High temperature deformation and fracture mechanisms in a nickel aluminide alloy
- 101 Downloads
The mechanisms that control high temperature deformation and fracture were studied in a nickel aluminide(Ni3Al) alloy that was thermo-mechanically treated to produce a non-porous microstructure. Comparisons of data corresponding to the dendritic morphology with that for the equiaxed grain structures indicated that the dendritic morphology results in a significantly lower creep rates as well as substantially greater times to rupture. From the microstructural observations, isolated interdendritic cavitation in th absence of grain boundary sliding was found to lead to rupture lifetime that are longer than those observed for the other microstructures.
Key WordsNickel Aluminide Creep Deformation High Temperature Facture Dendritic Microstructure Creep Damage Tolerance Creep Rupture Lifetimes Creep Cavity Damage
Unable to display preview. Download preview PDF.
- Bendersky, L., Rosen, A. and Mukherjee, A. K., 1985, “Creep and Dislocation Substructure.”International Materials Reviews, Vol. 30, pp. 1–15.Google Scholar
- Hemker, K. J., 1991, “A Study of High Temperature Deformation in the Intermetallic Alloy Ni3Al,” Ph. D Dissertation, Stanford University.Google Scholar
- Stoloff, N. S., 1989, “Physical and Mechanical Metallurgy of Ni3Al and Its Alloys,”International Materials Reviews, Vol. 34, pp. 152–183.Google Scholar