Interceram - International Ceramic Review

, Volume 63, Issue 3, pp 125–129 | Cite as

Influence of Calcination Temperature on the Densification of Refractory Mullite Grains Synthesized from Recycled Materials

  • S. E. Ahmed
  • F. Abd El-Raoof
  • M. A. Serry
Special Technologies
  • 5 Downloads

Abstract

Dense refractory mullite (3Al2O3·2SiO2) grains were synthesized by mechanical mixing of calculated amounts of pure ultra-fine Al-hydroxide and water-treated fumed silica powders. The powders were obtained by acid leaching of recycled Al-dross and boiling of fumed silica in water. Mixed powder samples were calcined at 900, 1000, 1100 and 1200°C and characterized with respect to phase composition, surface area, linear shrinkage and bulk density. They were then re-powdered, pressed and re-fired at 1650°C to determine which pre-calcined batch achieved maximum densification of its mullite grains. The solid phase composition, microstructure and microchemistry refractory properties of the dense, fired mullite samples were investigated, including volume stability and load-bearing capacity in terms of the temperature of maximum expansion (To), the temperature at beginning of subsidence under load (Ta), and the rate of creep at 1500°C. XRD, SEM and EDS were applied in the analysis.

Pre-calcination of the precipitated Al hydroxide/washed fumed silica at 1000–1100°C yielded a reactive amorphous Al2O3/SiO2 powder mixture with some crystalline major corundum and minor silica phases. This phase assemblage was best able to form dense stable mullite grains when re-fired at temperatures up to 1650°C. The mullite showed high refractory quality when tested for load-bearing capacity and volume stability. On firing under load up to 1500°C, the material linearly expanded 0.7%, with beginning of subsidence occurring above 1500°C. The sample also had minimal creep rate (0.2%/h) on firing under load for 1 h at 1500°C, and 0.0% permanent linear change after re-firing at 1600°C. As a result, the dense mullite samples prepared from mixed powders pre-calcined at 1000–1100°C can be recommended for applications at or above 1600°C service temperatures.

