Linear elastic fracture mechanics (LEFM) analysis of the effect of residual stress on fatigue crack propagation rate

  • Y. Prawoto
Peer Reviewed Articles

Abstract

In this research, both residual and applied stresses are converted to stress intensity factors independently and combined using the superposition principle. The fatigue crack propagation rates are predicted. Experiments using two different loading modes, constant applied stress intensity factor (SIF) range, and constant applied load modes are done for samples with and without initial tensile residual stresses. The samples with initial tensile residual stresses exhibit accelerations of the crack propagation rates. The results show that the weight function method combined with the three-component model provides a good prediction of fatigue crack propagation rates in tensile residual stress fields.

Keywords

fatigue crack propagation linear elastic fracture mechanics residual stress three-component model weight function 

References

  1. 1.
    J.H. Underwood, L.P. Pook, and J.K. Sharples: Fatigue Crack Propagation Through a Measured Residual Stress Field in Alloy Steel,Flaw Growth and Fracture, ASTM STP631, ASTM, W. Conshohocken, PA, 1977, pp. 402–15.Google Scholar
  2. 2.
    J.H. Underwood: “Residual Stress Effects at a Notch Root in A723 Steel to Extend Fatigue Life,”Exp. Mech., March 1995, pp. 61–65.Google Scholar
  3. 3.
    W. Elber: The Significance of Fatigue Crack Closure,Damage Tolerance in Aircraft Structure, ASTM STP486, ASTM, W. Conshohocken, PA, 1971, pp. 230–42.Google Scholar
  4. 4.
    D.V. Nelson: Effects of Residual Stress on Fatigue Crack Propagation,Residual Stress Effects in Fatigue, ASTM STP776, ASTM, W. Conshohocken, PA, 1982, pp. 172–94.Google Scholar
  5. 5.
    A.P. Parker: Stress Intensity Factors, Crack Profiles, and Fatigue Crack Growth Rates in Residual Stress Fields,Residual Stress Effects in Fatigue, ASTM STP776, ASTM, W. Conshohocken, PA, 1982, pp. 13–31.Google Scholar
  6. 6.
    A. Saxena, S.J. Hudak, Jr., and G.M. Jouris: “A Three Component Model for Representing Wide Range Fatigue Crack Growth Data,”Eng. Fract. Mech., 1979,12, pp. 103–15.CrossRefGoogle Scholar
  7. 7.
    M.S. Miller and J.P. Gallagher: An Analysis of Several Fatigue Crack Growth Rate Descriptions,Fatigue Crack Growth Measurement and Data Analysis, ASTM STP738, ASTM, W. Conshohocken, PA, 1981, pp. 205–51.Google Scholar
  8. 8.
    K. Walker: The Effect of Stress Ratio During Crack Propagation and Fatigue for 2024-T3 and 7075-T6 Aluminum,Effects of Environment and Complex Load History on Fatigue Life, ASTM STP462, ASTM, W. Conshohocken, PA, 1970, pp. 1–14.Google Scholar
  9. 9.
    X.R. Wu: “Approximate Weight Functions for Center and Edge Cracks in Finite Bodies,”Eng. Fract. Mech., 1984,20(1), pp. 35–49.CrossRefGoogle Scholar
  10. 10.
    X.R. Wu and A.J. Carlsson:Weight Functions and Stress Intensity Factor Solutions, Pergamon Press, Oxford, 1991.Google Scholar
  11. 11.
    T. Fett and D. Munz:Stress Intensity Factors and Weight Functions, Computational Mechanics Publications, Southampton, U.K., 1997.Google Scholar
  12. 12.
    W.J. Mills and L.A. James: “Residual Stress Effects on Fatigue Crack Growth Behavior in Stainless Steel Welds,”J. Press. Vess.-T. ASME, 1987,109, pp. 336–39.CrossRefGoogle Scholar
  13. 13.
    A. Stacey and G.A. Webster: Stress Intensity Factors Caused by Residual Stress Fields in Autofrettaged Tubing,Analytical and Experimental Methods for Residual Stress Effects in Fatigue, ASTM STP1004, ASTM, W. Conshohocken, PA, 1988, pp. 37–53.Google Scholar
