Some aspects of interface adhesion of electrolytically oxidized carbon fibres in an epoxy-resin matrix

  • C. A. Baillie
  • M. G. Bader
Article

Abstract

A comprehensive investigation of the adhesion at the interface of a carbon fibre in an epoxy resin was made. The fibre surfaces were modified, to increase their adhesion to resin, by an electrolytic surface treatment which was applied at various current densities. Subsequent changes in the fibre properties relating to possible mechanical, physical and chemical contributions to adhesion were monitored. Tensile tests on single fibres indicated that the treatment altered the strengths of the fibres, which were found to have their highest values and to be least variable at an optimum adhesion level. A method was developed to estimate the strength of the fibres in the resin, this confirmed the single-fibre data. A novel method of labelling the acidic sites by producing adsorption isotherms was developed to identify surface functionality. Surface acidity correlated well with adhesion levels. Single-fibre pull-out tests, modelled using a new combination failure criterion and fragmentation tests, indicated that the optimum adhesion level for this fibre/resin system was achieved with an electrolytic treatment at 25 C m−2. The principal effects of this treatment were considered to be due to chemical modification of the fibre surface coupled with the removal of a loosely adherent surface layer.

Keywords

Tensile Test Carbon Fibre Acidic Site Fibre Surface Interface Adhesion 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    W. W. Wright, “Composite polymers” 3, edited by P. Dickin (RAPRA Tech. Ltd. Info. Pub., London, 1990) Part 1 p. 231, Part 2 p. 360.Google Scholar
  2. 2.
    L. C. Wolstenholme and M.G. Bader, ICCM V111 Honolulu, edited by S. Tsai, G. Springer (SAMPE, Society for the Advancement of Materials Process Engineering, 1991).Google Scholar
  3. 3.
    H. D. Wagner and A. Eitan, Appl. Phys Lett. 56 (1990) 1965.CrossRefGoogle Scholar
  4. 4.
    B. Yavin, H. E. Gallis, J. Scherf, A. Eitan and H. D. Wagner, Polym. Compos. 12 (1991) 436.CrossRefGoogle Scholar
  5. 5.
    M. J. Pitkethly and J. B. Doble, “Interfacial phenomena in composite materials”, Sheffield, edited by F. R. Jones (1989) p. 35.Google Scholar
  6. 6.
    G. Desarmot and M. Sanchez, Quatriemes Journees National sur les Composites 4 (1984) 449.Google Scholar
  7. 7.
    J. C. Figueroa, T. E. Carney and L. S. Schadler, Comp. Sci. Tech. 42 (1991) 77.CrossRefGoogle Scholar
  8. 8.
    D. A. Clarke, PhD thesis, University of Surrey, UK (1988).Google Scholar
  9. 9.
    A. Kelly and W. R. Tyson, J. Mech. Phys. Solids 13 (1965) 329.CrossRefGoogle Scholar
  10. 10.
    R. B. Henstenburg and S. L. Phoenix, Polym. Compos. 10 (1989) 389.CrossRefGoogle Scholar
  11. 11.
    A. N. Netravali, P. Schwartz and S. L. Phoenix, ibid. 10 (1989) 385.CrossRefGoogle Scholar
  12. 12.
    H. L. Cox, Brit. J. Appl Phys. 3 (1952) 72.CrossRefGoogle Scholar
  13. 13.
    C. Gurney and J. Hunt, Proc. Roy. Soc. Lond A 299 (1967) 508.CrossRefGoogle Scholar
  14. 14.
    J. O. Outwater and M. C. Murphy, Twenty-Fourth Annual Technical Conference on Reinforced Plastics/Composites Division SPI 11C (1970).Google Scholar
  15. 15.
    Y. C. Gao, Y. W. Mai and B. Cotterell, J. Appl. Maths. Phys ZAMP 39 (1988) 550.Google Scholar
  16. 16.
    C. H. Hseuh, Mater. Sci. Engng. A 125 (1990) 67.CrossRefGoogle Scholar
  17. 17.
    Idem.ibid. 123 (1990) 1.CrossRefGoogle Scholar
  18. 18.
    J. K. Kim, C. A. Baillie and Y. W. Mai, J. Mater. Sci. 27 (1991) 143.Google Scholar
  19. 19.
    Idem., Scrip. Met. Mater. 25 (1991) 315.CrossRefGoogle Scholar
  20. 20.
    A. Takaku and R.G.C. Arridge, J. Phys. D. Appl. Phys. 6 (1973) 2038.CrossRefGoogle Scholar
  21. 21.
    P. Marshall and J. Price, Composites 22 (1991) 388.CrossRefGoogle Scholar
  22. 22.
    E. Klinklin and M. Guigon, Interfacial phenomena in composite materials, Leuven, edited by I. Verpoest and F. R. Jones (Butterworth-Heinemann, 1991) p. 83.Google Scholar
  23. 23.
    L. T. Drzal, M. J. Rich and P. F. Lloyd, J. Adhesion 16 (1982) 1.CrossRefGoogle Scholar
  24. 24.
    R. Robinson, S. Lehmann, G. Askew, D. Wilford, C. Megerdigian and R. Papalia, “High tech—the way into the 90's”, edited by K. Brunsch, H. D. Golden and C. M. Herkert (Elsevier, 1986) p. 299.Google Scholar
  25. 25.
    P. Denison, F. R. Jones and J. F. Watts, Sur. Int. Anal. 20 (1985) 4647.Google Scholar
  26. 26.
    C. A. Baillie, J. F. Watts and J. E. Castle, J. Mater. Chem (1991) in press.Google Scholar

Copyright information

© Chapman & Hall 1994

Authors and Affiliations

  • C. A. Baillie
    • 1
  • M. G. Bader
    • 1
  1. 1.Department of Materials Science and EngineeringUniversity of SurreyGuildfordUK

Personalised recommendations