- 29 Downloads
Since the early development, the sectors where the composite materials are being used have been growing gradually. Nowadays, these materials have extensive application in the structural components in the aerospace, defense, transportation, civil, and energy industries. The composites, especially carbon fabric/epoxy resin, have excellent in-plane properties. However, the susceptibility to delamination from out-of-plane loads, due to the lack of fibers oriented through the thickness, is still one of the weaknesses of this kind of materials. The introduction of reinforcement through the thickness has the potential to increase out-of-plane properties of composite materials. This can be accomplished by different reinforcement methods, such as Z-pinning, stitching, and tufting. This work aimed to develop and implement a simplified method of through-the-thickness reinforcement, based on tufting reinforcement. The experimental methodology was developed in a CNC router machine where glass fiber and polyamide were used as the main reinforcement materials in different square patterns (5 × 5 and 7 × 7) and applied in laminated carbon/epoxy composites manufactured by vacuum resin transfer molding process. Then, efficiency of the reinforcement was evaluated by means of mechanical testing, i.e., tensile and end-notched flexure testing in order to evaluate the ability to improve the interlaminar fracture strength. Results showed that the presence of the reinforcements provided around 27% increase in the delamination resistance compared to the non-reinforced composites in the thickness direction.
KeywordsTTT reinforcement Tufting Interlaminar fracture toughness Delamination Carbon/epoxy composites
Unable to display preview. Download preview PDF.
The authors would like to thank Giorgio Solinas (TEXIGLASS® Company) for his support.
This study received financial support from the Brazilian agency CNPq – Conselho Nacional de Desenvolvimento Científico e Tecnológico and CAPES – Coordenação de Aperfeiçoamento de Pessoal de Nível Superior.
Compliance with ethical standards
Conflict of interest
The authors declare that they have no conflict of interest.
- 1.AST (2014a) Standard test method for determination of the mode ii interlaminar fracture toughness of unidirectional fiber-reinforced polymer matrix composites. Standard, ASTM InternationalGoogle Scholar
- 2.AST (2014b) Standard test method for tensile properties of polymer matrix composite materials. Standard, ASTM InternationalGoogle Scholar
- 4.Cândido GM, Cerqueira Rezende M, Donadon MV, Frascino Müller de Almeida S (2014) Fractografia de compósito estrutural aeronáutico submetido ao ensaio de tenacidade à fratura interlaminar em modo ii. Polímeros 24(1)Google Scholar
- 5.Colin de Verdiere M (2009) Damage and strain rate optical characterisation of standard and tufted non crimp fabric carbon composites for mesoscale impact models. PhD thesis. Cranfield UniversityGoogle Scholar
- 6.Daniel IM, Ishai O (1994) Engineering mechanics of composite materials, vol 3. Oxford University Press, New YorkGoogle Scholar
- 11.Gomes GF, da Cunha SS, Ancelotti AC (2018) A sunflower optimization (SFO) algorithm applied to damage identification on laminated composite plates. Engineering with Computers, pp. 1–8Google Scholar
- 12.Gomes GF, Mendéz YAD, Alexandrino PDSL, da Cunha SS, Ancelotti AC (2018) The use of intelligent computational tools for damage detection and identification with an emphasis on composites-a review. Compos StructGoogle Scholar
- 13.Junqueira DM, Gomes GF, Silveira ME, Ancelotti AC (2018) Design optimization and development of tubular isogrid composites tubes for lower limb prosthesis. Appl Compos Mater 1–25Google Scholar
- 17.Lombetti D (2015) Tufting of complex composite structures. PhD thesis. Cranfield UniversityGoogle Scholar
- 18.Marasco IA (2005) Analysis and evaluation of mechanical performance of reinforced sandwich structures: X-CorTM and K-CorTM. PhD thesis. Cranfield UniversityGoogle Scholar
- 21.Mouritz AP, Cox BN (2000) A mechanistic approach to the properties of stitched laminates. Compos A: Appl Sci Manuf 31(1):1–27Google Scholar
- 24.Osmiani C, Mohamed G, Treiber JWG, Allegri G, Partridge IK (2016) Exploring the influence of micro-structure on the mechanical properties and crack bridging mechanisms of fibrous tufts. Compos A: Appl Sci Manuf 91:409–419Google Scholar
- 25.Pardini LC, Levy F (2006) Compósitos estruturais: ciência e tecnologia, Edição. Ed. Edgard Blucher. São PauloGoogle Scholar
- 27.Scott M, Dell’Anno G, Clegg H (2018) Effect of process parameters on the geometry of composite parts reinforced by through-the-thickness tufting. Appl Compos Mater 1–12Google Scholar
- 28.Sickinger C, Herrmann A (2001) Structural stitching as a method to design high- performance composites in future. In: Proceedings TechTextil Symposium, Vol 2001Google Scholar
- 30.Treiber JWG (2011) Performance of tufted carbin fibre/epoxy composites. PhD thesis. Cranfield UniversityGoogle Scholar
- 31.Treiber JWG, Cartié DDR, Partridge IK (2011) Effects of mesostructure on the in-plane properties of tufted carbon fabric composites. In: 5th International Conference on Composites Testing and Model Simulation, At EPFL, Lausanne, SwitzerlandGoogle Scholar
- 34.Zhang X, Khellil K, Aboura Z (2012) Mecahnical behavior of stitched 3d composite. In: 15h European conference on composite materials, Venice, Italy, pp. 24–28Google Scholar