Surface characterisation, corrosion and mechanical properties of polyester-polyester/snail shell powder coatings of steel pipeline for naval applications
- 7 Downloads
The pure polyester reinforced with snail shell powder (SSp) applications as coating to steel pipeline was carried out. The snail shell powder of size 75 μm in the range of 20 wt.% at 5 wt.% interval was used for these coatings. Characterisation of the snail shell powder by X-ray fluorescence (XRF) and morphological surface modification in the absence and presence of polyester and polyester reinforced with snail shell powder were also evaluated by electron microscope. The elements present before and after coatings were investigated. The steel pipelines coated with polyester/SSp being heat-treated at 150 °C were investigated for corrosion resistance by Tafel test in seawater. The mechanical and tribological properties of coated and uncoated were also investigated. The corrosion resistance properties of polyester/snail shell powder coatings were significantly improved. This was attributed to the hard coatings after heat-treated. Current density (icorr) of the steel pipeline, steel pipeline/polyester, steel pipeline/ polyester reinforced with 10 wt.% and 15 wt.% SSp in seawater was 36.61, 10.47, 9.05 and 0.81 μA/cm2 respectively. The hardness values of the formulation of polyester/snail shell powder were improved too. The test shows that addition of snail shell powder increases wear resistance of the coating reinforced with snail shell powder than polyester alone. From the above findings, the steel pipeline coated with polyester/snail shell powder in the range of 10–15 wt.% can be used conveniently in seawater environment.
KeywordsSnail shell powder Corrosion Microhardness Microstructure Wear rate
Unable to display preview. Download preview PDF.
The authors are thankful to the staff of Department of Metallurgical and Materials Engineering, University of Nigeria, Nsukka.
- 4.Takeshita Y, Sawada T, Handa T (2010) Influence of air-cooling time on physical properties of thermoplastic polyester powder coatings. Prog Org Coat 5:584–589Google Scholar
- 6.Hedayati M, Salehi M, Bagheri R, Panjepour M, Naeimi F (2012) Progress in organic coatings tribological and mechanical properties of amorphous and semi-crystalline PEEK / SiO2 nanocomposite coatings deposited on the plain carbon steel by electrostatic powder spray technique. Prog Org Coat 74:50–58CrossRefGoogle Scholar
- 9.Suleiman IY, Abdulwahab M, Awe FE (2016) Influence of particulate loading on the mechanical properties of al-4.5 Cu/GSA composite. Nig J Eng 23:86–97Google Scholar
- 15.Ghaziof S, Gao W (2015) Mechanical and chemical properties of Zn-Ni-Al2O3 nanocomposite coatings. Int J Chem Mol Nucl Mater Met Eng 9:945–949Google Scholar
- 17.Tolumoye J, Tuaweri PP, Jombo Alexander NO (2014) Corrosion resistance characteristics of Zn-Ni/SiO2 composite coatings. Int J Adv Mater Sci Eng 3:123–134Google Scholar