Strength properties of Scots pine from harbour piles degraded by erosion bacteria

Original
  • 30 Downloads

Abstract

140-year-old Scots pine piles displaying various levels of degradation by erosion bacteria were excavated from the harbour of Hamburg and investigated. Bending and compression strength correlated to the basic density, moisture content and lignin content. The compression strength was determined both on samples with dimensions of 30 mm × 20 mm × 20 mm and using 6.6 mm-increment cores taken perpendicular to the grain direction. Both sizes of the samples showed almost identical results. The sapwood of all samples was completely water-saturated; the heartwood did not even achieve 50% water saturation. The sapwood samples showed a good correlation between moisture content and strength properties, whereas basic density correlated well with the strength properties of both sapwood and heartwood. With increasing bacterial attack and resulting lower basic density, the lignin content increased in relation to holocellulose. The measured lignin content of the sapwood showed a good conformity with all strength properties. Determination of the lignin content represents an alternative method for predicting strength values of waterlogged wood while leaving most of the test material intact.

Notes

Acknowledgements

We thank the Hamburg Port Authority (HPA) for their valuable support.

References

  1. Almkvist G, Norbakhsh S, Bjurhager I, Varmuza K (2016) Prediction of tensile strength in iron-contaminated archaeological wood by FT-IR spectroscopy—a study of degradation in recent oak and Vasa oak. Holzforschung 70(9):855–865CrossRefGoogle Scholar
  2. Anagnost SE (1998) Light microscopic diagnosis of wood decay. IAWA J 19(2):141–167CrossRefGoogle Scholar
  3. ASTM D2395-14e1 Standard test methods for density and basic density (relative density) of wood and wood-based materialsGoogle Scholar
  4. Blanchette RA (2000) A review of microbial deterioration found in archaeological wood from different environments. Int Biodet Biodegr 46(3):189–204CrossRefGoogle Scholar
  5. Broda M, Mazela B, Królikowska-Pataraja K, Hill CAS (2015) The use of FT-IR and computed tomography non-destructive technique for waterlogged wood characterisation. Wood Res 60(5):707–722Google Scholar
  6. DIN 52185 (1976) Testing of wood—compression test parallel to grain. Deutsches Institut für Normung, BerlinGoogle Scholar
  7. DIN 52186 (1978) Testing of wood—bending test. Deutsches Institut für Normung, BerlinGoogle Scholar
  8. Gelbrich J, Mai C, Militz H (2008) Chemical changes in wood degraded by bacteria. Int Biodet Biodegr 61(1):24–32CrossRefGoogle Scholar
  9. Gelbrich J, Mai C, Militz H (2012) Evaluation of bacterial wood degradation by Fourier Transform Infrared (FTIR) measurements. J Cult Herit 13(3):S135-S138CrossRefGoogle Scholar
  10. ISO 3131 (1975) Wood—Determination of density for physical and mechanical tests. ISO International Organization for StandardizationGoogle Scholar
  11. Klaassen RK (2008) Bacterial decay in wooden foundation piles—patterns and causes. A study of historical pile foundations in the Netherlands. Int Biodet Biodegr 61(1):45–60CrossRefGoogle Scholar
  12. Klaassen RK (2014) Speed of bacterial decay in waterlogged wood in soil and open water. Int Biodet Biodegr 86:129–135CrossRefGoogle Scholar
  13. Lukowsky D (2015) Failure analysis of wood and wood-based products. McGraw-Hill Education, New YorkGoogle Scholar
  14. Macchioni N, Capretti C, Sozzi L, Pizzo B (2013) Grading the decay of waterlogged archaeological wood according to anatomical characterisation. The case of the Fiavé site (N-E Italy). Int Biodet Biodegr 84:54–64CrossRefGoogle Scholar
  15. Matthiesen H, Hollesen J, Dunlop R, Seither A, Beer J de (2015) In situ measurements of oxygen dynamics in unsaturated archaeological deposits. Archaeometry 57(6):1078–1094CrossRefGoogle Scholar
  16. Pedersen NB, Schmitt U, Koch G, Felby C, Thygesen LG (2014) Lignin distribution in waterlogged archaeological Picea abies (L.) Karst degraded by erosion bacteria. Holzforschung 68(7):791–798CrossRefGoogle Scholar
  17. Pizzo B, Pecoraro E, Alves A, Macchioni N, Rodrigues JC (2015) Quantitative evaluation by attenuated total reflectance infrared (ATR-FTIR) spectroscopy of the chemical composition of decayed wood preserved in waterlogged conditions. Talanta 131:14–20CrossRefPubMedGoogle Scholar
  18. Pizzo B, Macchioni N, Capretti C, Pecoraro E, Sozzi L, Fiorentino L (2016) Assessing the wood compressive strength in pile foundations in relation to diagnostic analysis. The example of the Church of Santa Maria Maggiore, Venice. Constr Building Mat 114:470–480CrossRefGoogle Scholar
  19. Rehbein M, Koch G, Schmitt U, Huckfeldt T (2013) Topochemical and transmission electron microscopic studies of bacterial decay in pine (Pinus sylvestris L.) harbour foundation piles. Micron (Oxford, England: 1993) 44:150–158CrossRefGoogle Scholar
  20. Riggio M, Sandak J, Sandak A, Pauliny D, Babiński L (2014) Analysis and prediction of selected mechanical/dynamic properties of wood after short and long-term waterlogging. Constr Building Mat 68:444–454CrossRefGoogle Scholar
  21. Schniewind AP (1990) Physical and mechanical properties of archaeological wood. In: Archaeological wood—properties, chemistry, and preservation. american chemical society, vol 225, Chap 4, pp 87–109.  https://doi.org/10.1021/ba-1990-0225.ch004
  22. Singh AP (2012) A review of microbial decay types found in wooden objects of cultural heritage recovered from buried and waterlogged environments. J Cult Herit 13(3):S16-S20CrossRefGoogle Scholar
  23. Singh AP, Kim YS, Singh T (2016) Bacterial degradation of wood. In: Kim YS, Funada R, Singh AP (eds) Secondary xylem biology, chap 9. Academic Press, Boston, pp 169–190CrossRefGoogle Scholar
  24. Thiele R (1996) Zerstörungsarme Bestimmung von inneren, festigkeitsbeschreibenden Kennwerten bei historischen Holzgründungskonstruktionen (Minor- destructive assessment of specific values that determine the strength of historical wooden foundations) (In German). Dissertation, Technische Hochschule LeipzigGoogle Scholar
  25. Uçar G, Yilgör N (1995) Chemical and technological properties of 300 years waterlogged wood (Abies bornmülleriana M.). Holz Roh Werkst 53(2):129–132CrossRefGoogle Scholar
  26. Wilcox WW (1978) Review of literature on the effects of early stages of decay on wood strength. Wood Fiber 9(4):252–257Google Scholar

Copyright information

© Springer-Verlag GmbH Germany, part of Springer Nature 2018

Authors and Affiliations

  1. 1.Fraunhofer Institute for Wood Research (WKI)BrunswickGermany
  2. 2.Wartig Nord GmbHHamburgGermany

Personalised recommendations