Interceram - International Ceramic Review

, Volume 65, Issue 3, pp 100–105 | Cite as

Development of Microporous Scaffolds through Slip Casting of Solution Combustion Derived Nano Hydroxyapatite

  • R. R. RaoEmail author
  • H. N. Roopa
  • L. Mariappan
High-Performance Ceramics


HAp powder with crystallite and particle sizes in the nanorange was prepared by a solution combustion method using glycine as fuel. The powders were characterized for phase and functional group, crystallite size, particle size and agglomerate size, morphology, surface area and sericin protein adhesion. The powder had a crystallite size in the range of 10–20 nm, a particle size in the range of 100–200 nm and a surface area of 10–16 m2/g. The nanosized HAp powder was mixed with de-ionized water to prepare a slurry with solid loading in the range of 20–40 vol.-%, which was homogenized by ball milling for 16–20 h and then cast in to plaster moulds. The slip cast samples sintered at 1250°C for 1 h were found ta have a bulk density in the range of 50–78%, an apparent porosity of 13–43% and a micropore size in the range of 0.5–5.0 µm. The three-point flexural strength and compressive strength values were correlated to the porosity of sintered HAp samples.


nanohydroxyapatite solution combustion synthesis slip casting microporous scaffolds 


Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.


  1. [1]
    Hench, L.L.: Bioceramics from concept to clinic. J. Am. Ceram. Soc. 74 (1991) [7] 1487–1510CrossRefGoogle Scholar
  2. [2]
    Lobo, S.E., Arinzeh, T.L.: Biphasic calcium phosphate ceramics for bone regeneration and tissue engineering applications. Open access Materials 3 (2010) [2] 815–826Google Scholar
  3. [3]
    Bignon, A., Choreteau, J., Chevalier, J., Fantozi, G., Carret, J.-P., Chavassieux, P. et al.: Effect of micro and macro porosity of bone substitutes on their mechanical properties and cellular response. J. Mater. Sci. Mater. Med. 14 (2003) [12] 1089–97CrossRefGoogle Scholar
  4. [4]
    Hing, K.A., Annaz, B., Saeed, S., Revell, P.A., Buckland, T.: Microporosity enhances bioactivity of synthetic bone graft substitutes. J. Mater. Sci. Mater. Med. 16 (2005) [5] 467–75CrossRefGoogle Scholar
  5. [5]
    Woodard, J.R., Hilldore, A.J., Lan, S.K., Park, C.J., Morgan, A.W., Eurell J.A.C. et. al.: The mechanical properties and osteoconductivity of hydroxyapatite bone scaffolds with multi scale porosity. Biomaterials 28 (2007) 45–54CrossRefGoogle Scholar
  6. [6]
    Christenson, E.M., Anseth, K.S., van den Beucken, J.J.J.P., Chan, C.K., Ercan, B., Jansen, J.A., Laurencin, C.T., Wan-Ju Li, Murugan, R., Nair, L.S., Ramakrishna, S., Tuan, R.S., Webster, T.J., Mikos, A.G.: Nanobiomaterial applications in orthopedics. J. Orthopaedic Res. 25 (2007) [1] 11–22CrossRefGoogle Scholar
  7. [7]
    Ramachandra Rao, R., Roopa, H.N., Kannan, T.S.: Solid state synthesis and thermal stability of HAp and HAp-β-TCP composite ceramic powder. J. Mater. Sci. Mater. Med. 8 (1997) [8] 511–518CrossRefGoogle Scholar
  8. [8]
    Nayak, A.K.: Hydroxyapatite synthesis methodologies: An overview. Int. J. Chem. Tech. Res. 2 (2010) [2] 903–907Google Scholar
  9. [9]
    Ferraz, M.P., Monteiro F.J., Manuel, C.M.: Hydroxyapatite nanoparticles: A review of preparation methodologies. J. Appl. Biomater. and Biomech. 2 (2004) 74–80Google Scholar
  10. [10]
    Cuneyt Tas, A.: Combustion synthesis of calcium phosphate bioceramic powders. J. Eur. Ceram. Soc. 20 (2000) [14–15] 2389–2394Google Scholar
  11. [11]
    Han, Y., Li, S., Wang, X., Chen, X.: Synthesis and sintering of nanocrystalline hydroxyapatite powders by citric acid sol-gel combustion method. Mater. Res. Bull. 39 (2004) [1] 25–32CrossRefGoogle Scholar
  12. [12]
