Mechanical properties of haynes alloy 188 after 22,500 hours of exposure to LiF-22CaF2 and vacuum at 1093 K

  • 54 Accesses

  • 7 Citations

Abstract

As a continuation of a study of a space-based thermal energy storage system centered on a LiF-CaF2 eutectic salt contained by Haynes alloy 188, this Co-base superalloy was subjected to molten salt, its vapor, and vacuum for 22,500 h at 1093 K. Samples from all three exposure conditions were tensile tested between 77 to 1200 K; in addition, vacuum and molten-salt exposed specimens were vacuum creep rupture tested at 1050 K. Comparison of these mechanical properties with those measured for the as-received alloy reveals no evidence for degradation beyond that ascribed to simple thermal aging of Haynes alloy 188. This behavior is identical to the 10,000 h results (Ref 3); hence, Haynes alloy 188 is a suitable containment material for an eutectic LiF-CaF2 thermal energy storage salt.

This is a preview of subscription content, log in to check access.

Access options

Buy single article

Instant unlimited access to the full article PDF.

US$ 39.95

Price includes VAT for USA

Subscribe to journal

Immediate online access to all issues from 2019. Subscription will auto renew annually.

US$ 408

This is the net price. Taxes to be calculated in checkout.

References

  1. 1.

    T.L. Labus, R.R. Secunde, and R.G. Lovely, Solar Dynamic Power Module Design, paper No. 899277 in IECEC ’89, Vol 1, Institute for Electrical and Electronic Engineers, New York, 1989, p 299–307

  2. 2.

    J.D. Whittenberger,J. Mater. Eng., Vol 12, 1990, p 211–226

  3. 3.

    J.D. Whittenberger,J. Mater. Eng. Perform., Vol 1, 1992, p 469–482

  4. 4.

    J.D. Whittenberger,J. Mater. Eng. Perform., Vol 2, 1993, p 745–757

  5. 5.

    J.D. Whittenberger,J. Mater. Eng. Perform., Vol 3, 1994, p 91–104

  6. 6.

    Haynes International Data Sheet for Haynes Alloy 188, Data sheer is available from Haynes International, 1020 West Park Ave., Kokomo, IN 46904-9013, USA

Download references

Author information

Correspondence to J. D. Whittenberger.

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Whittenberger, J.D. Mechanical properties of haynes alloy 188 after 22,500 hours of exposure to LiF-22CaF2 and vacuum at 1093 K. J. of Materi Eng and Perform 3, 754–762 (1994). https://doi.org/10.1007/BF02818376

Download citation

Keywords

  • Haynes alloy 188
  • heat treatment
  • long term exposure
  • mechanical properties
  • superalloy
  • thermal energy storage