Effects of SiC on the Properties and Microstructures of Closed-Pore Al2O3-MgAl2O4 Refractory Aggregates

  • L. Yuan
  • Z. Yan
  • X. Zhang
  • J. Yu
Special Technologies
  • 1 Downloads

Abstract

Closed-pore Al2O3-MgAl2O4 refractory aggregates have been prepared successfully based on the superplasticity of Al2O3 ceramic by using a mixed ball-milling method and the gelcasting method. The effects of SiC content on phase composition, porosity and microstructures of the refractory aggregates have been investigated. The properties of Al2O3-MgAl2O4 refractory aggregates fabricated by different methods have been compared to our results. We discuss the influence mechanism of SiC on the refractory aggregate. The results showed that the main phase compositions were corundum and MgAl2O4 spinel with accompanying small amounts of mullite phase. The closed porosity increased with increased addition of SiC. SiC facilitated the sinterability of materials resulting in a low level of apparent porosity. When compared to the mixed ball-milling method, the closed pore size distribution in the refractory aggregates fabricated by the gelcasting method was more uniform.

Keywords

refractory aggregate closed pore gelcasting mixed ball-milling superplasticity 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. [1]
    Berjonneau, J., Prigent, P., Poirier, J.: The development of a thermodynamic model for Al2O3-MgO refractory castable corrosion by secondary metallurgy steel ladle slags. Ceram. Int. 35 (2009) 623–635CrossRefGoogle Scholar
  2. [2]
    Yan, W., Li, N., Han, B.: Influence of microsilica content on the slag resistance of castables containing porous corundum-spinel aggregates. Int. J. Appl. Ceram. Technol. 5 (2008) 633–640CrossRefGoogle Scholar
  3. [3]
    Yan, W., Chen, J., Li, N., Qiu, W., Wei, Y., Han, B.: Preparation and characterization of porous MgO-Al2O3 refractory aggregates using an in-situ decomposition pore-forming technique. Ceram. Int. 41 (2015) 515–520CrossRefGoogle Scholar
  4. [4]
    Gregorová, E., Pabst, W.: Porous ceramics prepared using poppy seed as a pore-forming agent. Ceram. Int. 33 (2007) 1385–1388CrossRefGoogle Scholar
  5. [5]
    Bai, J., Wei, C., Meng, F., Liu, J., Wang, P., Du, Q., Tang, Z.: Fabrication of porous Al2O3-MgAl2O4 ceramics using combustion-synthesized powders containing in situ produced pore-forming agents. Mater. Lett. 65 (2011) 1559–1561CrossRefGoogle Scholar
  6. [6]
    Yan, W., Li, N., Han, B.: Preparation and characterization of porous ceramics prepared from kaolinite gangue and Al(OH)3 with double addition of MgCO3 and CaCO3. Int. J. Miner. Metall. Mater. 18 (2011) 450–454CrossRefGoogle Scholar
  7. [7]
    Li, S., Li, N.: Effects of composition and temperature on porosity and pore size distribution of porous ceramics prepared from Al(OH)3 and kaolinite gangue. Ceram. Int. 33 (2007) 551–556CrossRefGoogle Scholar
  8. [8]
    Salomão, R., Bôas, M.V., Pandolfelli, V.C.: Porous alumina-spinel ceramics for high temperature applications. Ceram. Int. 37 (2011) 1393–1399CrossRefGoogle Scholar
  9. [9]
    Deng, Z., Fukasawa, T., Ando, M.: Microstructure and mechanical properties of porous alumina ceramics fabricated by the decomposition of hydroxide. J. Am. Ceram. Soc. 84 (2001) 2638–2644CrossRefGoogle Scholar
  10. [10]
    She, J., Ohji, T.: Fabrication and characterization of highly porous mullite ceramics. Mater. Chem. Phys. 80 (2003) 610–614CrossRefGoogle Scholar
  11. [11]
    She, J., Yang, J., Jayaseelan, D.D., Kondo, N., Ohji, T., Kanzaki, S., Inagaki, Y.: Thermal shock behavior of isotropic and anisotropic porous silicon nitride. J. Am. Ceram. Soc. 86 (2003) 738–740CrossRefGoogle Scholar
  12. [12]
    Kishimoto, A., Obata, M., Asaoka, H., Hayashi, H.: Fabrication of alumina-based ceramic foams utilizing superplasticity. J. Europ. Ceram. Soc. 27 (2007) 41–45CrossRefGoogle Scholar
  13. [13]
    Mao, X.J., Shimai, S., Dong, M.J., Wang, S.W.: Gelcasting of alumina using epoxy resin as a gelling agent. J. Am. Ceram. Soc. 90 (2007) 986–988CrossRefGoogle Scholar
  14. [14]
    Mao, X.J., Shimai, S., Wang, S.W.: Gelcasting of alumina foams consolidated by epoxy resin. J. Europ. Ceram. Soc. 28 (2008) 217–222CrossRefGoogle Scholar
  15. [15]
    Mazzoni, A.D., Conconi, M.S., Aglietti, E.F.: Phase stability and microstructure of MgAl2O4/SiC composites sintered in argon atmosphere. Ceram. Int. 26 (2000) 147–151CrossRefGoogle Scholar

Copyright information

© Springer Fachmedien Wiesbaden 2016

Authors and Affiliations

  1. 1.School of MetallurgyNortheastern UniversityShenyangChina

Personalised recommendations