Effects of cooling rate and heat treatment on the microstructure of iron-based titanium carbide composites

  • B. S. Terry
  • O. S. Chinyamakobvu


The microstructural response of iron-carbon-TiC components produced by a liquid route to changes in cooling conditions and post-solidification heat treatments has been investigated. Heat treatments of pure Fe-TiC composite materials have been found to produce only minor changes in the TiC morphology and distribution with reduction in hardness resulting from some TiC precipitation and depletion of the iron matrix of titanium and carbon. As-cast composites containing Fe-2.4% C/10% TiC and Fe-3.27% C/10% TiC exhibit a white cast iron matrix containing dispersed TiC. Subsequent heat treatment of this material at 750° C renders the matrix malleable, replacing the cementite by free graphite with no apparent alteration to the TiC morphology or distribution.


Titanium Carbide Heat Treatment Cool Rate Cementite 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.


Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.


  1. 1.
    B. S. Terry and O. S. Chinyamakobvu, J. Mater. Sci. Lett. 10 (1991) 628.CrossRefGoogle Scholar
  2. 2.
    Idem, Mater. Sci. Technol. 7 (1991) 648.CrossRefGoogle Scholar
  3. 3.
    Idem, ibid., in press.CrossRefGoogle Scholar
  4. 4.
    I. Minkoff, “The Physical Metallurgy of Cast Iron” (Wiley, New York, 1983).Google Scholar
  5. 5.
    ASM, Metals Handbook, 9th Edn, Vol. 1 (American Society for Metals, Metals Park, Ohio, 1983) pp. 3–24.Google Scholar

Copyright information

© Chapman & Hall 1992

Authors and Affiliations

  • B. S. Terry
    • 1
  • O. S. Chinyamakobvu
    • 1
  1. 1.Department of MaterialsImperial CollegeLondonUK

Personalised recommendations