Mobile harbor crane wheel hub fatigue failure
- 173 Downloads
Failure analysis of a mobile harbor crane wheel hub demonstrated that the mechanism of failure was fatigue. The wheel hub was a ductile cast iron component that had been subjected to cyclic loading during a ten-year service period. The fracture surface of the fatigue failure also contained corrosion deposit, suggesting that cracking occurred over a period of time sufficient to allow corrosion of the cracked surfaces. Replacement and alignment of the failed wheel hub is recommended along with inspection of the nonfailed wheel hubs that remain on the crane.
Keywordscast iron corrosion ductile EDS fatigue SEM
Unable to display preview. Download preview PDF.
- 1.W.D. Callister, Jr.:Materials Science and Engineering: An Introduction, 5th ed., John Wiley & Sons, 2000, pp. 365–67.Google Scholar
- 2.R.E. Reed-Hill:Physical Metallurgy Principles, 2nd ed., D. Van Nostrand Co., New York, 1973, pp. 810–11.Google Scholar
- 3.P.F. Thomason:Ductile Fracture of Metals, Pergamon Press, Oxford, 1990, pp. 1–29.Google Scholar
- 4.R.M. Thomson:Physical Metallurgy, 3rd ed., R.W. Cahn and P. Haasen, Ed., Elsevier Science Publ. BV, 1983, pp. 1487–551.Google Scholar
- 5.C.R. Brooks and A. Choudhury:Metallurgical Failure Analysis, McGraw-Hill, Inc., 1993, pp. 119–269.Google Scholar
- 6.S. Kocanda:Fatigue Failure of Metals, Sijthoff and Noordhoff Int. Publ., Warsaw, 1978, pp. 269–362.Google Scholar
- 7.V.J. Colanjelo and F.A. Heiser:Analysis of Metallurgical Failures, 2nd ed., John Wiley & Sons, 1987, pp. 133–61.Google Scholar