solution for producing structurally sound, void-free tubes directly from machining chips at two simple steps. A numerical model was implemented to predict the evolution of the main field variables including temperature, density, and strain in the process.

Keywords

Recycling Friction stir consolidation Aluminum Tube Finite element modeling 

Notes

References

  1. 1.
    Yousefpour Naghibi H, Omidvar H, Farahmand Nikoo M (2018) Investigating the effects of traveling speeds and post-weld heat treatment on mechanical properties of nano-Al2O3-fortified AA6061-T6 friction stir welds. Proc Inst Mech Eng. L 232(10):816–828.  https://doi.org/10.1177/1464420716650913 CrossRefGoogle Scholar
  2. 2.
    Puga H, Barbosa J, Soares D, Silva F, Ribeiro S (2009) Recycling of aluminium swarf by direct incorporation in aluminium melts. J Mater Process Technol 209:5195–5203.  https://doi.org/10.1016/j.jmatprotec.2009.03.007 CrossRefGoogle Scholar
  3. 3.
    Gronostajski J, Marciniak H, Matuszak A (2000) New methods of aluminium and aluminium-alloy chips recycling. J Mater Process Technol 106(1–3):34–39.  https://doi.org/10.1016/S0924-0136(00)00634-8 CrossRefGoogle Scholar
  4. 4.
    WU S, JI Z, RONG S, HU M (2010) Microstructure and mechanical properties of AZ31B magnesium alloy prepared by solid-state recycling process from chips. Trans Nonferrous Metals Soc China 20(5):783–788.  https://doi.org/10.1016/S1003-6326(09)60214-4 CrossRefGoogle Scholar
  5. 5.
    Ying L, Yuan L, Da-Tong Z (2002) Microstructure and properties of AZ80 magnesium alloy prepared by hot extrusion from recycled machined chips. Trans Nonferrous Met Soc China 12(5):882-885Google Scholar
  6. 6.
    Stern M, Gardens K. Method for treating aluminium or aluminium alloy scrap. 1945. https://www.google.com/patents/US2391752
  7. 7.
    Sharma S, Nakagawa T, Takenaka N (1977) Recent development in the recycling of machining swarf by sintering and powder forging. Ann CIRP 25(1):121–125Google Scholar
  8. 8.
    Galanty M, Kazanowski P, Kansuwan P, Misiolek WZ (2002) Consolidation of metal powders during the extrusion process. J Mater Process Technol 125-126:491–496.  https://doi.org/10.1016/S0924-0136(02)00327-8 CrossRefGoogle Scholar
  9. 9.
    Chiba R, Nakamura T, Kuroda M (2011) Solid-state recycling of aluminium alloy swarf through cold profile extrusion and cold rolling. J Mater Process Technol 211(11):1878–1887.  https://doi.org/10.1016/j.jmatprotec.2011.06.010 CrossRefGoogle Scholar
  10. 10.
    Misiolek WZ, Haase M, Ben Khalifa N, Tekkaya AE, Kleiner M (2012) High quality extrudates from aluminum chips by new billet compaction and deformation routes. CIRP Ann - Manuf Technol 61(1):239–242.  https://doi.org/10.1016/j.cirp.2012.03.113 CrossRefGoogle Scholar
  11. 11.
    Widerøe F, Welo T (2013) Using contrast material techniques to determine metal flow in screw extrusion of aluminium. J Mater Process Technol 213(7):1007–1018.  https://doi.org/10.1016/j.jmatprotec.2012.11.013 CrossRefGoogle Scholar
  12. 12.
    Cooper DR, Allwood JM (2014) The influence of deformation conditions in solid-state aluminium welding processes on the resulting weld strength. J Mater Process Technol 214(11):2576–2592.  https://doi.org/10.1016/j.jmatprotec.2014.04.018 CrossRefGoogle Scholar
  13. 13.
