Biologically induced corrosion and consequent fracture of a pump shaft coupling
- 68 Downloads
During a routine start-up exercise of a standby service water pump, a threaded coupling that joined sections of a 41.5 ft (12.7 m) long pump shaft experienced fracture. The pump was taken out of service and examined to determine the cause of fracture. It was apparent early in the examination that the fracture involved hydrogen stress cracking. However, the nature of the corrosive attack suggested an interaction between the threaded coupling and biological organisms living in the freshwater environment of the pump shaft. The organisms had colonized on the coupling, changing the local environment and creating conditions favorable to hydrogen stress cracking. This paper describes the analysis of the fracture of the coupling and provides an example of how biologically induced corrosion can result in unexpected fracture of a relatively basic machine part.
Keywordsbiological organisms corrosion hydrogen stress cracking stainless steel
Unable to display preview. Download preview PDF.
- 1.C.D. Kim: Hydrogen Damage Failures,Failure Analysis and Prevention, vol. 11,ASM Handbook, American Society for Metals, 1986, pp. 245–6.Google Scholar
- 2.R.K. Churchill et al.: Failures of Steel Castings,Failure Analysis and Prevention, vol. 11,ASM Handbook, American Society for Metals, 1986, pp. 408–10.Google Scholar
- 3.Anon.: ASTM A 582-88, “Standard Specification for Free-Machining Stainless and Heat Resisting Steel Bars, Hot-Rolled or Cold Finished,” American Society for Testing and Materials, West Conshohocken, PA, 1991.Google Scholar
- 4.Anon: Heat Treating of Stainless Steels,Heat Treating, vol. 4,ASM Handbook, ASM International, 1991, p. 778.Google Scholar
- 5.ASM Handbook, Vol. 13, Corrosion, ASM International, Metals Park, OH, 1987, pp. 114–22, 314–5.Google Scholar
- 6.G. Kobrin: “Corrosion by Microbiological Organisms in Natural Waters,” inCorrosion Source Book, American Society for Metals, Metals Park, OH, 1984, pp. 365–70.Google Scholar