    Pratihar, S.K., Garg, M., Mehra, S., Bhattacharya, S.: Phase evolution and sintering kinetics of hydroxyapatite synthesized by solution combustion technique. J. Mater. Sci. Mater. Med. 17 (2006) [6] 501–507CrossRefGoogle Scholar
  13. [13]
    Sasikumar, S., Vijayaraghavan, R.: Synthesis and characterization of bioceramic calcium phosphates by rapid combustion synthesis. J. Mater. Sci. Technol. 26 (2010) [12] 114–118CrossRefGoogle Scholar
  14. [14]
    Ghosh, S.K., Roy, S.K., Kundu, B., Datta, S., Basu, D.: Synthesis of nano-sized hydroxyapatite powders through solution combustion route under different reaction conditions. Mater. Sci. and Eng. B, 176 (2011) [1] 14–21CrossRefGoogle Scholar
  15. [15]
    Ramachandra Rao R., Kannan, T.S.: Dispersion and slip casting of hydroxyapatite. J. Am. Ceram. Soc. 84 (2001) [8] 1710–1716Google Scholar
  16. [16]
    Ramachandra Rao, R., Mariappan L., Roopa, H.N.: Fabrication of micro-featured shapes of alumina ceramics. Procedia Mater. Sci. 5 (2014) 2595–2604CrossRefGoogle Scholar
  17. [17]
    Began, H., Chanda, A., Kundu, B.: Development of nano-grained calcium hydroxyapatite using slip casting technique. Int. J. Scientific and Eng. Res. 21 (2001) [3] 1–7Google Scholar
  18. [18]
    Sepulveda, P., Ortega, F.S., Innocentini M.D.M., Pandolfelli, V.C.: Properties of highly porous hydroxyapatite obtained by the gel casting of foams. J. Am. Ceram. Soc. 83 (2000) [12] 3021–3024CrossRefGoogle Scholar
  19. [19]
    Lee, E., Koh, Y., Yoon, B., Kim, H., Kim, H.: Highly porous hydroxyapatite bioceramics with interconnected pore channels using camphene-based freeze casting. Mater. Letters 61 (2007) 2270–2273CrossRefGoogle Scholar
  20. [20]
    Arita, I.H., Wilkinson D.S., Castazo, V.M.: Synthesis and processing of hydroxyapatite ceramic tapes with controlled porosity. J. Mater. Sci. Mater. Med. 6 (1995) [1] 19–23CrossRefGoogle Scholar
  21. [21]
    Bose, S., Vahabzadeh, S., Bandyopadhyay, A.: Bone tissue engineering using 3D printing. Materials today 16 (2013) [12] 496–504CrossRefGoogle Scholar
  22. [22]
    Hutmacher, D.W., Sittinger M., Risbud, M.V.: Scaffold-based tissue engineering: Rationale for computer-aided design and solid free-form fabrication systems. Trends in Biotechnology 22 (2004) [7] 354–362CrossRefGoogle Scholar
  23. [23]
    Ramachandra Rao, R.: Current Trends in Processing and Shaping of Bioceramics. E-Book Chapter in: Current Trends on Glass and Ceramic Materials, Eds. Sooraj Hussain, N., da Silva Santos, J.D., University of Porto, Portugal, Bentham Science Publishers, The Netherlands (2013) 3–48, ISBN: 978-1-60805-514-2, eISBN: 978-1-60805-452-7Google Scholar
  24. [24]
    Thangamani, N., Chinnakali K., Gnanam, F.D.: The effect of powder processing on densification, microstructure and mechanical properties of hydroxyapatite. Ceram. Inter. 28 (2002) [4] 355–362CrossRefGoogle Scholar
  25. [25]
    Tian, T., Jiang, D., Zhang J., Lin, Q.: Aqueous tape casting process for hydroxyapatite. J. Eur. Ceram. Soc. 27 (2007) 2671–2677.CrossRefGoogle Scholar
  26. [26]
    Padilla, S., Vallet-Regí, M., Ginebra M.P., Gil, F.J.: Processing and mechanical properties of hydroxyapatite pieces obtained by the gelcasting method. J. Eur. Ceram. Soc. 25 (2005) 375–383CrossRefGoogle Scholar
  27. [27]
    Kikuchi, M.: Effect of test circumstances on compressive strength of porous calcium phosphate ceramics for establishment of standard measurement condition. Bioceramics Develop. and Appl. 1 (2011) 1–3, doi:  10.4303/bda/D101201CrossRefGoogle Scholar

Copyright information

© Springer Fachmedien Wiesbaden 2016

Authors and Affiliations

  1. 1.Materials Science DivisionCSIR-National Aerospace laboratoriesBangaloreIndia

Personalised recommendations