Elaboration and characterization of YBa2Cu3O7−x thick tapes

  • C. His
  • N. Chardon
  • R. Kuentzler
  • S. Vilminot
Papers

Abstract

Thick tapes of YBa2Cu3O7−x superconductor have been tape-cast by the Doctor Blade technique. Sintering at temperatures higher than 950 °C reveals a texturing with (001) planes preferentially aligned parallel to the tape surface. The transition temperature and width as well as the resistivity at onset temperature are related to the sintering parameters. Low-temperature specific heat measurements show the disappearance of the upturn at low temperature, usually observed for this material.

Keywords

Polymer Transition Temperature Onset Temperature Heat Measurement Doctor Blade 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    J. G. Bednorz and K. A. Müller, Z. Physik B64 (1986) 189.CrossRefGoogle Scholar
  2. 2.
    C. W. Chu, P. H. Hor, R. L. Meng, L. Goa, Z. J. Huang and Y. Z. Wang, Phys. Rev. Lett. 58 (1987) 405.CrossRefGoogle Scholar
  3. 3.
    H. Maeda, Y. Tanaka, M. Fukutomi and T. Asano, Jpn J. Appl. Phys. 27 (1988) L209.CrossRefGoogle Scholar
  4. 4.
    Z. Z. Sheng, A. M. Herman, A. El Ali, C. Almasan, J. Estrada and T. Datta, Phys. Rev. Lett. 60 (1988) 1937.Google Scholar
  5. 5.
    R. J. Cava, B. Batlogg, R. B. van Dover, D. W. Hurphy, S. Sunshine, T. Siegrist, J. P. Remeika, E. A. Rietman, S. Zahurak and G. Espinoza, ibid. 58 (1987) 1676.CrossRefGoogle Scholar
  6. 6.
    P. Chaudhary, R. H. Koch, R. B. Laibowitz, T. R. McGuire and R. J. Cambino, ibid. 58 (1987) 2684.CrossRefGoogle Scholar
  7. 7.
    T. R. Dinger, T. K. Worthington, W. J. Gallagher and R. L. Sandstorm, ibid. 58 (1987) 2687.CrossRefGoogle Scholar
  8. 8.
    J. W. Ekin, A. I. Braginski, A. J. Panson, M. A. Janocko, D. W. Capone, N. Zaluzec, B. Flandermeyer, O. F. de Lima, H. Hong, J. Kwo and S. H. Liou, J. Appl. Phys. 62 (1987) 4821.CrossRefGoogle Scholar
  9. 9.
    S. Vilminot, S. Elhadigui, J. P. Kappler, J. C. Bernier, T. Dupin, R. Barral and G. Bouzat, Brit. Ceram. Proc. 40 (1988) 15.Google Scholar
  10. 10.
    S. Vilminot, S. Elhadigui, A. Derory, M. Drillon, J. C. Bernier, J. P. Kappler, R. Kuentzler and Y. Dossmann, Mater. Res. Bull. 23 (1988) 521.CrossRefGoogle Scholar
  11. 11.
    D. H. A. Blank, J. Flokstra, G. J. Gerritsma, L. J. M. van de Klundert and G. S. M. Velders, Physica 145B (1987) 222.Google Scholar
  12. 12.
    S. Vilminot, S. Elhadigui and C. His, Physica C 153–155 (1988) 387.CrossRefGoogle Scholar
  13. 13.
    T. H. Geballe, M. R. Beamsley, A. Kapitulnik, R. Hammond and J. Harris, Phys. Today 40(7) (1987) 19.Google Scholar
  14. 14.
    J. P. Singh, U. Balachandran, D. Shi, J. K. Degener and R. B. Poeppel, Mater. Lett. 7 (1988) 72.CrossRefGoogle Scholar
  15. 15.
    N. E. Phillips, R. A. Fisher, S. E. Lacy, C. Marcenat, J. A. Olsen, W. K. Ham, A. M. Stacy, J. E. Gordon and M. L. Tan, Physica 148B (1987) 360.Google Scholar
  16. 16.
    R. Kuentzler, Y. Dossmann, S. Vilminot and S. El Hadigui, Solid State Commun. 65 (1988) 1529.CrossRefGoogle Scholar

Copyright information

© Chapman & Hall 1991

Authors and Affiliations

  • C. His
    • 1
  • N. Chardon
    • 1
  • R. Kuentzler
    • 1
  • S. Vilminot
    • 1
  1. 1.Groupe des Matériaux InorganiquesIPCMS EHICSStrasbourgFrance

Personalised recommendations