Keywords

synthetic mullite calcination densification refractory quality volume stability loadbearing capacity 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. [1]
    Brindley, G.E., Nakahira, M.: The kaolinite-mullite reaction series, Part 1: A Survey of Outstanding Problems; Part II: Metakaolin; Part III: The high temperature phases. J. Amer. Ceram. Soc. 42 (1959) [7] 311, 314, 319CrossRefGoogle Scholar
  2. [2]
    Grace, A., Low, I.M., Burton, G.R., Garrod, T., Zhou, T., Skala, R.D., Phillips, D.N., Pillai, X.M: Synthesis and properties of mullite ceramics derived from fumed silica and various alumina. J. of Mater. Sci. Letters 14 (1995) [18] 1310–1313CrossRefGoogle Scholar
  3. [3]
    Chen, C.Y., Lan, G.S., Tuan, W.H.: Preparation of mullite by the reaction sintering of kaolinite & alumina. J. Europ. Ceram. Soc. 20 (2000) 2519–2525CrossRefGoogle Scholar
  4. [4]
    Chen, C.Y., Lan, G.S., Tuan, W.H.: Microstructure evolution of mullite during the sintering of kaolin powder compacts. Ceram. Internat. 26 (2000) 715–720CrossRefGoogle Scholar
  5. [5]
    Chen, Y.F., Wang, M.C., Hon, M.H.: Phase transformation and growth of mullite in kaolin ceramics. J. Europ. Ceram. Soc. 24 (2004) 2389–2397CrossRefGoogle Scholar
  6. [6]
    Serry, M.A., Ahmed, S.E., Elmaghraby, M.S.: Shaped MgO-Al2O3-SiO2 refractory ceramics from recycled materials. Advances in Applied Ceramics 106 (2007) [3]Google Scholar
  7. [7]
    Kim, B.M., Cho, Y.K., Yoon, S.Y., Stevens, R., Park, H.C.: Mullite whiskers derived from kaolin. Ceram. Internat. 35 (2007) 579–583CrossRefGoogle Scholar
  8. [8]
    Auran, G., Jiachen, L., Rui, X.U., Hai, X.U., Caifen, W.: Preparation of mullite from desilication-flyash. Fuel 89 (2010) 3630–3636CrossRefGoogle Scholar
  9. [9]
    Tripathi, R.S., Ghosh, A., Halder, M.K., Mukherjee, B., Maiti, H.S.: Microstructure and properties of sintered mullite developed from Indian bauxite. Bull. Mater. Sci. 35 (2012) [4] 639–643CrossRefGoogle Scholar
  10. [10]
    Ryshkewitch, E.: Oxide ceramics: physical chemistry and technology. Academic Press Inc, New York and London, (1960)Google Scholar
  11. [11]
    Kingery, W.D., Bowen, H.K., Uhlmann, D.R.: Introduction to ceramics. Willey Interscience, New York, (1975)Google Scholar
  12. [12]
    Clifton, G., Bergeron, Subhash, H., Risbud: Introduction to Phase Equilibria in Ceramics, 2nd Ed., Amer. Ceram. Soc. Inc. Columbus, Ohio, (1984)Google Scholar
  13. [13]
    Carniglia, S.C., Barna, G.: Handbook of industrial refractories technology. Noyes-Publications, Park-Ridge, USA, (1992)Google Scholar
  14. [14]
    Schacht, C.A.: Refractories Handbook. Marcel Dekker Inc., New York, Basel, (2004)CrossRefGoogle Scholar
  15. [15]
    Routschka, G.: Refractory materials: pocket manual. Vulkan Verlag, Essen, Germany, (2004)Google Scholar
  16. [16]
    Novak, A.E.: Refractory Engineering: Materials, Design & Construction, 2nd Ed., Vulkan Verlag, Essen, Germany, (2005)Google Scholar
  17. [17]
    Schneider, M.H., Schreuer, J., Hildmann, B.: Structure and properties of mullite — A review. J. Europ. Ceram. Soc. 28 (2008) [2] 1329–1344CrossRefGoogle Scholar
  18. [18]
    Okamaoto, Y., Fukudome, H., Hayashi, K., Nishikawa, T.: Creep deformation of polycrystalline mullite. J. Europ. Ceram. Soc. 6 (1990) 1661–1668Google Scholar
  19. [19]
    Schneider, H., Eberhard, E.: Thermal expansion of mullite. J. Amer. Ceram. Soc. 73 (1990). (67) 2073CrossRefGoogle Scholar
  20. [20]
    Osendi, M.I., Bandin, C.: Mechanical properties of mullite materials. J. Europ. Ceram. Soc. 16 (1996) [2] 217–224CrossRefGoogle Scholar
  21. [21]
    Hildmann, B., Schneider, H.: Heat capacity of mullite-new data & evidence for a high-temperature phase transformation. J. Amer. Ceram. Soc. 87 (2004) [2] 227–234CrossRefGoogle Scholar
  22. [22]
    Ahmed, S.E.: Recycling of aluminum dross in the preparation of pure corundum and alum. MSc. thesis, “Institute of Environmental Studies and Research”, Ain Shams University, Cairo, (1998)Google Scholar
  23. [23]
    Ahmed, S.E.: Refractory oxide ceramics within the MgO-Al2O3-SiO2 system from recycled materials. Ph.D. thesis, Faculty of science, Helwan University Cairo, (2005)Google Scholar
  24. [24]
    Abd El-Raoof, F.: Assessment of developed refractory composites for slide gates of continuous steel casting systems. Ph.D. thesis, Faculty of Science, Zagazig Universty, Zagazig, Egypt, (2008)Google Scholar
  25. [25]
    Mackenzie, R.C.: Differential thermal analysis. Vol. 1, Academic Press, London and New York, (1970)Google Scholar
  26. [26]
    Dumitru, N.T.: Thermal analysis of minerals. ABACUS Press, United Kingdom, (1976)Google Scholar

Copyright information

© Springer Fachmedien Wiesbaden 2014

Authors and Affiliations

  1. 1.Ceramic, Refractories and Building Materials DepartmentNational Research CentreCairoEgypt

Personalised recommendations