, Volume 30, Issue 22, pp 5681–5686 | Cite as

The orientation relationship between tetragonal zirconia precipitates with regard to elastic interaction energy

  • D. G. Jensen
Papers

Abstract

The elastic interaction energy between tetragonal zirconia precipitates for different mutual orientations is considered. The results of numerical analysis of this procedure are compared with experimentally observed preferred orientation relationships in the ceria-magnesia-partially stabilized zirconia (CM-PSZ) system. Two variants appear favourable, a parallel-stepped precipitate configuration with precipitate centres stepped at about 20°, and orthogonal precipitates in an edge-face configuration.

Keywords

Polymer Zirconia Interaction Energy Material Processing Prefer Orientation 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    V. Perovic, G. R. Purdy and L. M. Brown, Acta Metall. 27 (1979) 1075.CrossRefGoogle Scholar
  2. 2.
    Idem, ibid. 29 (1981) 889.CrossRefGoogle Scholar
  3. 3.
    N. Bhathena, R. G. Hoagland and G. Meyrick, J. Am. Ceram. Soc. 67 (1984) 799.CrossRefGoogle Scholar
  4. 4.
    D. J. Green, R. H. J. Hannink and M. V. Swain, “Transformation toughening of ceramics” (CRC Press, 1989).Google Scholar
  5. 5.
    A. G. Evans, J. Am. Ceram. Soc. 73 (1990) 187.CrossRefGoogle Scholar
  6. 6.
    R. W. Steinbrech, J. Eur. Ceram. Soc. 10 (1992) 131.CrossRefGoogle Scholar
  7. 7.
    D. G. Iensen, R. H. J. Hannink and B. C. Muddle, unpublished results.Google Scholar
  8. 8.
    V. Lanteri, T. E. Mitchell and A. H. Heuer, J. Am. Ceram. Soc. 69 (1986) 564.CrossRefGoogle Scholar
  9. 9.
    R. H. J. Hannink, J. Mater. Sci. 13 (1978) 2487.CrossRefGoogle Scholar
  10. 10.
    J. P. Hirth and J. Lothe, “Theory of dislocations” (Wiley, 1982).Google Scholar
  11. 11.
    V. Perovic, G. R. Purdy and L. M. Brown, Scripta Metall. 15 (1980) 217.CrossRefGoogle Scholar
  12. 12.
    D. G. Jensen, R. H. J. Hannink and B. C. Muddle, in “Proceedings of the 3rd IUMRS-ICAM Conference”, Symposium J. Japan (1993).Google Scholar

Copyright information

© Chapman & Hall 1995

Authors and Affiliations

  • D. G. Jensen
    • 1
  1. 1.Department of Materials EngineeringMonash UniversityClaytonAustralia

Personalised recommendations