  14. 14.
    N. Nguyen and M.A. Wahab: “The Effect of Residual Stresses on Fatigue of Butt Joints,”Weld. J., 1996,75, pp. 55.s-61.s.Google Scholar
  15. 15.
    Y.Z. Itoh: “Prediction of Fatigue Crack Growth Rate in Welding Residual Stress Field,”Eng. Fract. Mech., 1989,33(3), pp. 397–407.CrossRefGoogle Scholar
  16. 16.
    A. Okamoto and H. Nakamura: “The Influence of Residual Stress on Fatigue Cracking,”J. Press. Vess.-T. ASME, 1990,112, pp. 199–203.Google Scholar
  17. 17.
    A.F. Liu: “The Effect of Residual Stresses on Crack Growth from a Hole,”AIAA J., 1984,22(12), pp. 1784–85.CrossRefGoogle Scholar
  18. 18.
    G. Glinka: Effect of Residual Stresses on Fatigue Crack Growth in Steel Weldments Under Constant and Variable Amplitude Loads,Fracture Mechanics, ASTM STP677, ASTM, W. Conshohocken, PA, 1979, pp. 198–214.Google Scholar
  19. 19.
    G. Glinka:Residual Stresses in Fatigue and Fracture: Theoretical Analyses and Experiments, Advances in Surface Treatments: Technology-Applications-Effects, Pergamon Press, 1987, pp. 413–54.Google Scholar
  20. 20.
    A. Todoroki and H. Kobayashi: “Prediction of Fatigue Crack Growth Rate in Residual Stress Field (Application of Superposition Technique),”T. Jpn. Soc. Mech. Eng. A., 1988,54, pp. 30–36.Google Scholar
  21. 21.
    A. Todoroki and H. Kobayashi: Prediction of Fatigue Crack Growth Rate in Residual Stress Fields,Fracture and Strength ’90: Proc. LSME/JSME Joint Conf., Seoul, Korea, 1990,51–52, pp. 367–72.Google Scholar
  22. 22.
    J. Lu, J.F. Flavenot, and A. Turbat: Prediction of Residual Stress Relaxation During Fatigue,Mechanical Relaxation of Residual Stresses, ASTM STP993, ASTM, W. Conshohocken, PA, 1988, pp. 75–90.Google Scholar
  23. 23.
    R.A. Winholtz and J.B. Cohen: “Changes in the Macrostresses and Microstresses in Steel with Fatigue,”Mater. Sci. Eng., 1992,A154, pp. 155–63.Google Scholar
  24. 24.
    A. Saxena and S.J. Hudak: Role of Crack Tip Stress Relaxation in Fatigue Crack Growth,Fracture Mechanics: 11th Symp., ASTM STP677, ASTM, W. Conshohocken, PA, 1979, pp. 215–31.Google Scholar
  25. 25.
    Standard Test Methods for Measurement of Fatigue Crack Growth Rates, ASTM E647-95a.Google Scholar
  26. 26.
    J.D. Almer, J.B. Cohen, and R.A. Winholtz: “The Effects of Residual Macrostresses and Microstresses on Fatigue Crack Initiation and Growth,”Metall. Mater. Trans. A., 1998,29A, pp. 2127–36.CrossRefGoogle Scholar
  27. 27.
    MTS Systems Corporation,759.40 Testware Fatigue Crack Growth Test Operator’s Guide, MTS System Corporation, Eden Prairie, MN, 1993.Google Scholar
  28. 28.
    J.D. Almer, J.B. Cohen, K.R. McCallum, and R.A. Winholtz:Proc. 5th Int. Conf. on Residual Stress, T. Erricson and M. Oden, ed., Soc. Exp. Mech., Bethel, CT, 1997, pp. 1072–77.Google Scholar
  29. 29.
    Y. Prawoto and R.A. Winholtz: The Growth Rate and Plastic Zone Size Variations of a Fatigue Crack Grown in a Tensile Residual Stress Field,Proceedings of the Eighth International Conference on Nuclear Engineering, American Society of Mechanical Engineers, Paper 8785, 2000.Google Scholar

Copyright information

© ASM International - The Materials Information Society 2002

Authors and Affiliations

  • Y. Prawoto
    • 1
  1. 1.Laboratory for Strength of Materials, Components, and StructuresUPT-LUK BPPT, PUSPIPTEKTangerangIndonesia

Personalised recommendations