Heat treatment of YuNDK3 5T5 Alloys

  • 16 Accesses

Conclusions

We investigated the effect of the cooling rate from 900 to 600° and high-temperature magnetic tempering at 790–830° on the magnetic properties of YuNDK35T5 alloys.

It was found that the magnetic properties remain substantially unchanged with changes of the cooling rate from 2.1 to 0.73 deg/sec. The optimal temperature and time of high-temperature magnetic tempering coincide with those of ITMT in a lead bath.

Cooling in magnetic field at rates of 2.1–0.73 deg/sec with subsequent high-temperature magnetic tempering at 810° for 12 min and two-stage tempering at 650° for 6 h+550° for 24 h makes it possible to obtain the following magnetic properties of alloys YuNDK35T5 and YuNDK35T5BA without use of a lead bath; Br=9250 G and 11,300 G; Hc=1470 Oe and 1410 Oe; (BH)max=5.5·106 G-Oe and 11.2·106 G-Oe.

This is a preview of subscription content, log in to check access.

Literature cited

  1. 1.

    B. G. Livshits, Zh. Tekh. Fiz.,10, 23–24, 1981 (1940).

  2. 2.

    W. Wright, Cobalt, 48, 115 (1970).

  3. 3.

    L. A. Kovalerova, Trudy VNII Elektroizmeritel'nykh Priborov, 2 (6) (1969).

  4. 4.

    C. Bronner et al., Cobalt, 46, 15 (1970).

Download references

Additional information

Moscow Institute of Steel and Alloys. Translated from Metallovedenie i Termicheskaya Obrabotka Metallov, No. 8, pp. 30–33, August, 1973.

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Livshits, B.G., Samarin, B.A. & Shubakov, V.S. Heat treatment of YuNDK3 5T5 Alloys. Met Sci Heat Treat 15, 668–670 (1973). https://doi.org/10.1007/BF00654761

Download citation

Keywords

  • Magnetic Field
  • Heat Treatment
  • Magnetic Property
  • Cool Rate
  • Magnetic Tempering