Effect of scanning strategy and speed on the microstructure and mechanical properties of selective laser melted IN718 nickel-based superalloy

  • Mostafa AmirjanEmail author
  • Hassan Sakiani
ORIGINAL ARTICLE
  • 13 Downloads

Abstract

In the present study, the properties of selective laser melted IN718 superalloy specimens, prepared by using different processing parameters, were investigated. The scanning strategy (island strategy with and without 30° interlayer rotation and continuous bi-directional scanning with and without 90° interlayer rotation) and scanning speeds of 500, 700, and 1000 mm/s were selected as variables to prepare the superalloy samples. Then, the microstructure and mechanical properties (hardness and compressive strength) were characterized. The results showed, in a given scanning strategy, the density decreases as the scanning speed increases. Also, the island strategy with interlayer rotation during fabrication process leads to a higher level of density (near full density, about 8.20 g/cm3). Interlayer rotation resulted in a more uniform structure by re-melting of deposit layers in different directions during deposition of next layers in both scanning strategies. The higher values of hardness and compressive yield strength were obtained from the samples produced using continuous scanning strategy. Among the investigated samples, the sample produced with continuous scanning strategy with 90° interlayer rotation, 500 mm/s scanning speed has the highest value of hardness, 330 Vickers, and compressive yield strength, 686 MPa.

Keywords

Selective laser melting (SLM) IN718 superalloy Scanning strategy Scanning speed 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

Notes

References

  1. 1.
    Trosch T, Strößner J, Völkl R, Glatzel U (2016) Microstructure and mechanical properties of selective laser melted Inconel 718 compared to forging and casting. Mater Lett 164:428–431CrossRefGoogle Scholar
  2. 2.
    Jia Q, Gu D (2014) Selective laser melting additive manufacturing of Inconel 718 superalloy parts: densification, microstructure and properties. J Alloys Compd 585:713–721CrossRefGoogle Scholar
  3. 3.
    Valdez M, Kozuch C, Faierson EJ, Jasiuk I (2017) Induced porosity in superalloy 718 through the laser additive manufacturing process: microstructure and mechanical properties. J Alloys Compd 725:757–764CrossRefGoogle Scholar
  4. 4.
    Xia M, Gu D, Yu G, Dai D, Chen H, Shi Q (2017) Porosity evolution and its thermodynamic mechanism of randomly packed powder-bed during selective laser melting of Inconel 718 alloy. Int J Mach Tool Manu 116:96–106CrossRefGoogle Scholar
  5. 5.
    Tucho WM, Cuvillier P, Sjolyst-Kverneland A, Hansen V (2017) Microstructure and hardness studies of Inconel 718 manufactured by selective laser melting before and after solution heat treatment. Mater Sci Eng A 689:220–232CrossRefGoogle Scholar
  6. 6.
    Deng D, Peng RL, Brodin H, Moverare J (2018) Microstructure and mechanical properties of Inconel 718 produced by selective laser melting: sample orientation dependence and effects of post heat treatments. Mater Sci Eng A 713:294–306CrossRefGoogle Scholar
  7. 7.
    Caiazzo F, Alfieri V, Corrado G, Argenio P (2017) Laser powder-bed fusion of Inconel 718 to manufacture turbine blades. Int J Adv Manuf Technol 93:4023–4031Google Scholar
  8. 8.
    Cheng B, Shrestha S, Chou K (2016) Stress and deformation evaluations of scanning strategy effect in selective laser melting. Addit Manuf.  https://doi.org/10.1016/j.addma.2016.05.007
  9. 9.
    Wang Z, Guan K, Gao M, Li X, Chen X, Zeng X (2012) The microstructure and mechanical properties of deposited-IN718 by selective laser melting. J Alloys Compd 513:518–523CrossRefGoogle Scholar
  10. 10.
    Choi JP, Shin GH, Yang S, Yang DY, Lee JS, Brochu M, Yu JH (2017) Densification and microstructural investigation of Inconel 718 parts fabricated by selective laser melting. Powder Technol 30 C:60–66CrossRefGoogle Scholar
  11. 11.
    ASTM B962-15 (2015) Standard Test Methods for Density of Compacted or Sintered Powder Metallurgy (PM) Products Using Archimedes’ Principle. ASTM International, West ConshohockenGoogle Scholar
  12. 12.
    ASTM E9-09 (2009) Standard Test Methods of Compression Testing of Metallic Materials at Room Temperature, West ConshohockenGoogle Scholar
  13. 13.
    Sames WJ, List FA, Pannala S, Dehoff RR, Babu SS (2016) The metallurgy and processing science of metal additive manufacturing. Int Mater Rev 61(5):315–360CrossRefGoogle Scholar
  14. 14.
    Greene GA, Finfrock CC (2001) Oxidation of Inconel 718 in air at high temperatures. Oxid Met 55(5):505–521CrossRefGoogle Scholar
  15. 15.
    Takamichi I, Roderick ILG (1993) The physical properties of liquid metals. Clarendon Press, OxfordGoogle Scholar
  16. 16.
    Guan K, Wang Z, Gao M, Li X, Zeng X (2013) Effects of processing parameters on tensile properties of selective laser melted 304 stainless steel. Mater Des 50:581–586CrossRefGoogle Scholar
  17. 17.
    Li R, Shi Y, Liu J, Yao H, Zhang W (2009) Effects of processing parameters on the temperature field of selective laser melting metal powder. Powder Metall Met Ceram 48(3–4):186–195CrossRefGoogle Scholar
  18. 18.
    King WE, Barth HD, Castillo VM, Gallegos GF, Gibbs JW, Hahn DE, Kamath C, Rubenchik AM (2014) Observation of keyhole-mode laser melting in laser powder-bed fusion additive manufacturing. J Mater Process Technol 214(12):2915–2925CrossRefGoogle Scholar
  19. 19.
    Raghavan S, Zhang B, Wang P, Sun C-N, Nai MLS, Li T, Wei J (2017) Effect of different heat treatments on the microstructure and mechanical properties in selective laser melted Inconel 718 alloy. Mater Manuf Process 32(14):1588–1595CrossRefGoogle Scholar
  20. 20.
    Chlebus E, Gruber K, Kuźnicka B, Kurzac J, Kurzynowski T (2015) Effect of heat treatment on the microstructure and mechanical properties of Inconel 718 processed by selective laser melting. Mater Sci Eng A 639(Supplement C):647–655CrossRefGoogle Scholar
  21. 21.
    Strößner J, Terock M, Glatzel U (2015) Mechanical and microstructural investigation of nickel-based superalloy IN718 manufactured by selective laser melting (SLM). Adv Eng Mater 17(8):1099–1105CrossRefGoogle Scholar
  22. 22.
    Mostafa APR, Brailovski V, Jahazi M, Medraj M (2017) Structure, texture and phases in 3D printed IN718 alloy subjected to homogenization and HIP treatments. Metals 7(6):23CrossRefGoogle Scholar

Copyright information

© Springer-Verlag London Ltd., part of Springer Nature 2019

Authors and Affiliations

  1. 1.Metallurgy Division, Department of Chemical and Materials EngineeringNiroo Research Institute (NRI)TehranIran
  2. 2.Faculty of mining and metallurgyAmirkabir University of TechnologyTehranIran

Personalised recommendations