Lightweight Magnesium Oxychloride-Based Building Units from Egyptian Raw Magnesite

  • A. Tawfik
  • F. Abd El-Raoof
  • M. A. Serry
Raw Materials Worldwide

Abstract

Water resistant magnesium oxychloride (MOC)-based building products were prepared from different two samples of raw magnesite and rice straw waste up to 10 mass-%. Active magnesium oxide as starting material for the preparation of MOC was prepared from raw magnesite by calcination at temperatures of 650 and 1000°C. MOC-based lightweight building units can be prepared with a bulk density range between 1.0–1.4 g/cm3 with a compressive strength of up to 27 MPa and a modulus of rupture of up to 11 MPa. Selected samples were investigated using XRD and TEM. The XRD characterization results revealed the formation of phase 5, phase 3 and chlorartinite. The TEM informed that these phases are at nano scale.

Keywords

magnesium oxychloride raw magnesite rice straw waste phases microstructure 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. [1]
    Xiangming Zhou, Zongjin Li: Light-weight wood-magnesium oxychloride cement composite building products made by extrusion. Constr. and Build. Mater. 27 (2012) [1] 382–389CrossRefGoogle Scholar
  2. [2]
    Erdman S.V., Gapparova, K.M., Khudyakova, T.M., Tomshinaa, A.V.: Magnesia binder preparation from local natural and technogenic raw materials. Procedia Chemistry 10 (2014) 310–313CrossRefGoogle Scholar
  3. [3]
    Sorel S.: On a new magnesium cement. Comptes Rendus-Academie des Sciences [J] France 65 (1867) 102–104Google Scholar
  4. [4]
    Beaudin J.J., Ramachandran V.S.: Strength development in magnesium oxychloride and other cement. Cem. Conc. Res. 5 (1975) 617–630CrossRefGoogle Scholar
  5. [5]
    Beaudin, J.J., Ramachandran, V.S., Feldman, R.F.: Impregnation of magnesium oxychloride cement with sulfur. Am. Ceram. Soc. Bull. 56 (1977) [4] 424–427Google Scholar
  6. [6]
    Hewlett, P.C.: Lea’s chemistry of cement and concrete. Chap. 14 of special cements, 4th edition Arnold, New York-Toronto (1994) 813–815, ISBN: 0 470 24416 XGoogle Scholar
  7. [7]
    Deng, D., Zhang, C.: The formation mechanism of the hydrate phases in magnesium oxychloride cement. Cem. Conc. Res. 29 (1999) 1365–1371CrossRefGoogle Scholar
  8. [8]
    Chau, C.K., Zongjin Li: Microstructures of magnesium oxychloride. Materials and Structures 41 (2008) 853–862CrossRefGoogle Scholar
  9. [9]
    Misra A.K., Renu, M.: Magnesium oxychloride cement concrete. Indian Academy of Sciences, Bull. Mater. Sci. 30 (2007) [3] 239–246CrossRefGoogle Scholar
  10. [10]
    Tawfik, A., Serry, M.A.: Factors influencing the phase composition and properties of magnesium oxychloride cements. Interceram 62 (2013) [1] 25–29Google Scholar

Copyright information

© Springer Fachmedien Wiesbaden 2015

Authors and Affiliations

  1. 1.National Research CenterDokki, CairoEgypt

Personalised recommendations