This is a preview of subscription content, log in to check access.
Buy single article
Instant access to the full article PDF.
Price includes VAT for USA
Subscribe to journal
Immediate online access to all issues from 2019. Subscription will auto renew annually.
This is the net price. Taxes to be calculated in checkout.
Kh. L. Logan, Corrosion of Metals Under Stress [in Russian]. Metallurgiya, Moscow (1970).
R. K. Melekhov, The Corrosion Cracking of Titanium and Aluminum Alloys [in Russian], Tekhnika, Kiev (1979).
G. Keshe, The Corrosion of Metals: Physicochemical Principles and Pressing Problems [in Russian], Metallurgiya, Moscow (1984).
“The corrosion cracking of metals,” in: Accomplishments of the Sciences of Corrosion and Methods of Protection from It [in Russian], Metallurgiya, Moscow (1985), pp. 149–297.
O. D. Smiyan, M. V. Koval', R. K. Melekhov, et al., “Local corrosion damage of aluminum alloys,” Fiz.-Khim. Mekh. Mater., No. 5, 55–61 (1983).
I. I. Vasilenko and R. K. Melekhov, “The factor of polarization in the process of corrosion cracking of metallic materials in chloride solutions,” in: The Properties of Constructional Materials under the Action of Working Media [in Russian], Naukova Dumka, Kiev (1980), pp. 97–115.
V. A. Marichev, “Certain unsolved questions of the electrochemistry of corrosion cracking”, Zasch. Met., No. 1, 77–84 (1984).
D. F. Chernega, O. M. Byalyk, D. F. Ivanchuk, and G. A. Remizov, Gases in Nonferrous Metals and Alloys [in Russian], Metallurgiya, Moscow (1982).
E. Framm and E. Gebkhard, Gases and Carbon in Metals [in Russian], Metallurgiya, Moscow (1980).
O. D. Smiyan, “The hydrogen distribution in the zone of strain cracks,” Zh. Fiz. Khim.,54, No. 11, 2913–2917 (1980).
O. D. Smiyan, “Determination of diffusion coefficients with the use of the method of local analysis,” in: The Second All-Union Conference on Mass Spectrometry (Leningrad, Oct. 22–24, 1974) [in Russian], Nauka, Leningrad (1974), pp. 44–45.
O. D. Smiyan and K. K. Kadyreva, “New methods of direct experimental determination of the diffusion coefficients of gaseous impurities in the metal of weld joints,” in: Diffusion Processes in Welding [in Russian], Izd-vo O-va Znanie, Kiev (1976), pp. 19–21.
Translated from Fiziko-Khimicheskaya Mekhanika Materialov, Vol. 22, No. 5, pp. 22–27, September–October, 1986.
About this article
Cite this article
Smiyan, O.D. Diffusion of hydrogen into the crack wall metal in corrosion cracking of Al-Zn-Mg-Cu alloy. Mater Sci 22, 457–461 (1987). https://doi.org/10.1007/BF00723491
- Wall Metal
- Crack Wall