Metallurgical failure analysis of titanium wing attachment bolts
- 174 Downloads
Two titanium alloy wing attachment bolts from a commercial jetliner failed during the course of a routine service operation. Failure of the bolts occurred during the re-torque process as the wing was being reattached. Metallurgical failure analysis indicated that the fracture mechanism was ductile overload and that the mechanical properties of the bolts were consistent with exemplar bolts that had been supplied. After eliminating other sources of excessive load application, the most probable cause of failure was ascribed to variances between the frictional characteristics of the bolt at the time of re-torque and at the time of initial torque application several years earlier.
Keywordsaerospace fasteners failure analysis fractography titanium
Unable to display preview. Download preview PDF.
- 1.S.C. Cedarquist: “Improving Aging Airplane Safety,”Mater. Performance, 2000,39, pp. 20–5.Google Scholar
- 2.M.E. Hoffman and P.C. Hoffman: “Corrosion and Fatigue Research-Structural Issues and Relevance to Naval Aviation,”Int. J. Fatigue, 2001,23, pp. S1–10.Google Scholar
- 4.S.M. Sadri: “Aerospace Bolts,”Handbook of Bolts and Bolted Joints, J.H. Bickford and S. Nassar, ed., Marcel Dekker, Inc., 1998.Google Scholar
- 5.J. Barron: “Computing the Strength of a Fastener,”Handbook of Bolts and Bolted Joints, J.H. Bickford and S. Nassar, ed., Marcel Dekker, 1998, pp. 163–78.Google Scholar
- 6.J.A. Williams:Engineering Tribology, Oxford University Press, 1994.Google Scholar
- 7.N.E. Dowling:Mechanical Behavior of Materials, 2nd ed., Prentice Hall, London, 1999.Google Scholar
- 8.H. Terada: “Structural Fatigue and Joint Degradation,”Int. J. Fatigue, 2001,23, pp. S21–30.Google Scholar