Interface reactions between glass melts containing transition metal oxides and ferrites
The interface reactions between SiO2-PbO-MO melts (M = Fe, Mn, Zn and Ni) and Mn-Zn and Ni-Zn ferrites were studied using electron probe microanalysis and X-ray diffraction. Ni ions in the glass melt containing NiO were localized at the interface between the glass and Mn-Zn ferrite. The Ni-rich layer was also detected at the interface between NiO containing glass melt and Ni-Zn ferrite; the composition of this layer was thought to be close to NiFe2O4. Pb8NiSi6O21 crystal was deposited as the product of the reaction with the glass melt and Mn-Zn ferrite at 700 °C. As compared with Mn-Zn ferrite, no reaction products were formed in Ni-Zn ferrite at various temperatures. The dissolution length of Mn-Zn ferrite in SPN5 glass melt was found to be smaller than for other melts, and it is concluded that the NiO-rich layer at the surface of the ferrite is chemically very durable to the glass melts.
KeywordsOxide Polymer Ferrite Metal Oxide Material Processing
Unable to display preview. Download preview PDF.
- 7.Idem, Bull Ceram. Soc. Jpn 15 (1980) 427.Google Scholar
- 8.H. Tanigawa, T. Ueno and K. Fukushima, Bull. Gov. Ind. Res. Inst., Osaka 25 (1974) 142.Google Scholar
- 9.H. Tanigawa, T. Ueno and Y. Nishida, ibid. 27 (1976) 68.Google Scholar
- 11.K. Matusita, M. Satou, T. Komatsu and A. Nitta, in Proceedings of the International Conference on Science and Technology for New Glasses, Tokyo, October 16–17 1991, Tokyo, edited by S. Sakka and N. Soga (Ceramic Society of Japan) p. 163.Google Scholar
- 14.A. Nitta, T. Komatsu, K. Matusita and A. Inada, in Proceedings of XV International Congress on Glass in Leningrad, July 3–7, 1989 Vol. 3b edited by O. V. Mazurin (Nauka, Leningrad, 1989) p. 326.Google Scholar