, Volume 29, Issue 21, pp 5664–5672 | Cite as

Production of ultrafine alpha alumina powders and fabrication of fine grained strong ceramics

  • S. Rajendran
Papers

Abstract

Hydrous alumina powders, pure, seeded with alpha alumina, containing ammonium nitrate and containing both ammonium nitrate and seeds, were prepared by hydroxide precipitation. Their crystallization and sintering behaviour were investigated and mechanical properties of the ceramics were tested. Pure hydrous alumina transformed to alpha alumina crystals, with a size of ca. 200 nm, at 1200°C, after undergoing the usual metastable phase changes during heat-treatment. The powder needed to be sintered at 1600°C to achieve a high density. The ceramic had an average grain size of ca. 9 μm. Seeding lowered the transformation temperature to ca. 1120°C and caused the transformation to begin at ca. 600°C. The material could be sintered at 1500°C and had a grain size of 2 μm. The nitrate, predominantly present as ammonium nitrate, lowered the transformation temperature to ca. 1150°C and altered the proportion of the intermediate phases. However, the materials still had to be sintered at 1500°C to achieve >97% density. When both seed particles and nitrate ions were present the material almost completely transformed at 950°C to uniform crystals of alpha alumina with a size <60 nm that sintered to >99% theoretical density at 1450°C. The final ceramic had a uniformly grained (<1.0 μm) microstructure and exhibited strength up to 800 M Pa.

Keywords

Grain Size Nitrate Crystallization Phase Change Transformation Temperature 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    E. D. H. HUBNER, Alumina — Processing, properties and applications (Springer-Verlag, New York, 1970).Google Scholar
  2. 2.
    H. K. BOWEN, Mater. Sci. Engng. 44 (1980) 1.CrossRefGoogle Scholar
  3. 3.
    G. Y. ONADO Jr and L. L. HENCH (editors) “Ceramic processing before firing” (John Wiley, New York, 1978).Google Scholar
  4. 4.
    L. L. HENCH and D. R. ULRICH (eds) “Ultrastructure processing of ceramics, glasses and composites” (Wiley, New York, 1984).Google Scholar
  5. 5.
    G. L. MESSING, J. W. McCAULEY, K. S. (Joe) MAZDIYASNI and R. A. HABER (eds) “Ceramic powder science” (Adv. Ceram. 21, Amer. Ceram. Soc. Inc., Westerville, OH, 1987).Google Scholar
  6. 6.
    C. J. BRINKER, D. E. CLARK and D. R. ULRICH (eds) “Better ceramics through chemistry III”, Mater. Res. Soc. Symp. Proc., Vol 121 (Mater. Res. Soc., Pittsburgh, PA, 1988).Google Scholar
  7. 7.
    G. L. MESSING, S. HIRANO and H. HAUSNER (eds) “Ceramic powder science III”, Ceramic Trans., Vol 12 (Amer, Ceram. Soc. Inc., Westerville OH, 1990).Google Scholar
  8. 8.
    M. KUMAGAI and G. L. MESSING, J. Amer. Ceram. Soc. 67 (1984) C230.CrossRefGoogle Scholar
  9. 9.
    Y. SUWA, R. ROY and S. KOMARNENI, ibid. 68 (1985) C238.CrossRefGoogle Scholar
  10. 10.
    J. L. MCARDLE and G. L. MESSING, Adv. Ceram. Mater. 3 (1988) 387.CrossRefGoogle Scholar
  11. 11.
    L. PACH, R. ROY and S. KOMARNENI, J. Mater. Res. 5 (1990) 278.CrossRefGoogle Scholar
  12. 12.
    S. RAJENDRAN and J. L. WOOLFREY, Key Engng. Mater. 48–50 (1990) 462.Google Scholar
  13. 13.
    S. RAJENDRAN, D. J. CASSIDY and J. L. WOOLFREY, Unpublished work.Google Scholar
  14. 14.
    S. RAJENDRAN, Unpublished work.Google Scholar
  15. 15.
    K. WEFERS and G. M. BELL, in “Oxides and hydroxides of aluminium” (Technical Paper No. 19, Alcoa Res. Lab., 1972).Google Scholar
  16. 16.
    C. MISRA, “Industrial alumina chemicals” (ACS Monograph 184, Amer. Chem. Soc., Washington, 1986).Google Scholar
  17. 17.
    J. W. MELLOR, “Mellor's comprehensive treatise on inorganic and theoretical chemistry”, Vol. 8, Nitrogen Part II (Longman's, London, 1967).Google Scholar
  18. 18.
    G. A. CHADWICK, “Metalography of phase transformations” (Butterworths, London, 1972), p. 194.Google Scholar
  19. 19.
    W. A. YARBROUGH and R. ROY, J. Mater. Res. 2 (1987) 494.CrossRefGoogle Scholar
  20. 20.
    S. R. WITEK and E. P. BUTLER, J. Amer. Ceram. Soc. 69 (1986) 523.CrossRefGoogle Scholar
  21. 21.
    S. RAJENDRAN, Unpublished work.Google Scholar
  22. 22.
    C. A. HANDWERKER, R. M. CANNON and R. L. COBLE, “Structure and properties of MgO and Al2O3 ceramics, Advances in Ceramics”, edited by W. D. Kingery (Amer. Ceram, Soc., Columbus, OH, 1984) p. 619.Google Scholar
  23. 23.
    T. K. GUPTA, J. Amer. Ceram. Soc. 55 (1972) 276.CrossRefGoogle Scholar
  24. 24.
    B. J. KELLETT and F. F. LANGE, ibid. 72 (1989) 725.CrossRefGoogle Scholar

Copyright information

© Chapman & Hall 1994

Authors and Affiliations

  • S. Rajendran
    • 1
  1. 1.Advanced Materials ProgramAustralian Nuclear Science and Technology OrganisationMenaiAustralia

Personalised recommendations