    Duflou JR, Tekkaya AE, Haase M, Welo T, Vanmeensel K, Kellens K, Dewulf W, Paraskevas D (2015) Environmental assessment of solid state recycling routes for aluminium alloys: can solid state processes significantly reduce the environmental impact of aluminium recycling? CIRP Ann - Manuf Technol 64(1):37–40.  https://doi.org/10.1016/j.cirp.2015.04.051 CrossRefGoogle Scholar
  14. 14.
    Tang W, Reynolds AP (2010) Production of wire via friction extrusion of aluminum alloy machining chips. J Mater Process Technol 210(15):2231–2237.  https://doi.org/10.1016/j.jmatprotec.2010.08.010 CrossRefGoogle Scholar
  15. 15.
    Behnagh RA, Mahdavinejad R, Yavari A, Abdollahi M, Narvan M (2014) Production of wire from AA7277 aluminum chips via friction-stir extrusion (FSE). Metall Mater Trans B Process Metall Mater Process Sci 45(4):1484–1489.  https://doi.org/10.1007/s11663-014-0067-2 CrossRefGoogle Scholar
  16. 16.
    Behnagh RA, Shen N, Ansari MA, Narvan M, Besharati Givi MK, Ding H (2015) Experimental analysis and microstructure modeling of friction stir extrusion of magnesium chips. J Manuf Sci Eng 138(4):041008.  https://doi.org/10.1115/1.4031281 CrossRefGoogle Scholar
  17. 17.
    Ansari MA, Behnagh RA, Narvan M, Naeini ES, Givi MKB, Ding H (2015) Optimization of friction stir extrusion (FSE) parameters through taguchi technique. Trans Indian Inst Metals 69(7):1351–1357.  https://doi.org/10.1007/s12666-015-0686-6 CrossRefGoogle Scholar
  18. 18.
    Li X, Baffari D, Reynolds AP (2018) Friction stir consolidation of aluminum machining chips. Int J Adv Manuf Technol 94(5–8):2031–2042.  https://doi.org/10.1007/s00170-017-1016-4 CrossRefGoogle Scholar
  19. 19.
    Whalen S, Jana S, Catalini D, Overman N, Sharp J (2016) Friction consolidation processing of n-type bismuth-telluride thermoelectric material. J Electron Mater 45(7):3390–3399.  https://doi.org/10.1007/s11664-016-4454-0 CrossRefGoogle Scholar
  20. 20.
    Catalini D, Kaoumi D, Reynolds AP, Grant GJ (2013) Friction consolidation of MA956 powder. J Nucl Mater 442(1–3 SUPPL.1).  https://doi.org/10.1016/j.jnucmat.2012.11.054 CrossRefGoogle Scholar
  21. 21.
    Catalini D, Kaoumi D, Reynolds AP, Grant GJ (2015) Dispersoid distribution and microstructure in Fe-Cr-Al ferritic oxide dispersion-strengthened alloy prepared by friction consolidation. Metall Mater Trans A 46(10):4730–4739.  https://doi.org/10.1007/s11661-015-3059-1 CrossRefGoogle Scholar
  22. 22.
    Narvan M, Abdi Behnagh R, Shen N, Besharati Givi MK, Ding H (2016) Shear compaction processing of SiC nanoparticles reinforced magnesium composites directly from magnesium chips. J Manuf Process 22:39–48.  https://doi.org/10.1016/j.jmapro.2016.01.010 CrossRefGoogle Scholar
  23. 23.
    Shima S, Oyane M (1976) Plasticity theory for porous metals. Int J Mech Sci 18(6):285–291.  https://doi.org/10.1016/0020-7403(76)90030-8 CrossRefGoogle Scholar
  24. 24.
    Baffari D, Buffa G, Fratini L (2017) A numerical model for wire integrity prediction in friction stir extrusion of magnesium alloys. J Mater Process Technol 247:1–10.  https://doi.org/10.1016/j.jmatprotec.2017.04.007 CrossRefGoogle Scholar

Copyright information

© Springer-Verlag London Ltd., part of Springer Nature 2019

Authors and Affiliations

  • Reza Abdi Behnagh
    • 1
  • Fardin Fathi
    • 1
  • Mohammad Yeganeh
    • 1
  • Maryam Paydar
    • 1
  • Mohsen Agha Mohammad
    • 1
  • Yiliang Liao
    • 2
    Email author
  1. 1.Faculty of Mechanical EngineeringUrmia University of TechnologyUrmiaIran
  2. 2.Department of Mechanical EngineeringUniversity of Nevada, RenoRenoUSA

Personalised recommendations