Effect of annealing on magnetic properties and microstructure of electroless nickel-copper-phosphorus alloy deposits
- 264 Downloads
The relationship between magnetic properties and microstructure of the as-deposited and heat-treated Ni-Cu-P alloy deposits has been studied by means of vibrating sample magnetometry, differential scanning calorimetry. X-ray diffractometry and hot-stage transmission electron microscopy. The Ni-Cu-P deposits consist of low-P Ni-Cu solid solution crystallites and high-P-low-Ni-Cu amorphous phase. When the deposits are annealed at elevated temperatures, the Ni-Cu crystallites grow rejecting P from themselves and absorbing Cu from the neighbouring amorphous phase, while the P-rich amorphous phase transforms into Ni5P2 phase or into Ni5P2 and Ni3P phases. The metastable Ni5P2 phase finally transforms into the stable Ni3P phase. The non-magnetism observed in Ni-Cu-P deposits having a copper content above 28% in both as-deposited and annealed states, is attributed to their Cu-rich Ni-Cu solid solution crystallites. Nickel phosphides which crystallize from the amorphous phase existing mixed with the Ni-Cu crystallites in the as-deposited state, do not affect the saturated magnetic moment of the deposits.
KeywordsCopper Microstructure Nickel Transmission Electron Microscopy Differential Scanning Calorimetry
Unable to display preview. Download preview PDF.
- 1.A. Brenner and G. E. Riddle, US Pat. 2532283/4 (1950).Google Scholar
- 6.Y. Okamura, S. Futani, K. Kawada, A. Koga and F. Matsui, Kinzoku Hyomen Gijutsu (Jpn) 38 (1987) 424.Google Scholar
- 7.K. Aoki, O. Takano and S. Ishibashi, ibid. 30 (1979) 126.Google Scholar
- 8.M. Saito and A. Nakabayashi, US Pat. 4724188 (1988).Google Scholar
- 10.B. D. Cullity, “Introduction to Magnetic Materials” (Addison-Wesley, Massachusetts, 1972).Google Scholar